含偶氮苯和1,3,4-噁二唑基团化合物的合成及光响应性能

以间苯二甲酸为原料,经过多步合成了1种含偶氮苯和1,3,4-噁二唑基团化合物5-[4-(十六烷氧基)苯基偶氮-]1,3-苯基-二-(1,3,4-噁二唑硫基)乙酸甲酯(8),利用IR、UV-vis、1 H NMR对其结构进行表征.该化合物四氢呋喃溶液紫外光谱中,偶氮苯结构K带的最大吸收波长为360nm,摩尔吸光系数ε为27 476L.mol-1.cm-1.在365nm紫外光照射下,偶氮苯基团发生反-顺异构化,照射5min后达到光稳态,光稳态时偶氮苯基团光致反顺异构化速率常数kp为1.338 9min-1,反式异构体转化效率R为80.95%,顺式异构体比例Y为84.99%,光稳态时偶氮苯K带最大吸收波长由360nm蓝移至326nm,将其置于暗室中,35h后恢复到光照前状态.     

1-(2-萘酚-4-磺酸)-3-[4-(苯基偶氮)苯基]-三氮烯合成及与阴离子表面活性剂的显色反应

合成了新试剂1-(2-萘酚-4-磺酸)-3-[4-(苯基偶氮)苯基]-三氮烯(NASAPAPT),研究了该试剂与阴离子表面活性剂(AS)十二烷基硫酸钠、十二烷基苯磺酸钠的显色反应的条件.试剂和十二烷基硫酸钠、十二烷基苯磺酸钠形成配合物的最大吸收分别位于441nm和432nm,表观摩尔吸光系数为1.51×104 L.mol-1.cm-1和2.29×104 L.mol-1.cm-1.建立了水相测定微量阴离子表面活性剂的新方法,方法已应用于合成水样及环境水样中阴离子表面活性剂的测定.     

侧链含杂环偶氮结构聚合物的三阶非线性光学性能

合成了具非线性光学性能的杂环偶氮生色团的单体化合物甲基丙烯酸(4-苯并噻唑-2-偶氮基苯基)酯(BAMA),并通过自由基聚合得到均聚物聚甲基丙烯酸(4-苯并噻唑-2-偶氮基苯基)酯(PBAMA).利用1 H-NMR验证了聚合物的结构,采用Z-扫描法研究了聚合物溶液的三阶非线性光学性能.结果表明,单体和聚合物均具有较高的三阶非线性光学系数.     

新显色剂3—氯—4—(4—甲基—2—胂酸基苯基重氮氨基)偶氮苯的合成及其光度性能的研究

本文报道了新显色剂3-氯-4-(4-甲基-2-胂酸基苯基重氮氨基)偶氮苯的合成、纯化及结构分析。并且研究了该试剂与Cd、Hg等离子的显色反应。研究结果表明:在弱碱性介质中,有非离子表面活性剂Triton X-100的存在下,该试剂与Cd~(2+)、Hg~(2+)的显色反应具有较高的灵敏度和较好的选择性,可望该试剂在这些离子的光度测定中获得应用。     

双偶氮苯聚合物(PGMA-DO13)合成及其光学性能研究

偶氮苯侧链聚合物作为一类典型分子光开关、高容量数据存贮、非线性光学以及太阳能电池等材料得到广泛研究.文章合成了4-苯基偶氮-1-萘胺(DO7)、4-[4-(苯基偶氮基)-1-萘基偶氮基]-p-苯酚(DO13)及聚甲基丙烯酸缩水甘油醚(PGMA)与上述双偶氮(DO13)的共聚物(PGMA -DO13);利用元素、核磁共振...     

环糊精衍生物与偶氮苯Langmuir复合膜的界面自组装与主客体识别研究

设计合成了胆固醇修饰的环糊精衍生物(CD—CHOL)以及偶氮苯修饰的聚丙烯酸化合物(PAA—Azo),通过气液界面组装成功制备了Langmuir膜,由表面压-分子面积等温线表征界面铺展行为,采用原子力显微镜(AFM)对单层Langmuir膜的形貌进行了表征,进一步通过紫外光谱、圆二色谱、红外光谱、X射线光电子能谱研究组装膜中环糊精与偶氮苯基团的自组装过程与主客体识别机理。实验结果表明,CD—CHOL在纯水亚相与PAA—Azo亚相表面形成稳定的Langmuir膜,同时环糊精与偶氮苯基团之间发生了主客体识别。本研究工作为环糊精衍生物界面组装与主客体识别相关研究提供了新的探索。     

丙烯酰胺共聚物与表面活性剂复配体系研究

利用锥板粘度计和旋滴界面表张力仪研究了丙烯酰胺 ( AM) - N-乙烯基 - 2 -吡咯烷酮 ( VP) - 2 -丙烯酰胺基 - 2 -甲基丙磺酸 ( AMPS) ( AM- VP- AMPS)共聚物水溶液与阴离子表面活性剂十二烷基苯磺酸钠 ( C18H2 9Na O3 S)及中性表面活性剂聚乙二醇辛基苯基醚 ( OP- 1 0 )的相互作用以及该复配体系与原油之间界面张力 .研究结果表明 :AM- VP- AMPS共聚物水溶液与表面活性剂复配会降低水相 /油相界面张力 ,阴离子表面活性剂 ( C18H2 9Na O3 S)会引起共聚物水溶液表观粘度的下降 ,而中性表面活性剂 ( OP- 1 0 )对共聚物水溶液表观粘度影响不大     

5,5′-双(2-硝基苯基)偶氮二吡咯甲烷及其Ni(Ⅱ)配合物的合成与晶体结构

合成了一种5,5′-双(2-硝基苯基)偶氮二吡咯甲烷化合物及其镍配合物,采用X光衍射分析其晶体结构.由于分子内氢键的存在,配体分子的2个偶氮吡咯部分分别采取的是偶氮式异构体和腙式异构体.核磁共振和紫外-可见光谱分析进一步证明了配体分子在溶液中也存在腙式-偶氮式异构化.TGA研究表明配体化合物及其镍配合物均具有较高的热稳定性.     

高荧光量子产率BODIPY衍生物的荧光性能研究

本文以引入羧基的BODIPY荧光试剂(1,3,5,7-四甲基-8-苯基-(4’-O-乙酸)-二氟化硼-二吡咯甲烷,TMPAB)为研究对象,研究了不同类型的表面活性剂溶液、溶液的p H值、光照、平衡时间以及温度五种因素对荧光性质的影响,结果表明:在p H3.0~10.0的范围内,TMPAB随着p H值的增大,荧光强度增强;阳离子型表面活性剂对荧光强度有增敏效果;升高温度荧光强度下降;光照条件下,具有较好的光稳定性.     

七元瓜环与双子型表面活性剂相互作用的研究

本文研究了七元瓜环Q[7]与双子型表面活性剂12-2-12在水溶液中发生的相互作用,探讨了瓜环对表面活性剂性能的影响。结果表明:Q[7]和12-2-12可以形成2∶1的配合物;当存在Q[7]时,表面活性剂的临界胶团浓度(cmc)和最低表面张力(γ_(cmc))增大,降低表面张力的效率(pC_(20))和表面压(Π_(cmc))下降,表面活性和发泡能力降低;同时,表面活性剂的饱和吸附量(Г_(max))降低,最小分子横截面积(A_(min))增大,表面活性剂在溶液表面排列更疏松。瓜环对表面活性剂的性能具有重要影响。     

模型沉积物中POPs的超声波降解

以六氯苯为例,用超声波辐射及与其它高级氧化技术(AOPs)相结合来降解持久性有机污染物(POPs).结果表明,当超声波辐射与紫外线辐射结合时,六氯苯的降解率与单一超声波辐射降解率几乎相同,分别为39.7%和40.0%;而当超声波辐射与光催化相结合时,由于所添加的TiO2颗粒促进了空穴的形成,降解率可提高到49.4%;当表面活性剂的质量分数提高到0.1%时,降解率可提高到49.2%;当用双频超声波辐射时,六氯苯的降解率高于任一单频超声波辐射.经过1h超声波辐射,20/176kHz双频、20kHz单频和176单频条件下,六氯苯降解率分别为57.5%,3.67%和41.0%.     

树叶状CuO微结构:低温水浴合成、影响因素和光催化降解性能

以CuCl2·2H2O和NaOH为起始反应物,在没有任何表面活性剂或模板的辅助下,于80℃的水浴中恒温60 min,快速合成了树叶状的CuO微结构.利用X-射线粉末衍射仪和场发射的扫描电子显微镜对所得产物的物相和形貌进行了系统的表征,并调查了起始反应物的摩尔比、反应的温度和时间等实验参数对最终产物形貌的影响.实验显示,所得的树叶状的CuO微结构在365nm的紫外光的照射下具有强烈的促进有机小分子降解的能力.这在环境治理与防护领域有潜在的应用.     

UV/Fenton试剂处理阴离子表面活性剂废水性能研究

采用UV/Fenton试剂降解SDBS阴离子表面活性剂废水,在初始p H为3.0,Fe2+浓度为0.033 mol·L-1,H2O2分2次投加,总投加浓度为0.89 mol·L-1时,室温下紫外辐射反应30min,SDBS降解率可达89.01%.将UV、Fenton、UV/Fenton 3种体系处理SDBS废水的效果进行比较,发现UV对Fe2+催化H2O2氧化降解有机废水存在协同作用.     

Ordered mesoporous tungsten oxide and titanium oxide composites and their photocatalytic degradation behavior

Highly ordered mesoporous WO3/TiO2 (MWTs) composite materials with tunable chemical compositions were obtained by a surfactant template-assisted evaporation-induced selfassembly (EISA) processes. The structure properties of the MWT materials were characterized by small angle XRD, TEM and N2 sorption. The resultant materials showed large amount of ordered mesopores and high chemical homogeneity. With increasing crystallinity degree, the order degrees of mesostructure turned worse gradually. The MWT hybrids exhibited excellent visible light response due to the addition of WO3 with narrow band gap. Photocatalytic performances of the MWT samples were determined by measuring the photo-degradation of rhodamine B dye and phenol under simulated solar light irradiation. The effect of material parameters such as surface area, crystallinity and chemical compositions in the binary heterostructured system on photocatalytic performance were discussed in details.     

Template/surfactant free and UV light irradiation assisted fabrication of Mn-Co oxides composite nanorings: Structure and synthesis mechanism

A facile, green, cost effective, and template or surfactant free strategy via a two-step route i.e. UV irradiation followed by dissolution-growth for the controlled synthesis of Mn-Co composite nanorings at room temperature was proposed. The nanorings structures and the process were systematically studied via TEM, HRTEM, EDX and XRD. Bir-MnO_2 nanosheets first formed through the direct photolysis of KMnO_4 under UV light irradiation. This was followed by a dissolution-growth process via the dissolution of Bir-MnO_2 nanosheets by the generated H~+ from the redox reaction between the added Co(NO_3)_2 and residual KMnO_4, as well as the accompanied formation of CoOOH, and Mn-Co composite nanorings. It was found that a balance between the dissolution and growth rate was needed. Suitable pH, KMnO_4 presence and the starting nanosheets like Bir-MnO_2 were the key factors for the formation of nanorings. The obtained Mn-Co nanorings/TiO_2 showed enhanced efficiency for the catalytic oxidation of HCHO. Based on the above understandings, it is believed that the developed dissolution-growth method can be adopted for the designing and preparation of other Mn-Co composite nanostructures which can be further applied for environmental pollution remediation.     

红、蓝光照对大鼠视力早衰和神经网络的影响

目的探究红、蓝光照对大鼠视网膜衰老和神经网络的影响。方法将50只雄性Wistar大鼠随机分为5组,分别为蓝光照射1 h、蓝光照射8 h、红光照射1 h、红光照射8 h和空白对照组。干预12周后进行强制游泳实验(FSTs)评估精神状态。解剖取新鲜眼球视网膜色素上皮细胞(RPE)进行原代培养并进行衰老相关-β-半乳糖苷酶(SA-β-Gal)活性的鉴定,分析光照时间和复制衰老之间的关联,并采用试剂盒检测脑组织中一氧化氮(NO)和一氧化氮合酶(NOS)含量,分析光刺激对大鼠的应激反应。结果与红光照射相比较,蓝光光照8 h可显著上调RPE细胞的增殖(P <0. 05)和NOS的含量(P <0. 01),同时蓝光照射8 h更容易使大鼠陷入紧张、绝望的精神状态。结论蓝光较红光刺激对大鼠视网膜衰老和神经网络的影响更大。     

高能氙光传递窗的杀菌效果研究

摘要: 目的研究高能氙光传递窗对空气中和物品表面细菌的消毒效果。方法分别用标准菌株金黄色葡萄球菌、枯草芽孢杆菌和大肠埃希菌制备细菌悬液并涂布血平板,模拟物品表面细菌; 用普通营养琼脂平板培养空气落下菌。将两种平板经氙光传递窗和紫外线分别照射3 min 后,与对照组均放置于37℃恒温培养箱24-48 h,计算杀菌率。结果涂布于血平板的细菌悬液,经氙光照射3 min 后,平均杀菌率达到93. 2%; 空气落下菌经氙光照射3 min后,平均杀菌率达到99. 1%。两种平板经紫外线照射3 min 后的杀菌率不到50%。结论氙光传递窗能够高效、快速杀灭物品表面和空气中的细菌,平均杀菌率达到95%以上,氙光传递窗有可能成为常规传递窗的替代品。     

TiO_2悬浆体系光催化降解苯酚的研究

以高压汞灯为光源,研究了TiO2悬浆体系光催化降解苯酚的动力学规律,并考察了苯酚初 始质量浓度、催化剂投加量、溶液pH值、光强等对苯酚光解速率的影响.研究结果表明:该反应过 程可以用Langmuir-Hinshelwood(L-H)动力学方程描述;在一定条件下,催化剂的投加量、溶液 pH值均存在一最佳值;各因素对光催化降解苯酚反应影响的重要性排列顺序是,光照时间>pH 值>光照强度>TiO2投加量.     

类桃形钼酸铁微纳结构材料的水热合成、磁性和催化性能

以Fe(NO3)3和(NH4)6Mo7O24为反应物，在不添加表面活性剂的情况下，采用一步水热法成功地合成了一种新颖的钼酸铁（Fe2(MoO4)3）材料. 扫描电子显微镜和粉末X-射线衍射仪结果表明，所合成产品具有类桃形的微纳米结构，为单斜晶系结构材料，所用反应前驱物中的铁/钼投料比以及反应时间和温度等条件，对于形成Fe2(MoO4)3的层层紧密组装结构起到了关键作用，定向生长和层层自组装的纳米线构建了Fe2(MoO4)3的微纳米结构. 磁性能和催化性能测试结果表明，该Fe2(MoO4)3材料具有软磁性能，并在无光照的条件下对盐酸四环素(TC)表现出较好的催化降解效果，有望作为可磁性回收重复使用的TC降解催化剂.     

微波辐照下均分散氧化亚铜超细粒子的制备

在微波辐射条件下,用沉淀法制备了氧化亚铜均分散超细粒子,实验表明：随加热方式、CuSO4浓度、表面活性剂或螯合剂的不同,粒子的开状呈方形、雪花形、球形多种形态,特别是雪花形粒子,尚未见文献报道,与传统加热方式相比,微波辐照制备的粒子均分散性更好、形状更规整。