AZ31镁合金氩弧焊接接头组织与力学性能研究

钨极氩弧焊(TIG)为镁合金焊接中最常用的一种焊接方法。本文采用直流钨极氩弧焊对6.0 mm厚AZ31镁合金挤压板材进行了双面焊接实验。采用光学显微镜、扫描电镜、拉伸试验机考察分析了焊接接头显微组织与力学性能。显微组织分析表明,AZ31镁合金直流TIG焊接头由母材、热影响区、焊缝区组成,焊缝组织呈现焊丝熔化后凝固组织;在母材热影响区与焊缝区之间坡口处形成过渡区,晶粒细小,为母材与焊丝的熔合区。采用AZ31焊丝焊接接头平均抗拉强度为241.0 MPa,延伸率为13.8%,分别达到了母材的86.0%和63.6%。焊接接头的断裂均位于热影响区,断口呈现韧脆混合断裂特征。     

AZ31B镁合金TIG和MIG焊接接头组织性能比较分析

研究了AZ31B镁合金钨极氩弧焊(TIG)和熔化极氩弧焊(MIG)焊接接头组织及性能。在厚度为8.0 mm的AZ31B镁合金板材上分别进行了填丝TIG和MIG两种焊接试验,分析了AZ31B镁合金两种焊接工艺以及接头焊缝的微观组织和显微硬度。试验结果表明,填丝TIG焊缝成形良好;MIG焊接时有飞溅现象,焊缝成形不及TIG均匀。TIG和MIG焊接接头的相组成与母材的相组成一致。MIG焊接热影响区HAZ的晶内析出相弥散分布,焊缝区晶界析出相连续分布;而且MIG焊接接头的显微硬度值较TIG焊接时要高,焊接接头的力学性能有所提高。     

不锈钢热轧板材焊接接头的HAZ组织及性能

通过对304及430不锈钢热轧板材焊接接头热影响区(HAZ)的金相观察、无损检测、显微硬度测定、力学性能和晶间腐蚀性能试验,研究经手工钨极氩弧焊(TIG)的304及430热轧板材的HAZ组织及性能,并进行对比分析.结果表明,采用TIG焊接方法和较小的焊接规范,304焊接接头的热影响区奥氏体晶粒较细(7.5～8.0级),显微硬度为376 HV,焊缝与母材熔合良好;430焊接接头的热影响区铁素体晶粒明显长大(约为4.5级),粗晶粒区宽度约为0.7 mm,碳化物析出不多;热影响区的晶界部位受焊接热循环影响发生了α→γ→M相变,生成的M质量分数约占14%;304和430焊接接头的力学性能良好,拉伸断裂部位是焊缝和热影响区;EPR法测定表明,304及430母材和热影响区均没有产生晶间腐蚀.     

钪铒微合金化对7A52合金焊缝组织与性能的影响

采用传统ER5183焊丝及单独和复合添加Sc,Er的自制5183焊丝对7A52铝合金进行钨电极惰性气体保护焊,并对焊接接头的力学性能和焊缝显微组织进行了研究.结果表明,拉伸断裂均在焊缝中心处,焊缝处是焊接接头的最薄弱环节,其次是焊接热影响区内的软化区.在ER5183焊丝中添加微量元素Sc和Er可有效细化焊缝处的组织,提高合金焊接接头的强度,其中单独添加Sc的焊丝效果最好,单独添加Er的焊丝效果次之.焊接接头的抗拉强度可达3324MPa,是母材强度的725%.     

2219-T87铝合金TIG焊缝摩擦塞补焊接头组织及性能

采用摩擦塞补焊工艺,对8,mm厚的2219-T87铝合金TIG焊缝进行焊接实验,采用光学显微镜、扫描电子显微镜观察接头的焊缝成型、显微组织和强化相转变,通过硬度测试、拉伸试验、断口观测研究接头的力学性能和断裂特征.结果表明:摩擦塞补焊接头可分为塞棒区、塞棒热力影响区、再结晶区、热力影响区、热影响区和母材区/TIG焊缝区6部分;接头热影响区和热力影响区的强化相粗化,发生局部软化,垂直于TIG焊缝方向的最低硬度(95.1,HV)出现在热力影响区,平行于TIG焊缝方向的最低硬度(75.3,HV)出现在热影响区;接头的抗拉强度可达321.3,MPa,断后伸长率可达2.8%,,分别为母材的72.2%,和28.0%,;拉伸试样断裂位置为热力影响区,断口呈剪切韧窝,属于塑性断裂.     

热处理工艺对Al-12.7Si-0.6Mg合金焊接接头组织性能的影响

采用ER5356焊丝对厚度为6 mm的T6态Al-12.7Si-0.6Mg合金进行平板对接试验,使用交流脉冲TIG单面双道焊缝成形工艺,获得了良好的焊缝成形并且对焊接后材料分别进行了T5和T6态热处理。研究表明:热处理前,焊接接头热影响区内存在软化现象,接头抗拉强度为157.58 MPa,经T5态和T6态热处理后,焊接接头强度分别增至265.34 MPa和308.09 MPa;焊后热处理使熔合区析出的Si颗粒重新固溶到基体中,形成Al-Si固溶体及细小的α-Al枝晶组织,与焊缝区的等轴晶过渡良好,热影响区的显著硬度提高,使断裂位置由热影响区转移至熔合区,接头的抗拉强度和屈服强度大幅度提高。     

国产与进口5183焊丝及焊接接头组织与性能

采用国产与进口5183焊丝作为填充丝对5083-O状态合金板材实施MIG焊接.利用金相观察、拉伸性能测试、扫描电镜观察等方法研究了焊丝及焊接接头的显微组织与力学性能.结果表明:与进口5183焊丝相比,国产5183焊丝屈服强度较高,延伸率略低;在所选的焊接工艺参数条件下,MIG焊可以获得焊缝质量良好的焊接接头;两种焊丝焊接的接头各区组织基本相同,焊缝区是典型的急冷结晶的铸态组织;热影响区晶粒呈现出了沿轧制方向伸长变形的特点,部分析出相固溶到基体中.使用两种焊丝焊接的接头抗拉强度都达到基材的85%以上.     

Fe-6.5% Si合金热轧板焊接接头的组织和力学性能

针对Fe-6.5% Si合金热轧板焊接接头易萌生裂纹的问题,研究了不同氩弧焊工艺对焊接接头显微组织和力学性能的影响规律.研究表明:不使用填充焊丝的TIG焊不适合Fe-6.5% Si合金热轧板焊接,因在焊缝内出现大量显微裂纹;使用工业纯铁焊丝的MIG焊实现了Fe-6.5% Si合金热轧板的良好连接,焊缝表面连续、鱼鳞纹均匀,焊缝内无显微裂纹.稀释硅浓度是改善焊缝区组织和力性的有效方法.优化工艺下的焊接接头在500℃拉伸延伸率5.5%,抗拉强度280 MPa,满足Fe-6.5%Si合金板带制造过程中的温轧工艺要求.     

Ti60合金板材电子束焊接接头组织性能研究

研究了Ti60合金板材电子束焊接接头的显微组织与力学性能.研究表明,焊接接头熔合区中的显微组织由针状α''相、α相和β相组成,热影响区的显微组织为β相转变组织、针状α''相及部分未溶解的等轴初生α相组成的混合组织.焊接接头硬度呈不均匀分布,焊缝熔合区的硬度最高,热影响区次之,母材区最低.焊接接头的室温和高温拉伸均断裂于母材区,焊接接头处拉伸强度等同于接头处母材区的强度.焊接接头的持久断裂均发生于焊缝区域,接头的持久寿命均>100 h.     

35#钢摩擦焊多级加压对轴向缩短量及焊后组织的影响

以35#钢为焊接母材,应用连续驱动摩擦焊接方式,采用正交试验的方法并经过极差分析后,探究了中等直径焊件多级加压方式下各工艺参数对轴向缩短量的影响规律,并对焊接接头显微组织及显微硬度进行了分析.实验结果表明,对焊件轴向缩短量影响程度依次为:二级摩擦位移、二级摩擦压力、一级摩擦压力、一级摩擦位移;观察焊接接头显微组织发现焊缝处得到了细小的铁素体与珠光体相互融合的优良组织,焊缝组织达到正火态;通过对焊件焊缝及热影响区显微硬度测试后可以得出,各焊件焊缝的显微硬度值明显高于母材,不同焊接工艺参数组合方式对焊件接头晶粒存在一定影响并直接影响焊件接头硬度.     

高速列车用6005A铝合金厚板的焊接工艺

采用半自动MIG焊完成了厚度为12mm的6005A-T6铝合金板材的连接,通过正交试验研究了焊接工艺参数对焊接接头抗拉强度及焊缝表面质量的影响.结果表明,各工艺参数对焊接接头抗拉强度影响显著性从大到小依次为:焊接电流,焊接电压,焊接速度和预热温度.考虑焊缝表面质量因素,各工艺参数影响显著性从大到小依次为焊接速度、预热温度和焊接电流.本研究条件下最佳MIG焊接6005A-T6板材的工艺参数为:预热温度200℃,焊接电流180A,焊接电压18.0V,焊接速度12mm/s.焊接后试样接头热影响区内晶粒平均尺寸小于5μm,且无过分长大现象.焊接后板材拉断时为韧性断裂.     

Characterizations of dissimilar S32205/316L welds using austenitic,super-austenitic and super-duplex filler metals

UNS S32205 duplex stainless steel plates were welded to AISI 316L stainless steel using the pulsed gas tungsten arc welding process with three different filler metals: ER2594, ER312, and ER385. The microstructures of the welds were characterized using optical and scanning electron microscopy, and all of the specimens were evaluated by ferrite measurements. The mechanical properties were studied through hardness, tensile, and impact tests. In addition, the pitting resistance equivalent number was calculated and cyclic polarization tests were performed to evaluate the corrosion resistance of the weld metal. The results showed that chromium nitride was formed in the heat-affected zone of the duplex side, whereas no sigma phase was detected in any of the specimens. The ferrite number increased from the root pass to the final pass. The absorbed energies of the impact test decreased with increasing ferrite number, whereas the tensile strength was enhanced. The fully austenitic microstructure of the specimen welded with ER385 exhibited the highest resistance to pitting corrosion at 25°C, and the super-duplex weld metal presented superior corrosion resistance at 50°C.     

用于高强钢胶粘修补的螺柱塞焊接头性能分析

为了解决车身装配中胶粘接头由于工艺操作或受力过载等原因造成的胶粘接头失效问题,提出了螺柱塞焊(SPW)连接方法,该方法可结合工业焊接机器人对高强钢胶粘接头进行自动化修补.以试验为基础,研究了使用螺柱塞焊工艺修补后的胶粘接头静态力学性能与疲劳特性,将其与同种材料电阻点焊(RSW)焊接试样进行比较.试验结果表明,螺柱塞焊焊接试样静拉伸强度接近电阻点焊,熔池组织致密,两种试样疲劳寿命曲线几乎相同,使用该方法可以获得与电阻点焊接头相近的接头力学性能.     

奥氏体不锈钢焊接接头抗腐蚀性能研究

研究了不同焊接工艺对SUS316奥氏体不锈钢焊接接头的抗腐蚀性能。分别采用了钨极氩弧焊（TIG）、熔化极钨极氩弧焊（MIG）和钨极氩弧焊加填丝（TIG＋M）的方法焊接SUS316奥氏体不锈钢，焊接材料选用超低碳高铬镍焊丝H0Cr19Ni12Mo2。利用金相显微镜、晶间腐蚀实验和电化学腐蚀等的测试分析方法，对不同焊接工艺条件下的化学成分、显微组织和抗腐蚀性能进行了分析研究。结果表明，焊缝区抗晶间腐蚀性能依次为母材〉TIG＋M〉MIG〉TIG，焊缝区在硫酸溶液中的抗电压学腐蚀性能依次为；TIG＋M〉MIG〉TIG。     

某型飞机5A02铝合金焊接接头疲劳性能研究

本文研究了某型飞机所使用的5A02铝合金焊接头的疲劳性能。试验研究了该材料的原始焊接接头与一次补焊接头的疲劳性能,通过疲劳试验及疲劳断口形貌分析等手段对焊接接头疲劳性能进行了研究。试验结果表明,补焊会造成焊缝附近区域材料晶粒粗大,并且补焊后,焊接接头的中值疲劳强度下降。     

Effect of welding process on the microstructure and properties of dissimilar weld joints between low alloy steel and duplex stainless steel

To obtain high-quality dissimilar weld joints, the processes of metal inert gas (MIG) welding and tungsten inert gas (TIG) welding for duplex stainless steel (DSS) and low alloy steel were compared in this paper. The microstructure and corrosion morphology of dissimilar weld joints were observed by scanning electron microscopy (SEM); the chemical compositions in different zones were detected by energy-dispersive spectroscopy (EDS); the mechanical properties were measured by microhardness test, tensile test, and impact test; the corrosion behavior was evaluated by polarization curves. Obvious concentration gradients of Ni and Cr exist between the fusion boundary and the type II boundary, where the hardness is much higher. The impact toughness of weld metal by MIG welding is higher than that by TIG welding. The corrosion current density of TIG weld metal is higher than that of MIG weld metal in a 3.5wt% NaCl solution. Galvanic corrosion happens between low alloy steel and weld metal, revealing the weakness of low alloy steel in industrial service. The quality of joints produced by MIG welding is better than that by TIG welding in mechanical performance and corrosion resistance. MIG welding with the filler metal ER2009 is the suitable welding process for dissimilar metals jointing between UNS S31803 duplex stainless steel and low alloy steel in practical application.     

焊接热输入对镁合金与镀铜钢冷金属过渡焊接接头性能和缺陷影响

利用冷金属过渡焊(CMT)对镁合金和镀铜钢异种金属进行焊接,填充材料选择AZ31镁合金焊丝,对焊接接头的显微组织进行检测,分析焊接接头的性能和缺陷。实验结果表明:Cu元素对镁合金在钢表面的润湿铺展起到良好的促进作用,焊接热输入影响Cu元素对镁/钢表面的润湿铺展效果。焊接接头产生富铜区,易产生裂纹,降低了焊接接头强度。经过拉伸测试,在焊接热输入为212. 2 J/mm时,焊接接头强度达到最大值3. 99 k N,但在焊接热输入达到254. 6 J/mm时,焊接强度反而降低,这是由于钎焊区生成了大量的中间层脆性化合物。焊接接头组织中检测到气孔、夹渣和裂纹等焊接缺陷的存在,这与母材表面的氧化膜和焊缝内应力有关。