非均相Fenton反应催化剂Fe2O3/γ-Al2O3的制备及其性能

采用等体积浸渍法制备非均相Fenton反应催化剂Fe2O3/γ-Al2O3,以对羟基苯丙酸为降解目标物,考察了γ-Al2O3粒径的大小、浸渍时间、焙烧温度、焙烧时间、负载量等因素对催化剂催化活性的影响.通过热重、XRD、电镜扫描对催化剂形貌和特征的分析以及催化反应的结果分析可知,在γ-Al2O3上负载了催化剂Fe2O3,但Fe2O3并不均匀,在γ-Al2O3为100~120目,负载量为11.7%,浸渍10,h,焙烧温度为550,℃,焙烧4,h,与60,mg/L的对羟基苯丙酸反应60,min的条件下,催化剂的活性最好,对羟基苯丙酸的去除率可达到70.26%.重复实验说明催化剂的稳定性较好.     

纳米Cu/γ-Al_2O_3催化剂制备与选择催化还原NO性能

采用NH4Al(SO4)2、NH4HCO3和NH3.H2O为原料沉淀制备γ-Al2O3,然后浸渍负载活性组分Cu2+,制成纳米Cu/γ-Al2O3催化剂,并考察其催化性能.SEM测试结果表明:制得的纳米Cu/γ-Al2O3催化剂粒径均小于100 nm.活性测试结果表明:在pH值为8.5时制备的γ-Al2O3负载上3%Cu2+的纳米Cu/γ-Al2O3催化剂性能最佳,在275℃时能使NO的转化率达到82.3%,与普通Cu/γ-Al2O3催化剂相比较,最佳活性温度降低了25℃,NO最大转化率提高了31.8%.     

制备方法对NiO/γ-Al2O3催化剂重整活性的影响

利用固定床流动反应装置,研究了NiO/γ-Al2O3催化剂的制备方法对CH4与CO2转化制合成气催化活性的影响.在本实验条件下,采用浸渍法和焙烧温度为400℃制备的NiO/γ-Al2O3(w=0.113)催化剂,在反应温度为750C和空速为2500h-1下,对CH4和CO2重整反应会显示良好的催化活性.本文还对催化剂抗积炭性能作初步讨论.     

Cu/Ce-Zr-La/γ-Al_2O_3的制备及其三效催化性能

将AlNH4(SO4)2溶液滴入到NH4HCO3和PEG6000的混合溶液中,用沉淀法制备γ-Al2O3载体.然后用等体积浸渍法分别负载上Ce-Zr-La以及活性组分Cu,制备催化剂Cu/Ce-Zr-La/γ-Al2O3.考察该催化剂的三效催化性能,并借助扫描电子显微镜(SEM)、X-射线衍射(XRD)、热重分析(TG)等方法研究催化剂活性与结构的关系.实验结果表明:Cu/Ce-Zr-La/γ-Al2O3具有良好的三效催化性能,NO、CO和C3H6的起燃温度都较低,分别为250℃、150℃和300℃;CeO2-ZrO2对载体γ-Al2O3和活性组分Cu具有稳定作用,避免了CuAl2O4尖晶石相的生成;La能够显著提高催化剂的热稳定性.     

负载型催化剂Pt-γ-Al2O3-CeO2的合成和活性研究

模拟贫燃机车尾气条件下,比较浸渍法和共沉淀法制备的Pt-γ-Al2O3-CeO2纳米催化剂对NO的催化还原活性.结果表明,采用浸渍法所得的样品催化活性最高,使NO的转化率达83%;而共沉淀法所得的样品抗烧结性能好,活性温度范围宽.利用XRD,BET,TEM等手段对活性好的样品进行了一系列分析和比较.     

纳米TiO2/γ-Al2O3制备及光催化性质的研究

制备了TiO2/γ-Al2O3负载型纳米复合催化剂,利用XRD,UV-VIS手段对其光降解活性进行表征,考察了TiO2/γ-Al2O3纳米催化剂降解工业废水中的丙烯酸。结果表明：在可见光条件下,TiO2/γ-Al2O3纳米催化剂对高浓度工业废水中的丙烯酸有降解作用。     

LaCeCuMn/γ-Al2O3纳米稀土催化剂的制备及性能研究

以纳米纤维状γ-Al₂O₃为载体，采用工艺路线简单的浸渍法制备了La_xCe_1-xCuMn纳米稀土催化剂，并应用微反活性评价装置测试了对CO和C₃H₈的氧化活性。利用XRD，TEM，BET等手段，分析了产品的结构和粒子形貌。实验结果表明，催化剂活性组分在载体上分散比较均匀，平均粒径在15～20nm之间，为纳米级催化剂。La物质的量为0.4mol、活性组分质量分数为15.04%时，制得了较为纯净的钙钛矿催化剂，CO和 C₃H₈氧化反应中起燃温度分别可以达到161，186℃，且二者的最终转化率均在99%以上。     

Mo-Ni/γ-Al2O3甲烷化催化剂研究(Ⅱ)制备条件及还原条件对催化剂结构的影响

用程序升温还原 ( TPR)、程序升温脱附 ( TPD)、X射线粉末衍射 ( XRD)及透射电子显微镜 ( TEM)等法对分步浸渍法制备的一系列 Mo-Ni/ γ-Al2 O3甲烷化催化剂的结构进行了表征 .考察了浸渍液的 p H值、焙烧温度及还原温度对催化剂的表面结构的影响 .结果表明∶先浸 Mo时 ,调 ( NH4 ) 6Mo7O2 4 溶液的 p H=3、浸 Mo后 50 0℃焙烧的催化剂易于还原 ,而且能抑制后浸 Ni时 ,难还原铝酸盐的形成 ;浸 Ni时 ,调 Ni( NO3) 2 溶液的 p H=8,浸后 4 30℃焙烧的催化剂易于还原 ;浸 Mo后 ,650℃焙烧易形成难还原的 Al2 ( Mo O4 ) 3,浸 Ni后 530℃焙烧的催化剂易形成难还原的 Ni Al2 O4 与类 Ni Al2 O4 铝酸盐 .催化剂于 50 0℃还原时 ,还原态的 Ni最多 ,4 50℃还原时有利于 Mo-Ni合金的形成     

制备方法对NiO/γ-Al2O3催化剂重整活性的影响

利用固定床流动反应装置,研究了NiO/γ-Al2O3催化剂的制备方法对CH4与CO2转化制合成气催化活性的影响.在本实验条件下,采用浸渍法和焙烧温度为400℃制备的NiO/γ-Al2O3(w=0.113)催化剂,在反应温度为750C和空速为2500h-1下,对CH4和CO2重整反应会显示良好的催化活性.本文还对催化剂抗积炭性能作初步讨论.     

V2O5/γ-Al2O3催化四氢糠醇合成吡啶

研究了以四氢糠醇（THFA）、氨为原料，V2O5／γ-Al2O3为催化剂经气固相接触催化合成吡啶的反应．采用XPS、BET时催化剂进行了表征，用气相色谱-质谱联用仪对反应产物进行了分析，确定了主要产物吡啶．考察了反应温度、四氢糠醇流量、V2O5负载量和催化剂用量时反应的影响．结果表明，在反应温度为500℃，n（THFA）：n（NH3）=1：5，V2O5／γ-Al2O3负载量为20％的条件下，四氢糠醇的转化率为93．47％，吡啶的选择性为77．43％。吡啶的反应收率达到72．38％．     

Au/γ-Al2O3催化剂上高浓度甲醇催化消除反应的研究

采用沉积沉淀法制备了负载型Au/γ-Al2O3催化剂,并进行了BET、SEM等表征.对高浓度甲醇蒸汽进行催化消除反应.探讨了载体粒径、金含量和活化气体(O2、N2、H2)对催化剂性能的影响.结果表明:载体粒径不同的催化剂表面积不同,不同的活化气体对反应产物有很大影响.在O2活化的最佳催化剂Au(2.0%)/γ-Al2O3(0.4-0.5 mm)上浓度为86.3 g/m3的甲醇的最低全转化温度是170℃,产物中CO2和甲醚的选择性分别为99.7%和0.3%,达到国家安全排放标准.图1,表3,参16.     

Characteristic parameters and operational curves of γ-Al2O3 nanofiltration membranes

The γ-Al2O3 nanofiltration membranes were manufactured by the sol-gel technique. The result of N2 adsorption and desorption test indicates that the characteristic parameters of the membranes: BJH desorption average pore diameter, BJH desorption cumulative volume of pores and BET surface area are about 3.9 nm, 0.33 cm^3/g and 245 m^3/g respectively, and the pore size distribution is very narrow.The operational curves of γ-Al2O3 nanofiltration membranes of the Ca^2 retention rate vs the trans-membrane pressure,feed concentration of solution treated and pH of solution treated were studied for the first time. It is found that the retention rate for Ca2~ increases with the transmembrane pressure increasing and decreases with the feed concentration of CaCl2 solution increasing. The retention of Ca^2 is very rmuch dependent on the pH of the solution. Minima Ca^2 retention rate is found at the isoelectric point (pH=7.5).     

浸渍法制备的Cu/Al2O3催化剂上仲丁醇的催化脱氢

采用浸渍法制备Cu/Al₂O₃催化剂. 研究了Al₂O_{3< /sub>晶形对催化剂结构和性能的 影响, 考察了催化剂对仲丁醇脱氢活性和选择性的影响. 借助BET, XRD和TPR对催化剂进 行 表征, 结果表明, 载体影响催化剂表面铜物种的存在状态. 对载体进行处理, 可 获得性能较佳的仲丁醇脱氢催化剂.}     

CuO//La2O3/γ-Al2O3合成2-甲基吡嗪的催化性能

用改进的柠檬酸络合法制备了CuO//La2O3/γ-Al2O3催化剂,并通过XRD、NH3-TPD技术对样品进行了表征,探索其对乙二胺(ED)和1,2-丙二醇(PG)为原料合成2-甲基吡嗪(2-MP)反应的催化活性。分别考察了催化剂不同金属配比、煅烧温度以及反应温度、气体空速等对催化剂活性的影响。结果表明:当铜铝摩尔比为4∶6,煅烧温度为700℃时催化剂的催化性能最好;在原料液中1,2-丙二醇、乙二胺和水的摩尔比为1∶1∶2、反应温度为320℃、气体空速(GHSV)1 815 h-1的条件下,1,2-丙二醇的转化率为100%,2-甲基吡嗪的收率为82.7%。     

CaO/γ-Al2O3干法脱除燃煤烟气中砷的实验研究

将γ-Al2O3浸渍于Ca(NO3)2溶液中制备出CaO/γ-Al2O3负载型吸附剂,以贵州省高砷煤为研究对象,运用固定床管式炉对CaO/γ-Al2O3在煤燃烧过程中的除砷性能及影响因素进行了系统研究,并对吸附剂和脱砷产物进行了红外光谱表征和X-射线衍射分析,简单探讨了CaO/γ-Al2O3的除砷机理.实验结果表明:γ-Al2O3在2.0mol.L-1的Ca(NO3)2溶液中浸渍2h后煅烧制得的CaO/γ-Al2O3吸附剂具有最佳脱砷效率,红外图谱中出现的As—O键物质和X-射线衍射图谱中发现的Ca3(AsO4)2也进一步说明了CaO/γ-Al2O3吸附剂能够脱除燃煤烟气中的砷.     

CO选择性氧化催化剂K-Pt/γ-Al2O3催化剂的TPD/TPR研究

用TPD和TPR技术考察了K的添加对CO选择性氧化催化剂Pt/γ-Al2O3的表面吸附性能及还原性能的影响,结合催化剂的活性进行了讨论. 结果表明,添加适量K2O有助于增加弱吸附态CO的数量,并影响Pt的还原过程,使Pt变得难于还原. 当w(K2O)=3.4%时,CO的低温脱附量最大,催化剂还原温度最低. 同时,120 ℃时转化率可达到90%以上.     

一种新的γ-Al2O3制备方法

经蒸发浓缩氯化铝、氨水与扩孔剂草酸铵的混合溶液，生成氢氧化铝沉淀物,再经加热分解除去NH4Cl,所得粉末成型后在550℃下煅烧转化为γ-Al2O3。着重考察扩孔剂加入量，分解温度等对产品性质的影响，与常规制备γ-Al2O3方法比较，本方法省去了老化、过滤、洗涤等步骤，具有缩短制备周期、保护环境等优点。本方法所制γ-Al2O3孔体积大，孔分布集中，压碎强度高。     

真空内氧化法制备α-Al_2O_3/Cu复合材料

对 Cu O-Al体系进行热力学和动力学分析的基础上 ,采用将 Cu O和 Al粉末压块的方法加入到真空条件的 Cu液中使其发生化学反应 ,生成 Al2 O3增强颗粒而获得复合材料。对复合材料进行了扫描电镜观察及 X射线衍射分析 ,并测试了 Al2 O3含量对复合材料电导率的影响。结果表明 ,内氧化法是制备 Al2 O3/ Cu复合材料较理想的方法 ;Al2 O3/ Cu复合材料用于高强度高导电领域时 Al2 O3含量应小于 1 .85 wt%     

γ-Al2O3对铜基甲醇合成催化剂的促进作用

设计并制备了一系列添加隔离剂的铜基甲醇合成催化剂,测试结果显示,添加隔离剂γ-Al2O3对催化剂有明显的促进作用.添加3%γ-Al2O3的铜基甲醇合成催化剂(标记为A3),在2.0MPa、235℃的反应条件下,其合成甲醇的初活性和耐热后的活性分别提高18%和24%.采用TPR和XPS-Auger等谱学方法对催化剂进行表征.结果表明,添加了γ-Al2O3的催化剂的还原温度提高18～23℃,耗氢峰变宽,隔离剂阻止了Cu的深度还原,使工作态催化剂的Cu /Cu0比值更高.     

V2O5/TiO2片状催化剂上NH3选择性还原NOx反应传质情况研究

在固定床反应器中对片状V₂O₅/TiO₂催化剂上NH₃选择性催化还原NO_x 的反应体系进行了传质对反应影响的研究。V₂O₅/TiO₂催化剂上NH₃选择性催化还原NO_x 的反应为1级反应,内扩散对反应速率和NO_x 转化率的影响显著。NO_x 转化率可以表示为空速和其它参数的显函数并获得单一的解析解。实验与模型结果相一致,模型能够较好的反映转化率的变化趋势,为SCR反应器的优化设计提供理论依据。