C-Si-Mn系热轧双相钢显微组织与力学性能之间的关系

通过对热轧试样的组织性能测试,研究了热轧双相钢显微组织与力学性能之间的关系.研究发现,铁素体和马氏体强度是影响力学性能的主要因素.建立了C-Si-Mn系热轧双相钢力学性能的数学模型,可以作为热轧双相钢基本力学性能参数预测的理论依据.     

锰对热轧态双相钢显微组织和力学性能的影响

用薄晶体透射电镜研究锰对热轧空冷后低碳Si—Mn双相钢的组织和力学性能的影响。实验结果表明:钢中锰含量为1.79％时,显微组织中出现珠光体。拉伸工程应力—应变曲线有明显物理屈服延伸。钢中锰含量越少、珠光体量越多时,应力—应变曲线上屈服平台越长。锰含量大于2.09％时,轧态组织中不再出现非马氏体型转变产物珠光体。轧态组织中的马氏体岛区,由几个微区组成。这些微区分别为内孪晶马氏体区和位错板条马氏体区。     

变形工艺对热轧双相钢显微组织和性能的影响

以热轧双相钢为研究对象,在实验室通过热轧实验,研究了变形量、卷取温度、终轧温度对高强热轧双相钢组织细化和力学性能的影响.通过研究可以发现,变形工艺参数对热轧双相钢的显微组织和力学性能有很大的影响,热轧双相钢的显微组织主要有三种典型微观形貌,而这三种典型形貌又赋予了双相钢不同的强韧化机制和力学性能.在实验室条件下,开发了780 MPa级以Mn,Si为主要添加元素的热轧双相钢生产工艺,可以使热轧双相钢的屈服强度达到要求的级别,并且断后伸长率良好.     

超高强度冷轧双相钢组织与性能

在Gleeble-3500热模拟试验机上进行冷轧超高强度双相钢的连续退火工艺研究,利用光学显微镜、扫描电镜、透射电镜和拉伸试验研究了连续退火过程中各个参数对1 000 MPa级冷轧双相钢组织性能的影响.结果表明:试验用钢在退火温度800℃下保温80 s,可以得到抗拉强度为1030MPa、延伸率为14%超高强双相钢;随着退火温度的升高,屈服强度和抗拉强度降低.当退火温度为830℃时,显微组织中粒状的非马氏体组织明显增多.过时效温度低于300℃时,屈服强度和抗拉强度变化不大;当过时效温度超过300℃时,抗拉强度急剧下降,屈服强度先降低后升高,在过时效温度为360℃时开始出现屈服平台.     

显微组织对双相钢Bauschinger效应及残余相应力的影响

本文应用有限单元法分析了预变形、粒子尺寸、体积分数和组分相的屈服强度比对双相钢的 Bauschinger Effect(BE)及残余相应力的影响.对 BE 和残余相应力之间的关系、非弹性卸载、卸载塑性及反向变形对 BE 和残余相应力的影响也作了讨论.一些计算分析和相应的实验结果相比较,符合较好.     

热轧态双相钢压缩形变后的回复与再结晶

利用透射电镜（ＴＥＭ）观察了热轧态双相钢压缩态相钢压缩形变后回复与再结晶过程的组织结构变化，研究了硅及形变量的影响。结果表明：硅明显地延迟试验钢回复与再结晶过程。经３０％形变的试验钢的回复与再结晶过程，迟于经９０％的同样过程，由硬度（ＨＲＣ），试验钢再结晶过程的激活能。     

分段冷却模式下热轧双相钢的组织演变及力学性能

通过热模拟实验研究了分段冷却模式下变形温度、保温温度及保温时间对Nb-Ti微合金热轧双相钢组织演变及性能的影响.结果表明:降低变形温度可促进铁素体的转变,使马氏体形态由大块状过渡到岛状;保温温度从740℃逐渐降至580℃时,铁素体转变量先增加后减少,保温温度为660℃时铁素体转变量达到峰值;随保温时间延长铁素体转变量增加,且铁素体转变量与时间的关系曲线呈“S”型.采用超快冷+空冷+层流冷的冷却模式并通过调整终轧温度及空冷时间获得了630~710MPa的热轧双相钢,屈强比≤061,相应的组织为铁素体+马氏体或铁素体+马氏体+少量的贝氏体.     

Effect of hot-dip galvanizing processes on the microstructure and mechanical properties of 600-MPa hot-dip galvanized dual-phase steel

A C-Mn dual-phase steel was soaked at 800℃ for 90 s and then either rapidly cooled to 450℃ and held for 30 s (process A) or rapidly cooled to 350℃ and then reheated to 450℃ (process B) to simulate the hot-dip galvanizing process. The influence of the hot-dip galvanizing process on the microstructure and mechanical properties of 600-MPa hot-dip galvanized dual-phase steel (DP600) was investigated using optical microscopy, scanning electron microscopy (SEM), transmission electron microscopy (TEM), and tensile tests. The results showed that, in the case of process A, the microstructure of DP600 was composed of ferrite, martensite, and a small amount of bainite. The granular bainite was formed in the hot-dip galvanizing stage, and martensite islands were formed in the final cooling stage after hot-dip galvanizing. By contrast, in the case of process B, the microstructure of the DP600 was composed of ferrite, martensite, bainite, and cementite. In addition, compared with the yield strength (YS) of the DP600 annealed by process A, that for the DP600 annealed by process B increased by approximately 50 MPa because of the tempering of the martensite formed during rapid cooling. The work-hardening coefficient (n value) of the DP600 steel annealed by process B clearly decreased because the increase of the YS affected the computation result for the n value. However, the ultimate tensile strength (UTS) and elongation (A₈₀) of the DP600 annealed by process B exhibited less variation compared with those of the DP600 annealed by process A. Therefore, DP600 with excellent comprehensive mechanical properties (YS=362 MPa, UTS=638 MPa, A₈₀=24.3%, n=0.17) was obtained via process A.     

Effects of overaging temperature on the microstructure and properties of 600 MPa cold-rolled dual-phase steel

C–Mn steels prepared by annealing at 800°C for 120 s and overaging at 250–400°C were subjected to pre-straining (2%) and baking treatments (170°C for 20 min) to measure their bake-hardening (BH2) values. The effects of overaging temperature on the microstructure, mechanical properties, and BH2 behavior of 600 MPa cold-rolled dual-phase (DP) steel were investigated by optical microscopy, scanning electron microscopy, and tensile tests. The results indicated that the martensite morphology exhibited less variation when the DP steel was overaged at 250–350°C. However, when the DP steel was overaged at 400°C, numerous non-martensite and carbide particles formed and yield-point elongation was observed in the tensile curve. When the overaging temperature was increased from 250 to 400°C, the yield strength increased from 272 to 317 MPa, the tensile strength decreased from 643 to 574 MPa, and the elongation increased from 27.8% to 30.6%. Furthermore, with an increase in overaging temperature from 250 to 400°C, the BH2 value initially increases and then decreases. The maximum BH2 value of 83 MPa was observed for the specimen overaged at 350°C.     

一种超高强度钢组织性能的研究

通过力学测试、金相、扫描电镜观察等方法研究了不同淬火温度下一种淬火 低温回火超高强度钢的组织性能,系统的探讨了未溶相与淬火温度的关系。结果表明：钢采用低于950℃的淬火温度,组织中存在大量未溶碳化物,当温度高于1010℃时,未溶碳化物基本溶解,马氏体板条束明显粗化,对钢的力学性能有害,适宜的淬火温度为1010℃。     

纤维双相钢的组织形成及对性能的影响

研究了纤维双相15Mn2Nb钢组织的形成及对性能的影响.结果表明,纤维双相钢具有优异的强塑性匹配,是一种天然的复合材料.其纤维组织的获取主要取决于合金化和热处理工艺规程,而合金元素Nb阻碍铁素体再结晶是形成纤维组织的关键.     

Cr元素对冷轧TRIP钢的组织性能影响研究

以两种合金成分的相变诱导塑性钢为实验对象,先利用热模拟试验机确定其热轧及热处理参数后,经过热轧、冷轧工艺并连续退火,研究其力学性能。金相组织及宏观织构的特征。实验结果表明,Cr元素可以稳定低温奥氏体,降低贝氏体形成温度,使贝氏体的孕育期延长,增加最终组织中的贝氏体及残余奥氏体的体积分数;Cr元素的添加还增强了试验钢的力学性能,添加了Cr元素的2#钢强度和塑性均比没有添加的1#钢要高;两种成分的TRIP钢织构情况相似,主要组分包括：{332}纤维织构,{110}<001>组分和{112}<110>组分,可见Cr元素在提高钢板强度增加延伸率的同时,并没有损害钢板的成形性能。     

退火温度对430不锈钢冷轧板组织和力学性能的影响

针对现场生产的430不锈钢冷轧板,通过高温连续退火实验研究了退火温度对材料显微组织、强度、塑性以及各向异性性能的影响.通过实验得到了合理的两段式加热连续退火工艺:选取中间温度为600℃,加热II段的加热速率为2.3℃·s-1,最高加热温度为840℃.随着退火温度的升高,薄板的屈服强度和硬度呈明显的两阶段降低趋势,延伸率呈"S"型趋势增加,平均塑性应变比基本保持不变(1.25左右),而轧制平面各向异性指数有一定的降低.针对430不锈钢冷轧板分别建立了屈服强度与退火软化率和延伸率之间的定量关系.     

预处理组织对低碳钢IQ&P工艺下组织及性能影响

采用γ单相区和γ+α双相区轧制并淬火工艺以及双相区再加热-淬火-碳配分( IQ&P)工艺,研究预处理组织对低碳钢室温状态多相组织特征及力学性能的影响规律. 实验用低碳钢经两种工艺轧制并淬火处理,获得马氏体和马氏体+铁素体的预处理组织,再经双相区IQ&P工艺处理后均获得多相组织. 马氏体预处理钢的室温组织由板条状亚温铁素体、块状回火马氏体以及一定比例的针状未回火马氏体和8. 2%的针状残余奥氏体组成;马氏体+铁素体预处理钢由板条状亚温铁素体、块状和针状未回火马氏体以及14. 3%的短针状或块状残余奥氏体组成. 在相同的双相区IQ&P工艺参数下,预处理组织为马氏体的钢抗拉强度为770 MPa,伸长率为28%,其强塑积为21560 MPa·%;而预处理组织为马氏体+铁素体的钢抗拉强度为834 MPa,伸长率增大到36. 2%,强塑积达到30190 MPa·%,获得强度与塑性的优良结合.     

热轧高碳钢线材组织-性能预报系统

在模拟实验和工业试验验证的基础上,建立了高碳钢高速线材在轧制和冷却过程中组织演变及力学性能系列模型,包括临界应变、奥氏体动态及静态再结晶、奥氏体相变体积分数、珠光体片间距以及组织-性能关系等子模型.基于以上模型,开发了一个模拟程序,对高速线材生产的物理冶金过程进行了仿真计算,得到轧件的温度场、奥氏体晶粒尺寸演变、最终组织特征和力学性能.模拟结果显示主要轧制温度及最终组织性能与现场实测结果吻合较好.     

退火温度对退火马氏体基TRIP钢显微组织和力学性能的影响

将C-Si-Mn系TRIP钢通过完全淬火和两相区退火相结合的工艺,得到一种以退火马氏体为基体的TRIP钢(简称TAM钢),并对比分析了TAM钢在不同温度退火后的显微组织和力学性能.结果表明,TAM钢经退火后的显微组织特征为精细规整的板条退火马氏体基体、片状残余奥氏体和贝氏体/马氏体组成的混合组织.这种组织降低了基体的硬度以及基体和第二相之间的强度比,减少了基体的位错密度.随着退火温度的提高,退火马氏体基体的板条形态逐渐消失,新生马氏体/贝氏体的团状混合组织逐渐增多.当退火温度为780℃时,综合力学性能优异,抗拉强度为1130 MPa,延伸率可达20%,强塑积为22600 MPa·%.当退火温度较低时,残余奥氏体主要以片状存在于退火马氏体板条间,有利于TRIP效应的发生.