A356合金近液相线法铸造坯料及重熔加热组织研究

采用近液相线半连续铸造法制备了A356铝合金半固态坯料,并利用电阻炉加热,采用电子显微镜研究了近液相线铸造A356铝合金在二次加热过程中的组织演变.结果表明:A356铝合金半固态坯料组织呈均匀、细小的蔷薇状分布;在585℃加热,保温10~15 min,可获得半固态加工所需的触变性组织.而且,保温温度和保温时间共同影响着二次加热组织的演变过程.随着加热温度的升高,α相的生长和球化的速度变快,保温时间越长,晶粒球化度越高.     

A2017半固态合金二次加热组织演化

对SCR技术制备的A2017半固态坯料进行二次加热,利用光学显微镜,电镜,图像分析仪等手段,对坯料二次加热微观组织的演化进行了研究·实验结果表明,在相同加热温度条件下,随着保温时间的延长,晶粒平均等积圆直径增大,晶粒越来越圆整,液相率增加;提高二次加热温度,晶粒长大和球化速度加快·二次加热最佳工艺条件为加热温度580℃,保温时间40～60min或者加热温度600℃,保温20～40min,晶粒平均等积圆直径为70～90μm,固相率在70%左右,适合于半固态加工·组织演化机制分析表明,加热初期阶段,液相少,晶粒主要通过碰撞熔合快速长大;随着保温时间延长,液相增加,晶粒主要通过原子扩散慢速长大并发生...     

6061合金电磁半连续铸锭与二次加热组织研究

用电磁半连续铸造技术制备6061合金半固态坯料,并在不同的保温温度和保温时间下进行二次加热实验,观察铸锭及二次加热坯料的微观组织,研究保温温度和保温时间对二次加热淬火组织的影响.结果表明:6061合金可以通过电磁半连续铸造获得具有细小、均匀、非枝晶组织的铸锭;二次加热过程中,随着保温温度的升高,组织转变速度加快;保温温度过高,淬火组织粗大,对成形件性能不利;随着保温时间的增加,初生α-Al不断球化,淬火组织也越圆整,但晶粒长大明显;在610~630℃下保温10~15 min,所得淬火组织均匀,晶粒细小,是理想的成形组织.     

液相线半连续铸造7075铝合金半固态组织演变

研究了液相线半连续铸造法生产的7075铝合金半固态浆料二次加热时组织的演变和主要合金元素的分布·结果表明,液相线铸造7075铝合金在相同加热温度下,随着保温时间的延长,晶粒尺寸与球化倾向增大;在相同保温时间下,随着加热温度的升高,晶粒尺寸与球化倾向也增加·加热温度580℃左右,保温时间在15～30min之间,和加热温度600℃左右,保温时间在5～15min之间,可以将半连续铸造锭坯中的蔷薇状和近球状组织转化为球形晶粒,晶粒的平均直径范围为40～55μm,完全适合于半固态加工·液相线铸造7075铝合金二次加热组织中,主要合金元素M...     

过共晶铝硅合金半固态二次加热时组织演变

利用热涵法、液淬技术和金相分析等手段,研究了预变形后的过共晶铝硅合金在进行半固态二次加热时组织演变规律.结果表明,半固态组织演变经历以下几个阶段:共晶硅熔断、粒化,共晶组织逐渐熔化成液相,液相体积分数逐渐增加并包围α相,α相趋于近球形的组织,共晶组织完全熔化等几个阶段.在二次加热过程中,初生硅颗粒也发生了一定的球化.     

TiC_p/7075Al基复合材料半固态坯料二次加热组织

利用扫描电镜(SEM)、透射电镜(TEM)和示差扫描量热法(DSC)研究了4.4%TiC_p/7075Al基复合材料的二次加热组织演变规律及其影响因素. 结果表明:4.4%TiC_p/7075Al基复合材料的最佳二次加热工艺参数是加热温度为590～610℃,保温时间为10～20min;4.4%TiC_p/7075Al基复合材料在二次加热过程中具有较高的稳定性,随温度的升高和保温时间的延长,球形晶粒尺寸增加较小;4.4%TiC_p/7075Al基复合材料在600℃时的晶粒粗化速率常数为118.96μm~3·s~(-1),远小于7075基体合金的晶粒粗化速率常数311.7μm~3·s~(-1),更加适宜于半固态触变成形.     

超超临界机组叶片钢KT5331晶粒长大行为

通过在不同温度下等温奥氏体化,研究KT5331钢奥氏体晶粒长大行为,并探讨析出相对奥氏体晶粒长大行为的影响机理. 研究表明,KT5331钢奥氏体晶粒长大可分为三个阶段:1075℃以下,由于含W和Nb的析出相钉扎作用,晶粒长大缓慢;1075℃以上,含W和Nb的析出相溶解,钉扎作用减弱,随加热温度和保温时间延长晶粒迅速长大;1225℃及以上,δ铁素体析出,晶粒尺寸随加热温度升高而急剧减小. 通过拟合分别得到晶粒粗化温度以下( 950~1075℃)和晶粒粗化温度以上(1100~1200℃)的晶粒长大模型.     

形变对板条马氏体回火组织的影响

对Q235级低碳钢板条马氏体在550 ℃多道次单向压缩变形后退火和室温大塑性变形轧制后在此温度退火的显微组织演变规律进行了对比研究,结合未变形板条马氏体在此温度的回火组织演变,讨论了变形对马氏体分解过程、铁素体再结晶晶粒尺寸和析出碳化物形貌的影响. 实验结果表明,变形显著影响马氏体分解过程,促进渗碳体的析出和铁素体回复及再结晶. 热变形组织铁素体再结晶晶粒尺寸在0.5 μm左右;渗碳体形貌从细棒状向球状转变,随变形量增大渗碳体尺寸增大,继续保温60 min导致铁素体晶粒长大到1 μm左右,晶粒内部的渗碳体消失,原先在铁素体晶界析出的渗碳体球化、粗化. 冷轧试样在550 ℃退火保温时间在30 min内得到0.3～0.4 μm超细晶粒和尺度小于150 nm的弥散渗碳体颗粒组织;随退火保温时间延长到60 min,铁素体再结晶晶粒长大到1.9 μm,渗碳体颗粒尺寸约160 nm.     

机车车轮用钢奥氏体晶粒的长大行为

采用金相显微镜和截距法,对不同加热温度和保温时间下机车车轮用钢的奥氏体晶粒长大行为进行研究,分析加热温度和保温时间对奥氏体晶粒尺寸的影响,应用简单动力学模型对奥氏体晶粒的长大过程进行分析,同时研究钢中第二相粒子变化对奥氏体晶粒长大的影响.随着加热温度的升高和保温时间的延长,奥氏体晶粒尺寸明显增加,加热温度对晶粒的长大影响更明显.奥氏体晶粒长大的动力学时间指数随着温度升高而增加且其值均接近理论值0.5;奥氏体晶粒长大和钢中第二相粒子AlN体积分数和尺寸的变化呈明显的相关性.     

奥氏体化温度对低碳铬钼镍轴承钢晶粒尺寸、碳化物及韧性的影响规律

为了探究低碳铬钼镍轴承钢在不同热处理工艺下组织和韧性的变化规律,对其进行奥氏体等温保温实验,研究了加热温度、保温时间对低碳铬钼镍轴承钢奥氏体晶粒尺寸、碳化物和冲击功的影响。结果表明:奥氏体化温度≤1 070℃时,钢中碳化物溶解不明显,碳化物面积占比为1.93%,奥氏体晶粒长大不明显,平均晶粒尺寸为49μm,冲击功>50 J;奥氏体化温度≥1 080℃时,碳化物面积占比为1.23%,1 090℃时碳化物面积占比为0.16%,碳化物大量溶解,产生解钉效应,奥氏体晶粒明显长大,冲击功大幅下降,低于30 J;保温时间大于45 min时,晶粒尺寸趋于稳定。根据实验结果得出试验钢在1 050～1 090℃加热并保温15～60 min的晶粒长大模型,可为该钢种热处理工艺的设计提供理论依据。     

ZL201合金低频电磁铸造与二次加热的合金组织

采用低频电磁铸造技术制备ZL201合金半固态坯料,研究了电磁场频率以及二次加热温度和保温时间对合金微观组织的影响.结果表明,随着电磁场频率从10 Hz增大到30 Hz,组织的枝晶化趋势逐渐减弱,当电磁场频率为30 Hz时,可以获得均匀、细小的蔷薇状和等轴晶组织.对电磁场频率为30 Hz时铸造的半固态坯料进行二次加热表明,当二次加热温度为630℃,保温20 min后,铸造组织逐渐转变为均匀的近球形组织,具有良好的触变成形性.     

Effect of prolonged isothermal heat treatment on the mechanical behavior of advanced NANOBAIN steel

The microstructural evolution and consequent changes in strength and ductility of advanced NANOBAIN steel during prolonged isothermal heat-treatment stages were investigated. The microstructure and mechanical properties of nanostructured bainite were not expected to be influenced by extending the heat-treatment time beyond the optimum value because of the autotempering phenomenon and high tempering resistance. However, experimental results indicated that the microstructure was thermodynamically unstable and that prolonged austempering resulted in carbon depletion from high-carbon retained austenite and carbide precipitations. Therefore, austenite became thermally less stable and partially transformed into martensite during cooling to room temperature. Prolonged austempering did not lead to the typical tempering sequence of bainite, and the sizes of the microstructural constituents were independent of the extended heat-treatment times. This independence, in turn, resulted in almost constant ultimate tensile strength values. However, microstructural variations enhanced the yield strength and the hardness of the material at extended isothermal heat-treatment stages. Finally, although microstructural changes decreased the total elongation and impact toughness, considerable combinations of mechanical properties could still be achieved.     

AlSi7MgBe合金半固态坯料制备及其触变成形

采用近液相线半连续铸造技术制备AlSi7MgBe合金半固态坯料,研究制坯工艺以及二次加热温度和保温时间对半固态浆料微观组织的影响,通过组织与性能分析对AlSi7MgBe合金的半固态触变成形性进行了研究.研究结果表明,AlSi7MgBe合金采用近液相线半连续铸造,坯料具有均匀、细小的蔷薇状组织.当二次加热温度为595℃,保温15 min时,能够得到适合于进行半固态触变成形的球化组织.对近液相线半连续铸造AlSi7MgBe合金坯料进行半固态触变成形,可以获得轮廓清晰、组织致密的成形件,成形件的组织与性能得到改善,与液态模锻工艺相比,硬度提高20%.     

电感应再加热对低合金钢热轧组织影响的模拟

利用热模拟试验机Gleeble1500D研究了低合金钢变形后,冷却至一定温度进行电感应再加热后微观组织的变化情况.在不同冷却温度,以及淬火和正火两种热处理方式下,研究了再加热过程对微观组织的影响.结果表明:变形后再加热过程对淬火试样组织影响较大;冷却温度处于两相区时,电感应再加热过程能改善温度分布均匀性,影响铁素体相变过程和碳氮化物的析出行为,促进晶粒长大,能够有效地控制和改善淬火热处理钢材的微观组织和性能.     

低碳钢形变诱导相变组织在冷却过程中的晶粒长大

通过热模拟实验考察了低碳钢在略高于Ar3温度变形时发生形变诱导铁素体相变(DIFT)的组织演变规律;探讨了变形后连续冷却以及在不同温度下保温对DIFT组织的影响·结果表明,DIFT组织含量随变形量的增大而增多,但在较大的变形量下仍然有部分奥氏体没有发生DIFT;在随后的冷却过程中,未转变奥氏体通过静态相变形成粗大的铁素体,与形变诱导铁素体组织一起形成混晶组织·DIFT铁素体晶粒在形变后冷却过程中发生长大现象·实验测定和理论计算结果都表明,在连续冷却条件下,形变诱导组织存在晶粒长大终止温度,当温度低于该温度时DIFT晶粒停止长大;在不同温度等温时,也存在DIFT晶粒稳定的温度上限,在低于该温度保...     

球墨铸铁中渗碳体球化的影响

The research aims to provide an alternative to austempering treatment of ductile cast iron with a simple and cost-effective heat-treatment process. This goal was accomplished by applying a simple one-step spheroidization heat treatment to the as-cast ductile iron, which would normally possess a coarse pearlitic microstructure to a significant extent. Spheroidization experiments involving isothermal holding below the lower critical temperature (A1) were conducted followed by standard mechanical testing and microstructural characterization for an experimental ductile iron. After improving the spheroidization holding time at a given temperature, the work shows that the ductility and toughness of an as-cast ductile iron can be improved by 90% and 40%, respectively, at the cost of reducing the tensile strength by 8%. Controlled discretization of the continuous cementite network in pearlitic matrix of the ductile iron is deemed responsible for the improved properties. The work also shows that prolonged holding time during spheroidization heat treatment leads to degradation of mechanical properties due to the inhomogenous microstructure formation caused by heterogeneous decomposition and cementite clustering in the material. The main outcome of this work is the demonstration of ductile cast iron’s necking behavior due to spheroidization heat treatment.     

分段冷却模式下热轧双相钢的组织演变及力学性能

通过热模拟实验研究了分段冷却模式下变形温度、保温温度及保温时间对Nb-Ti微合金热轧双相钢组织演变及性能的影响.结果表明:降低变形温度可促进铁素体的转变,使马氏体形态由大块状过渡到岛状;保温温度从740℃逐渐降至580℃时,铁素体转变量先增加后减少,保温温度为660℃时铁素体转变量达到峰值;随保温时间延长铁素体转变量增加,且铁素体转变量与时间的关系曲线呈“S”型.采用超快冷+空冷+层流冷的冷却模式并通过调整终轧温度及空冷时间获得了630~710MPa的热轧双相钢,屈强比≤061,相应的组织为铁素体+马氏体或铁素体+马氏体+少量的贝氏体.     

一种低焊接裂纹敏感性钢的奥氏体粗化温度研究

通过高温淬火试验观察试验钢奥氏体晶粒尺寸的变化情况.结合金相和TEM观察、显微硬度和第二相粒子的溶解度积公式分析了加热温度和保温时间对试验钢奥氏体晶粒粗化温度、第二相粒子的溶解情况以及显微硬度值的影响.结果表明:试验钢的奥氏体粗化温度在1200℃附近.当加热温度低于1200℃时,大量细小的第二相粒子阻碍奥氏体晶粒粗化;当加热温度高于1200℃时,细小的第二相粒子溶解,奥氏体晶粒出现异常长大.确定试验钢的合理加热温度为1150～1200℃,在此范围内可获得淬火组织的显微硬度值低于HV330.