Co²⁺/γ-Al₂O₃ samples were prepared by incipient wetness impregnation of γ-Al₂O₃ with different concentration solution of CoCl₂ and dried at 40 °C. We measured the positron lifetime spectra of the samples of different Co²⁺ mass fractions (0%–8.24%) heated at different temperatures (100–500°C). All lifetime spectra were resolved into four components, in which the third and the fourth components were related to the surface state of the micropores and the secondary pores of the γ-Al₂O₃. The experimental results showed that the Co²⁺ was mainly located in the micropores and the secondary pores near to the exterior of the support. For low Co²⁺ mass fraction samples, when the heating temperature was above 400 °C, dispersal was almost finished. When the Co²⁺ mass fraction was above 5.59%, Co²⁺ and Cl⁻ were dispersed into the secondary pores in the form of multiple layers.     

非均相Fenton反应催化剂Fe2O3/γ-Al2O3的制备及其性能

采用等体积浸渍法制备非均相Fenton反应催化剂Fe2O3/γ-Al2O3,以对羟基苯丙酸为降解目标物,考察了γ-Al2O3粒径的大小、浸渍时间、焙烧温度、焙烧时间、负载量等因素对催化剂催化活性的影响.通过热重、XRD、电镜扫描对催化剂形貌和特征的分析以及催化反应的结果分析可知,在γ-Al2O3上负载了催化剂Fe2O3,但Fe2O3并不均匀,在γ-Al2O3为100~120目,负载量为11.7%,浸渍10,h,焙烧温度为550,℃,焙烧4,h,与60,mg/L的对羟基苯丙酸反应60,min的条件下,催化剂的活性最好,对羟基苯丙酸的去除率可达到70.26%.重复实验说明催化剂的稳定性较好.     

CuO//La2O3/γ-Al2O3合成2-甲基吡嗪的催化性能

用改进的柠檬酸络合法制备了CuO//La2O3/γ-Al2O3催化剂,并通过XRD、NH3-TPD技术对样品进行了表征,探索其对乙二胺(ED)和1,2-丙二醇(PG)为原料合成2-甲基吡嗪(2-MP)反应的催化活性。分别考察了催化剂不同金属配比、煅烧温度以及反应温度、气体空速等对催化剂活性的影响。结果表明:当铜铝摩尔比为4∶6,煅烧温度为700℃时催化剂的催化性能最好;在原料液中1,2-丙二醇、乙二胺和水的摩尔比为1∶1∶2、反应温度为320℃、气体空速(GHSV)1 815 h-1的条件下,1,2-丙二醇的转化率为100%,2-甲基吡嗪的收率为82.7%。     

乙酸改性γ-Al2O3高效去除痕量PCl3的研究

在多晶硅生产过程中,为了不影响产品性能,必须将杂质PCl₃的含量降低到ppb的水平,然而,这目前仍旧是一个巨大的挑战。本研究提出了一种可高效去除痕量PC1₃的方法,即利用乙酸改性γ-Al₂O₃作为吸附剂,其可去除ppb级别的PC1₃,去除率高达84.2%。Boehm滴定实验表明,改性后的γ-Al₂O₃表面羧基含量大幅增加,从而增加了吸附PCl₃的活性位点,使其对PCl₃的吸附性能显著提升。表征分析和DFT模拟计算表明,乙酸与γ-Al₂O₃主要是通过γ-Al₂O₃中的羟基H和乙酸中的羰基O形成氢键而相互作用的;除了物理吸附外,γ-Al₂O₃中的Al与PCl₃中的Cl,以及乙酸中的羰基O与PCl₃中的P之间还可通过电荷转移...     

Pd/γ-Al2O3催化剂作用下对苯醌加氢制备对苯二酚

采用浸渍法制备了负载型钯催化剂（Pd/γ-Al₂O₃）,并将制备的催化剂应用于对苯醌加氢制备对苯二酚反应. 考察了不同反应温度、压力、时间、催化剂用量等因素对Pd/γ-Al₂O₃催化剂性能的影响. 以甲醇（CH₄O）作为溶剂,在反应温度为30 ℃、氢气（H₂）压力为3.0 MPa、反应时间为2 h、对苯醌和甲醇的质量比m（对苯醌）:m（甲醇）=3:47、催化剂质量分数仅为0.25%（以对苯醌质量计）的条件下,对苯醌转化率为100%,对苯二酚的选择性为96.9%,产率为96.9%.     

制备方法对NiO/γ-Al2O3催化剂重整活性的影响

利用固定床流动反应装置,研究了NiO/γ-Al2O3催化剂的制备方法对CH4与CO2转化制合成气催化活性的影响.在本实验条件下,采用浸渍法和焙烧温度为400℃制备的NiO/γ-Al2O3(w=0.113)催化剂,在反应温度为750C和空速为2500h-1下,对CH4和CO2重整反应会显示良好的催化活性.本文还对催化剂抗积炭性能作初步讨论.     

高湿度条件下O3在MnOx/γ-Al2O3催化剂上的分解

用共沉淀法制备了一系列MnOx/γ-Al     

K2CO3/Al2O3固体碱催化酯化原油脱酸

开发高效催化剂是提高原油催化酯化脱酸效率的关键。将K2CO3/Al2O3固体碱催化剂用于原油的酯化脱酸,用XRD、N2吸附-脱附、Hammett指示剂-苯甲酸滴定法表征催化剂性质,研究活性组分含量及酯化反应条件对催化剂性质和活性的影响。结果表明:当K2CO3负载量为25%时,活性组分呈多层分散,催化剂比表面积和孔体积显著下降。催化剂的总碱量(H->9.3)和弱碱量(9.3相似文献   

CaO/γ-Al2O3干法脱除燃煤烟气中砷的实验研究

将γ-Al2O3浸渍于Ca(NO3)2溶液中制备出CaO/γ-Al2O3负载型吸附剂,以贵州省高砷煤为研究对象,运用固定床管式炉对CaO/γ-Al2O3在煤燃烧过程中的除砷性能及影响因素进行了系统研究,并对吸附剂和脱砷产物进行了红外光谱表征和X-射线衍射分析,简单探讨了CaO/γ-Al2O3的除砷机理.实验结果表明:γ-Al2O3在2.0mol.L-1的Ca(NO3)2溶液中浸渍2h后煅烧制得的CaO/γ-Al2O3吸附剂具有最佳脱砷效率,红外图谱中出现的As—O键物质和X-射线衍射图谱中发现的Ca3(AsO4)2也进一步说明了CaO/γ-Al2O3吸附剂能够脱除燃煤烟气中的砷.     

Synthesis of PbS–K2La2Ti3O10 composite and its photocatalytic activity for hydrogen production

Photocatalyst, lead sulfide (PbS )-intercalated layer perovskite-type compound (K2La2Ti3O10), was synthesized via ion-exchange reaction, butylamine pillaring and sulfuration processes under the assistance of the microwave irradiation. The structure of the photoc atalysts was determined by means of powder X-ray diffraction, scanning electron microscope, ultraviolet- visible diffuse reflection spectra and photoluminescence measu rement. And the photocatalytic activity of the composite compound for hydrogen production was also investigated. The experimental results showed that the intercalation of PbS in the layered space of K2La2Ti3O10 greatly improved the absorption edge and the photocatalytic activity. Hydrogen production of the PbS–K2La2Ti3O10 was 127.19 mmol/(g cat) after 3 h irradiation of ultraviolet light.     

In-situ fabrication of Al(Zn)-Al2O3 graded composite using the aluminothermic reaction during hot pressing

In this study, the fabrication of multilayer Al(Zn)–Al₂O₃ with different volume fractions of Al₂O₃ was investigated. Al and ZnO powders were milled by a planetary ball mill, after which five-layer functionally graded samples were produced through hot pressing at 580℃ and 90 MPa pressure for 30 min. Formation of reinforcing Al₂O₃ particles occurred in the aluminum matrix via the aluminothermic reaction. Determination of the ignition temperature of the aluminothermic reaction was accomplished using differential thermal and thermogravimetric analyses. Scanning electron microscopy, energy dispersive spectroscopy, and X-ray diffractometery analyses were utilized to characterize the specimens. The thermal analysis results showed that the ignition temperatures for the aluminothermic reaction of layers with the highest and lowest ZnO contents were 667 and 670℃, respectively. Microstructural observation and chemical analysis confirmed the fabrication of Al(Zn)–Al₂O₃ functionally graded materials composites with precipitation of additional Zn in the matrix. Moreover, nearly dense functionally graded samples demonstrated minimum and maximum hardness values of HV 75 and HV 130, respectively.     

α-Al2O3陶瓷与金属镍的真空扩散焊

为研究α-Al2O3陶瓷和金属镍之间的扩散焊接,以α-Al2O3陶瓷和高纯金属镍为母材,通过真空扩散焊的方法,考察焊接温度、压力及保温时间对焊接效果的影响。采用电子万能试验机测试工件的焊接强度,用扫描电镜(SEM)观察陶瓷与金属界面的显微结构,用能谱仪(EDS)研究焊接面的扩散情况。结果表明:用Mo-Mn法将陶瓷表面金属化,在θ=1 164℃、p=7.5 MPa、t=30 min的实验焊接条件下,具有较强的扩散能力,金属镍向α-Al2O3陶瓷一侧扩散渗透,实现了α-Al2O3陶瓷与金属镍的连接。     

TiO2/Al2O3-Al2O3-TiO2/Al2O3绝缘结构的真空沿面闪络特性

基于变插入层介电常数的多层绝缘结构能改善电场分布、提高真空沿面闪络特性.通过真空热压烧结制备了TiO2/Al2O3-Al2O3-TiO2/Al2O3(A-B-A)3层绝缘结构,A层w(TiO2)为0.5%到20%.测量了该绝缘结构的真空沿面闪络特性,发现闪络特性随w(TiO2)的增加而提高,当w(TiO2)为20%时,其脉冲初次闪络电压较同等厚度的Al2O3陶瓷提高了63%.研究发现:A层的介电常数可由w(TiO2)调控,介电常数的增大能有效降低真空-绝缘子-阴极三结合点处的电场强度;A层表面存在的TiO2颗粒可以减小二次电子发射系数并改善表面电荷分布;TiO2的电导率虽比Al2O3高,但其仍为绝缘体,即使TiO2含量较高时也不会形成贯穿的导电通道.     

两种液相法制备超细γ-Al2O3粉体的形貌及纯度的研究

超细氧化铝因其优良的机械性能及耐高温、耐腐蚀、高强度的物理性能得以广泛应用.采用液相法制备超细氧化铝粉体即通过沉淀法、溶胶-凝胶法制备出形貌规则、分散性好,粒径较小的氧化铝纳米粉体.纳米氧化铝粉体通过X射线衍射仪(XRD),马尔文纳米粒度仪,扫描电子显微镜(SEM)等进行表征.探究使用不同方法制备的氧化铝纳米粉体的形貌、粒径及结晶情况之间的差异,以及相同方法加不同用量的分散剂对粉体的粒径和形貌的影响.根据表征结果发现在该条件下制备出的粉体为γ-Al₂O₃,SEM结果表明沉淀法制备出的粉体为结晶状态较好、形状均匀的球形Al₂O₃粉体,使用溶胶凝胶法制备的粉体为蠕虫状的Al₂O₃粉体,但相较于沉淀法,采用溶胶凝胶法制备的粉体粒径较小.     

H3PW12O40/H2O2/H2O体系催化氧化苯甲醇合成苯甲醛

合成一系列杂多酸(盐)并采用红外光谱对其进行表征,研究它们对苯甲醇氧化合成苯甲醛反应的催化性能.并以H3PW1 2O40为催化剂,分别考察溶剂类型、反应时间、反应温度、催化剂用量和H2O2用量对该反应的影响,并且初步探讨该反应的反应机理.实验结果表明:5种杂多酸(盐)均具有Keggin型结构,以水为溶剂时,5种杂多酸(盐)均具有催化活性,其中H3PW12O40催化活性最高.在催化剂用量0.04mmol、w(H2O2)=30%的H2O2用量0.015mol、反应时间3.5h、反应温度90℃、溶剂水用量10mL的优化反应条件下,苯甲醇的转化率为95.59%,苯甲醛的收率可达91.62%.由此可知,H3PW12O40/H2O2/H2O体系是环境友好的高效催化体系,具有工业化应用前景.     

关于用K2Cr2O7+K2CrO4作双指示剂法示例的探讨

在酸碱滴定的双指示剂法示例中，用Ｋ２Ｃｒ２Ｏ７＋Ｋ２ＣｒＯ４取代Ｎａ２ＣＯ３＋ＮａＨＣＯ３，并改用溴甲酚绿和酚酞作指示剂．其结果表明，本法滴定的终点前颜色变化较明显，终点较敏锐，准确度较好．     

纳米Al2O3颗粒对Cu-Al2O3性能的影响

采用溶胶-凝胶法制备纳米Al₂O₃颗粒,通过粉末冶金法制备氧化铝铜（Cu-Al₂O₃）。采用X射线光电子能谱仪、扫描电子显微镜、洛氏硬度仪和涡流计分别测试了Cu-Al₂O₃的结合能、微观组织、硬度和导电率。结果表明：随Al₂O₃颗粒含量的增加,Cu-Al₂O₃的硬度先升高后降低,当Al₂O₃颗粒的质量分数达到0.084%时,Cu-Al₂O₃的硬度达到最大值75.73（HRB）。Cu-Al₂O₃的导电率随着Al₂O₃颗粒含量的增加逐渐下降。Al₂O₃颗粒的质量分数为0.084%时为最佳值,Cu-Al₂O₃的硬度达到最大值,导电率达到69.1% IACS。     

Al2O3含量变化对CaO–SiO2–Cr2O3–Al2O3熔渣粘度及结构的影响

熔渣粘度对冶炼过程中渣金反应的传质有着至关重要的作用,适当的熔渣粘度能够有效促进渣金反应,提升传质效率。为了促进含铬熔渣中铬的回收利用,本文使用柱体旋转法研究了Al₂O₃含量变化对CaO-SiO₂-Cr₂O₃-Al₂O₃渣粘度和结构的影响规律。熔渣在高温下表现出良好的牛顿流体行为。当Al₂O₃含量从0%增加到10wt%时,酸性渣的粘度首先从0.825增加到1.141 Pa·s,然后当Al₂O₃含量进一步增加到15wt%时,粘度降低到1.071 Pa·s。当Al₂O₃含量从0增加到15wt%时,碱性炉渣的粘度首先从0.084增加到0.158Pa·s,然后当Al₂O₃含量进一步增加到20wt%时,粘度降低到0.135 Pa·s。此外,含Cr₂O₃的炉渣比无Cr₂O₃的炉渣需要更少的Al₂O₃才能达到最大粘度;对于酸性和碱性炉渣,熔渣粘度达到最大值所需的Al₂O₃含量分别为10%和15%。熔渣的活化能变化规律与粘度结果一致。拉曼光谱表明,熔渣中仅有少量Al₂O₃时,Al以[AlO₄]四面体形式出现,随着Al₂O₃含量的逐渐增加,[AlO₄]四面体被[AlO₆]八面体所取代,对硅酸盐结构的分峰解谱结果也与粘度结果一致。     

MnO2和K2Cr2O7氧化盐酸制备Cl2条件的讨论

本文应用Nernst方程讨论了无机化学中MnO2、K2Cr2O7作为氧化剂氧化盐酸制备氯气的实验条件。     

CaO-SiO2-MgO-Al2O3四元渣系Al2O3活度预测模型

高炉渣系各组元活度对高炉冶炼和产品质量具有重要的影响作用. 基于分子-离子共存理论,建立CaO-SiO₂-MgO-Al₂O₃四元渣系Al₂O₃活度预测模型;结合试验测定值对其进行验证与修正,最终建立了修正的CaO-SiO₂-MgO-Al₂O₃四元渣系Al₂O₃活度预测模型;同时,依据模型计算结果探究R(w(CaO)/w(SiO₂)),w(MgO)/w(Al₂O₃)和w(Al₂O₃)对Al₂O₃活度的影响. 研究结果表明:修正后的CaO-SiO₂-MgO-Al₂O₃四元渣系Al₂O₃活度预测模型具有较高的预测精度,能够很好地预测熔渣Al₂O₃活度;当w(MgO)/w(Al₂O₃)=0.40,w(Al₂O₃)=20%时,随着R增加,Al₂O₃活度逐渐减小;当R=1.25,w(Al₂O₃)=20%时,随着w(MgO)/w(Al₂O₃)增加,Al₂O₃活度逐渐减小;当w(MgO)/w(Al₂O₃)=0.40,R=1.25时,随着w(Al₂O₃)增加,Al₂O₃活度逐渐增大.