30SiMnCrB5热成形钢的微观组织和力学性能

为了提高热成形钢的综合性能,设计了一种C-Si-Mn-Cr-B系热成形钢,采用热膨胀仪测定并研究了30Si Mn Cr B5热成形钢的连续冷却转变曲线和相变规律.分析了经轧制、退火及热成形模拟后钢板的微观组织形貌和力学性能,结合等密度线极图的方法,判定了热成形模拟后钢板中马氏体变体与母相的取向关系.30Si Mn Cr B5热成形钢具有较好的淬透性,临界冷速为5℃·s-1,有效抑制了珠光体和贝氏体的形成,完全马氏体组织的硬度可达600 HV以上.热成形模拟后的微观组织由板条马氏体和残余奥氏体构成,残余奥氏体主要以薄膜状分布在马氏体板条间,质量分数为6%~8%,抗拉强度为1800 MPa左右,总伸长率可达10%以上,强度和塑性的匹配较好.热成形模拟后30Si Mn Cr B5热成形钢板中马氏体变体与母相的取向关系更接近N-W关系,12种变体没有都出现在原始奥氏体内.     

退火温度对430不锈钢冷轧板组织和力学性能的影响

针对现场生产的430不锈钢冷轧板,通过高温连续退火实验研究了退火温度对材料显微组织、强度、塑性以及各向异性性能的影响.通过实验得到了合理的两段式加热连续退火工艺:选取中间温度为600℃,加热II段的加热速率为2.3℃·s-1,最高加热温度为840℃.随着退火温度的升高,薄板的屈服强度和硬度呈明显的两阶段降低趋势,延伸率呈"S"型趋势增加,平均塑性应变比基本保持不变(1.25左右),而轧制平面各向异性指数有一定的降低.针对430不锈钢冷轧板分别建立了屈服强度与退火软化率和延伸率之间的定量关系.     

连续退火的无Si TRIP钢的组织和力学性能

在实验室用Gleeble3500热模拟试验机制备了一种无Si TRIP钢.利用拉伸试验机、扫描电镜、透射电镜、X射线衍射以及热膨胀仪对其力学性能、微观组织和相变规律进行研究,在此基础上分析了贝氏体相变温度和时间对力学性能和残余奥氏体的影响.无Si TRIP钢呈现出良好的整体力学性能,抗拉强度分布在740～810 MPa,延伸率均在25%以上,最高可达32%以上;贝氏体等温温度为420℃时能获得最佳的综合力学性能,抗拉强度随贝氏体相变时间增加而下降,延伸率随之上升,而屈服强度没有显著变化.无Si TRIP制的铁素体晶粒大小约为3～4μm,比含Si TRIP钢铁素体晶粒细小;残余奥氏体的体积分数在8%～10%,比含Si TRIP钢低约3%;420℃保温300 s后贝氏体相变基本结束,而碳的扩散仍然在进行;无Si TRIP钢贝氏体相变速率比含Si TRIP钢快,贝氏体相变总量也更多.     

退火后冷却方式对冷轧中锰钢微观组织和力学性能的影响

采用拉伸试验、扫描电镜、电子背散射衍射、透射电镜、X射线衍射等手段，研究了冷乳中锰钢（0.2C-5Mn)退火后不同冷却方式下的微观组织特点和拉伸性能.实验钢冷乳退火后为铁素体加逆转变奥氏体的双相组织.退火后空冷可以获得稳定性较髙的逆转变奥氏体，且其体积分数也明显髙于退火后炉冷.退火后空冷实验钢中的逆转变奥氏体在变形过程中产生持续的TRIP效应，提髙强度的同时获得了较髙的塑性，强塑积可达到26.5GPa.%.     

Effects of overaging temperature on the microstructure and properties of 600 MPa cold-rolled dual-phase steel

C–Mn steels prepared by annealing at 800°C for 120 s and overaging at 250–400°C were subjected to pre-straining (2%) and baking treatments (170°C for 20 min) to measure their bake-hardening (BH2) values. The effects of overaging temperature on the microstructure, mechanical properties, and BH2 behavior of 600 MPa cold-rolled dual-phase (DP) steel were investigated by optical microscopy, scanning electron microscopy, and tensile tests. The results indicated that the martensite morphology exhibited less variation when the DP steel was overaged at 250–350°C. However, when the DP steel was overaged at 400°C, numerous non-martensite and carbide particles formed and yield-point elongation was observed in the tensile curve. When the overaging temperature was increased from 250 to 400°C, the yield strength increased from 272 to 317 MPa, the tensile strength decreased from 643 to 574 MPa, and the elongation increased from 27.8% to 30.6%. Furthermore, with an increase in overaging temperature from 250 to 400°C, the BH2 value initially increases and then decreases. The maximum BH2 value of 83 MPa was observed for the specimen overaged at 350°C.     

一种超高强度钢组织性能的研究

通过力学测试、金相、扫描电镜观察等方法研究了不同淬火温度下一种淬火 低温回火超高强度钢的组织性能,系统的探讨了未溶相与淬火温度的关系。结果表明：钢采用低于950℃的淬火温度,组织中存在大量未溶碳化物,当温度高于1010℃时,未溶碳化物基本溶解,马氏体板条束明显粗化,对钢的力学性能有害,适宜的淬火温度为1010℃。     

预合金化处理对22MnB5热成型钢镀层组织成分的影响

在热成型钢上施加镀层,可有效避免其在热成型工艺中出现表面氧化、脱碳等缺陷,使成型后工件具有一定程度的抗腐蚀能力,研究了22MnB5热成型钢镀Zn层在升温过程中的微观组织结构变化和热处理工艺对镀层组织、性能的影响,对镀锌22MnB5钢进行不同的预合金化+相同的奥氏体化处理后,采用扫描电镜、能谱仪和辉光光谱分析仪对其镀层形貌、微观结构和组成成分进行了分析。其结果表明,在预合金化时间相同的情况下,随着温度上升,镀层由开始的ζ相、δ相、Γ_1相和Γ相互相掺杂逐渐转变为以Γ相为主;在预合金化温度相同的情况下,随着预合金化处理时间的延长,镀层中的Zn含量逐渐减少,Fe含量持续增加;在经过奥氏体化处理后镀层中Fe含量可达到88%左右,Zn含量可达到8%左右,镀层几乎全部为α-Fe(Zn),只在表面存在少量Γ相,镀层厚度在12μm左右;预合金化工艺为550℃保温30min、奥氏体化工艺为920℃保温4min时能得到质量较好的镀层。此结果对于发展新型含镀层热成型钢板具有重要参考价值。     

预处理组织对低碳钢IQ&P工艺下组织及性能影响

采用γ单相区和γ+α双相区轧制并淬火工艺以及双相区再加热-淬火-碳配分( IQ&P)工艺,研究预处理组织对低碳钢室温状态多相组织特征及力学性能的影响规律. 实验用低碳钢经两种工艺轧制并淬火处理,获得马氏体和马氏体+铁素体的预处理组织,再经双相区IQ&P工艺处理后均获得多相组织. 马氏体预处理钢的室温组织由板条状亚温铁素体、块状回火马氏体以及一定比例的针状未回火马氏体和8. 2%的针状残余奥氏体组成;马氏体+铁素体预处理钢由板条状亚温铁素体、块状和针状未回火马氏体以及14. 3%的短针状或块状残余奥氏体组成. 在相同的双相区IQ&P工艺参数下,预处理组织为马氏体的钢抗拉强度为770 MPa,伸长率为28%,其强塑积为21560 MPa·%;而预处理组织为马氏体+铁素体的钢抗拉强度为834 MPa,伸长率增大到36. 2%,强塑积达到30190 MPa·%,获得强度与塑性的优良结合.     

热轧带钢力学性能预测模型及其应用

为实现对热轧带钢的屈服强度、抗拉强度、断裂延伸率等力学性能的预测及控制,利用人工神经网络技术,分别建立了根据生产工艺参数预测力学性能的质量模型,以及根据力学性能要求对生产工艺参数进行优化的逆质量控制模型.利用质量预测模型,分析得出屈服强度随卷取温度的上升而下降的变化规律,进而可以对组织性能进行在线调整,实现在线应用.     

高铝TRIP钢的高温力学性能

利用Gleeble3500试验机研究汽车用C-Mn-Al系TRIP钢的高温力学性能,测定了零塑性温度和零强度温度,应用差示扫描量热法测定其相变区间,采用扫描电镜和光学显微镜分析了不同拉伸温度对应的断口宏观形貌及断口附近组织组成.该钢种零塑性温度和零强度温度分别为1425℃和1430℃,第Ⅰ脆性区间为1400℃~熔点,第Ⅲ脆性区间为800~925℃.第Ⅲ脆性区脆化的原因是α铁素体从γ晶界析出,试样从975℃冷却至700℃过程中,随着α铁素体析出比例的增大,断面收缩率先减小后增大.基体α铁素体比例为8.1%时(850℃),断面收缩率降至28.9%;而拉伸温度在800℃以下时,基体α铁素体比例超过16.7%,断面收缩率回升至38.5%以上.该钢种在1275.6℃时开始析出少量粗大的AlN颗粒,但对钢的热塑性没有影响.     

C—Si—Mn系热轧双相钢显微组织与力学性能之间的关系

通过对热轧试样的组织性能测试,研究了热轧双相钢显微组织与力学性能之间的关系。研究发现,铁素体和马氏体强度是影响力学性能的主要因素。建立了C-Si-Mn系热轧双相钢力学性能的数学模型,可以作为热轧双相钢基本力学性能参数预测的理论依据。     

Effect of hot-dip galvanizing processes on the microstructure and mechanical properties of 600-MPa hot-dip galvanized dual-phase steel

A C-Mn dual-phase steel was soaked at 800℃ for 90 s and then either rapidly cooled to 450℃ and held for 30 s (process A) or rapidly cooled to 350℃ and then reheated to 450℃ (process B) to simulate the hot-dip galvanizing process. The influence of the hot-dip galvanizing process on the microstructure and mechanical properties of 600-MPa hot-dip galvanized dual-phase steel (DP600) was investigated using optical microscopy, scanning electron microscopy (SEM), transmission electron microscopy (TEM), and tensile tests. The results showed that, in the case of process A, the microstructure of DP600 was composed of ferrite, martensite, and a small amount of bainite. The granular bainite was formed in the hot-dip galvanizing stage, and martensite islands were formed in the final cooling stage after hot-dip galvanizing. By contrast, in the case of process B, the microstructure of the DP600 was composed of ferrite, martensite, bainite, and cementite. In addition, compared with the yield strength (YS) of the DP600 annealed by process A, that for the DP600 annealed by process B increased by approximately 50 MPa because of the tempering of the martensite formed during rapid cooling. The work-hardening coefficient (n value) of the DP600 steel annealed by process B clearly decreased because the increase of the YS affected the computation result for the n value. However, the ultimate tensile strength (UTS) and elongation (A₈₀) of the DP600 annealed by process B exhibited less variation compared with those of the DP600 annealed by process A. Therefore, DP600 with excellent comprehensive mechanical properties (YS=362 MPa, UTS=638 MPa, A₈₀=24.3%, n=0.17) was obtained via process A.     

焊接电流对镁/镀锌钢 TIG熔--钎焊接头显微组织与力学性能的影响

采用TIG熔-钎焊焊接方法,以镁合金焊丝为填充材料,对镁合金与镀锌钢进行连接实验,并分析热输入量对接头显微组织和力学性能的影响.热输入量过小会阻碍镁/钢界面反应层的形成而使得焊缝难以焊合,热输入量过大又会促进焊缝内部脆性第二相的长大,降低接头力学性能.接头强度随着焊接电流和焊接速度的增大都呈现先上升后下降的趋势,电流为70 A时强度达到最大,该值接近AZ31B母材的88．7%.此时断裂发生于焊缝熔焊区,断面出现大量韧窝和撕裂棱,呈现出塑性断裂特征.     

TMCP工艺对Si--Mn系贝氏体钢组织与性能的影响

研究了轧后中温缓慢冷却与中温等温两种不同的热机械控制工艺( thermomechanical control process, TMCP)对硅锰系贝氏体钢的组织与性能的影响。通过拉伸试验机测试试验钢的力学性能,利用扫描电子显微镜、电子背散射衍射等分析手段对试验钢进行显微组织结构分析,并利用X射线衍射测定残余奥氏体含量。结果表明：随着轧后连续缓慢冷却开始温度的升高,贝氏体钢的抗拉强度、硬度及拉伸应变硬化指数n值有所提高,伸长率和冲击韧性降低,屈强比先降低后升高。随着轧后等温时间的延长,贝氏体钢的抗拉强度与屈强比先降低后升高,伸长率及冲击韧性先升高后降低。相对于等温制度,连续缓慢冷却可得到更好的综合力学性能,强塑积明显高于前者,伸长率比前者高20%以上。     

B1500 HS硼钢热冲裁过程的相变和冲裁精度

为了研究热冲裁零件微观组织及尺寸精度的变化规律,采用不同的冲裁温度和模具间隙比对B1500HS钢板进行了热冲裁试验.根据冷却曲线,研究了冲裁温度对硼钢组织转变和零件力学性能的影响;根据落料件的尺寸,分析了冲裁温度和模具间隙比对尺寸精度的影响;通过观察零件的断口形貌,分析了冲裁温度对断口质量的影响.结果表明:当冲裁温度一定时,落料件的尺寸随着模具间隙比的减小而增大;当模具间隙比一定时,落料件的尺寸误差随着冲裁温度的降低出现"正—负—正"的增长波动趋势;当冲裁温度为600~650℃或750~800℃时,落料件具有较高的冲裁精度;落料件的硬度随着冲裁温度的升高而增大,当冲裁温度为650~800℃时,落料件的组织为马氏体,硬度值HV约为550;冲裁断面光亮带的宽度随着冲裁温度升高而增大.     

热处理工艺对40CrNiMoA合金组织及力学性能的影响

为了提高矿用链轮耐磨性,延长其使用寿命,选取电渣离心铸造40CrNiMoA合金链轮件作为母材,研究热处理工艺对40CrNiMoA合金组织和力学性能的影响。采用正交试验法,研究不同热处理工艺对合金显微硬度、摩擦磨损及拉伸强度等力学性能的影响,并将测试结果进行极差分析和综合加权评分计算,得出最优热处理工艺参数,最后进行试验验证。结果表明,正交试验法得到的最优热处理工艺为880℃淬火0.5 h, 600℃高温回火2 h,样品热处理后的组织主要为回火索氏体,维氏硬度为364 HV,抗拉强度为1 166 MPa,磨损率为0.427×10^-4 mm³/(N·m);验证试验结果与正交试验分析结果相近,且热处理后的样品性能可达到使用要求。研究结果可为矿用链轮件热处理工艺提供理论依据,对有效解决链轮耐磨性和使用寿命问题具有参考价值。     

Effects of metal binder on the microstructure and mechanical properties of Al2O3-based micro-nanocomposite ceramic tool material

The Al2O3?(W,Ti)C composites with Ni and Mo additions varying from 0vol% to 12vol% were prepared via hot pressing sintering under 30 MPa. The microstructure was investigated via X-ray diffraction (XRD) and scanning electron microscopy (SEM) equipped with energy dispersive spectrometry (EDS). Mechanical properties such as flexural strength, fracture toughness, and Vickers hardness were also measured. Results show that the main phases A12O3 and (W,Ti)C were detected by XRD. Compound MoNi also existed in sintered nanocom-posites. The fracture modes of the nanocomposites were both intergranular and transgranular fractures. The plastic deformation of metal particles and crack bridging were the main toughening mechanisms. The maximum flexural strength and fracture toughness were obtained for 9vol% and 12vol% additions of Ni and Mo, respectively. The hardness of the composites reduced gradually with increasing content of metals Ni and Mo.     

硼钢热冲压微观组织仿真及力学性能预测

基于Johnson-Mehl-Avrami相变动力学模型和Koistinen-Marburger方程,建立了硼钢22MnB5车门防撞梁热冲压过程的热机械-相变耦合有限元模型,得到了车门防撞梁热冲压过程中板料温度、微观组织及维氏硬度的分布特征,研究了保压压力和保压时间对防撞梁热冲压零件的性能影响.仿真结果表明:车门防撞梁顶部冷却速度为137.3℃·s-1,侧壁冷却速度为69.8℃·s-1,冷却速度决定了防撞梁各个部位的微观组织和维氏硬度;随着保压压力的增大,获得95％以上马氏体的防撞梁的保压时间缩短,可加快生产节拍.进行了防撞梁热冲压试验,对微观组织及维氏显微硬度进行了检测.结果表明:车门防撞梁保压10s后,顶部及侧壁均已转化为板条状马氏体组织,且顶部硬度为508 HV,侧壁硬度为474 HV.     

退火温度对退火马氏体基TRIP钢显微组织和力学性能的影响

将C-Si-Mn系TRIP钢通过完全淬火和两相区退火相结合的工艺,得到一种以退火马氏体为基体的TRIP钢(简称TAM钢),并对比分析了TAM钢在不同温度退火后的显微组织和力学性能.结果表明,TAM钢经退火后的显微组织特征为精细规整的板条退火马氏体基体、片状残余奥氏体和贝氏体/马氏体组成的混合组织.这种组织降低了基体的硬度以及基体和第二相之间的强度比,减少了基体的位错密度.随着退火温度的提高,退火马氏体基体的板条形态逐渐消失,新生马氏体/贝氏体的团状混合组织逐渐增多.当退火温度为780℃时,综合力学性能优异,抗拉强度为1130 MPa,延伸率可达20%,强塑积为22600 MPa·%.当退火温度较低时,残余奥氏体主要以片状存在于退火马氏体板条间,有利于TRIP效应的发生.     

连续退火工艺对低硅型冷轧低合金高强钢板 力学性能的影响

利用多功能连续退火模拟器Multipas对屈服强度为380MPa的低硅型冷轧低合金高强钢板连续退火生产工艺进行了模拟,研究了在820,800, 780℃三种不同退火温度和60, 120,160m·min-1三种不同退火速度下,连退工艺对冷轧低合金高强钢板组织、力学性能的影响.结果表明,在不同的退火温度、退火速度下钢板退火组织的晶粒度基本相同,采用较低的退火温度和较高的退火速度时,可获得较好的强化效果.同时指出,在较高的连续退火温度下,退火速度对力学性能的影响较为显著.