拉伸载荷下镍基粉末高温合金中夹杂物行为

采用扫描电镜原位拉伸方法,跟踪观察了人工植入A12O3夹杂物的镍基粉末高温合金P/MRene95中夹杂物导致裂纹萌生、扩展乃至断裂的过程.结果表明,在单轴拉伸载荷下,裂纹首先萌生于脆性非金属夹杂物A12O3处,大于一定尺寸的夹杂物,还会使该裂纹扩展成为导致合金断裂的主裂纹,从而大大降低合金的屈服强度及断裂强度.     

XCQ16和20Mn2车轴用钢疲劳失效的微观机理

利用扫描电镜(SEM)对XCQ16和20Mn2两种车轴用钢疲劳断口和裂纹扩展断口进行分析,研究疲劳失效过程中的裂纹萌生及扩展机理.结果表明:裂纹均是从试样表面萌生,非金属夹杂和位错是主要的萌生机制;XCQ16钢在疲劳断口中部区的裂纹闭合效应大于20Mn2钢,裂纹扩展较慢;两者在裂纹扩展区的扩展机理不同,XCQ16钢属于塑性断裂,20Mn2钢属于解理断裂;在非金属夹杂上,XCQ16钢多含氧化物和硫化物的混合夹杂,20Mn2钢主要是氧化物夹杂,混合夹杂对材料的疲劳性能影响较小.     

奥氏体耐热不锈钢310S动态拉伸变形行为研究

采用扫描电子显微镜(SEM)静载动态拉伸原位观察方法研究了310S奥氏体耐热不锈钢常温动态拉伸过程中裂纹的萌生、扩展及断裂过程.结果表明:裂纹源容易在夹杂物、基体界面以及应力集中部位形成.随着拉伸变形进行,不同位置形成的微裂纹中,处于与拉伸应力方向相同或相近的有利位相的微裂纹不断亚稳扩展,最后与周围微裂纹连接形成主裂纹.当主裂纹扩展到一定程度达到或超出临界裂纹尺寸后,试样裂纹发生全面失稳扩展而试样迅速断裂.     

Al-Cu-Li合金轧制厚板的 疲劳性能及断裂机理研究

利用疲劳试验机、扫描电子显微镜(SEM)和透射电子显微镜(TEM)等设备研究了95 mm厚的Al-Cu-Li合金热轧板材不同方向的组织特征、疲劳性能和断裂机理.结果表明:Al-Cu-Li合金热轧厚板的力学性能和疲劳性能均存在各向异性.LT向(横向)的力学性能和疲劳性能均优于L向(纵向)和ST向(高向),L向(纵向)的力学性能较ST向更好,但疲劳性能较ST向更差.Al-Cu-Li合金厚板的疲劳裂纹源主要出现在试样表面、近表面的夹杂物和晶界处.裂纹扩展过程中,LT向裂纹扩展路径较L向更曲折,ST向具有典型的解理特征,瞬断区形貌与静态拉伸断口相似.晶界越多,裂纹扩展阻力越大,LT向和ST向的未溶第二相能够有效阻碍裂纹扩展,导致其疲劳性能优于L向.     

Mo-30Cu合金室温变形组织

对Mo-30Cu合金室温拉伸性能进行了研究,并对其断口进行观察分析.通过对Mo-30Cu合金冷轧实验,研究了不同变形量下组织的变化规律.结果表明:Mo-30Cu合金的断裂以Cu相的韧性断裂为主,并伴随着Mo/Cu界面的分离和Mo晶粒的解理断裂.Mo/Cu界面的分离和Mo晶粒的解理断裂是Mo-30Cu合金室温轧制过程中产生裂纹的主要原因.     

铸造共晶铝硅合金中析出相对断裂行为的影响

通过对铸造共晶Al-Si合金断口及析出相的分析研究了拉伸过程中基体内析出相的断裂特点.结果发现：拉伸过程中基体内初、共晶硅以穿晶断裂为主,这与颗粒内部存在的结构缺陷有关;直径小于2.0μm的初晶硅能够抑制二次裂纹的扩展.块状富铁相表现出穿晶断裂特点,鱼骨状富铁相中的微裂纹沿一次枝晶轴向生长.富铜相对裂纹扩展具有强烈地偏折作用;以富铁相为核心析出的富铜相能抑制富铁相中微裂纹的形成.提高合金中Cu含量可以降低富铁相的有害作用,改善合金的力学性能.     

解理断裂机制

解理断裂是典型的脆性断裂 ,解理断裂也是一个裂纹萌生和扩展的过程 ,其机制与位错和晶粒有关。应力的大小和晶粒的尺寸影响解理断裂。细化晶粒可抑制脆性断裂。     

固溶处理对2E12铝合金组织及疲劳断裂行为的影响

通过对2E12铝合金进行493 ℃/20 min和503℃/20 min固溶处理,研究固溶处理对2E12合金室温拉伸及疲劳性能的影响.采用X线衍射分析、扫描电镜和金相分析对合金组织及疲劳断口进行观察.研究结果表明:提高固溶处理温度对合金拉伸性能影响不大,但可明显减少合金中残留相(Al2Cu,A12CuMg)的含量;经503 ℃/20 min处理后合金的拉伸强度较经493℃/20 min处理后合金的拉伸强度略有提高,但其疲劳寿命延长约20％;合金中残留相在疲劳过程中容易开裂形成微小二次裂纹,在主裂纹扩展过程中起到桥接作用,从而加速疲劳裂纹扩展,降低合金疲劳性能.     

铸铁断裂机理原位拉伸研究

用SEM原位拉伸实验对不同缺口的灰铸铁试件的断裂过程做了详细研究和分析.研究结果表明,铸铁的断裂与钢的脆性解理断裂不同.铸铁试件的断裂过程与预缺口的形态有关;在载荷很小时产生微裂纹,随着载荷的增加,微裂纹扩展,微裂纹扩展的同时产生大量新的微裂纹,直至各裂纹连接使试件整体断裂.     

车轮钢形变断裂过程的原位研究及氢影响

在扫描电镜下对CL60车轮钢单边缺口薄试样(厚度≤0.5mm)进行了原位拉伸实验,并研究了氢的影响.在金相显微镜下观察了带预裂纹的厚度为30mm的楔形张开加载试样开裂过程.结果表明,对薄试样拉伸变形时,不论是否有氢,先共析铁素体优先发生塑性变形,微裂纹沿先共析铁素体与珠光体团的边界形核、扩展;在有氢的情况下,微裂纹更容易通过夹杂物的剥落或夹杂物与基体界面的分离而萌生;薄试样拉伸主要是韧窝断口;对厚试样,裂纹主要通过珠光体中渗碳体片层开裂而扩展,断口也因此主要呈解理特征.     

Hish-strensth wrousht masnesium alloy with dense nano-scale spherical precipitate

This paper reported the influences of Yb addition on the precipitate and mechanical properties of wrought magnesium alloy ZK60. The ingots of ZK60-1.78Yb （wt%, 0.26 at%） alloys were cast using permanent mould and extruded at 370~C. By means of TEM and HRTEM, it was observed that Yb affected the precipitate and precipitation of ZK60-1.78Yb alloys significantly. Dynamic precipitation occurred in the as-extruded alloy and spherical nano-scale precipitate with high density and homogeneity exhibited in the aged alloys. The precipitate particles were about 5-20 nm in diameter, 10-30 nm in average space length. The tensile test results showed that the ZK60-1.78Yb alloy had excellent precipitation strengthening response with the maximum tensile strength 417.5 MPa at ambient temperature.     

Size and distribution of Te inclusions in detector-grade CdZnTe ingots

The effects of Sc addition on the microstructure and mechanical properties of the ZK60 wrought magnesium alloy were investigated by using optical microscope,scanning electron microscopy,X-ray diffraction and tensile testing.The experimental results show that a minor Sc addition to ZK60 alloy has an obvious effect on the refinement of the microstructure of the ZK60 alloy. During hot extrusion,incomplete dynamic recrystallization occurs in all the alloys,and the recrystallized grains become much finer with...     

Surface characteristics and corrosion resistance of biodegradable magnesium alloy ZK60 modifi ed by Fe ion implantati on and deposition

The ZK60 magnesium alloy has been modified by Fe ion implantation and deposition with a metal vapor vacuum arc plasma source. The surface morphology, phase constituent and elemental distribution are determined by scanning electron microscopy, transmission electron microscopy, X-ray diffractometer and Auger electron spectroscopy. The results show that Fe thin film is deposited on ZK60 alloy and the corresponding thickness increases from 2.73 μm to 6.36 μm with increasing deposition time. A transition layer mainly composed of Mg, Fe and O elements is formed between Fe thin film and ZK60 substrate. The potentiodynamic polarization tests reveal that a high corrosion potential and a low corrosion current density are detected for the Fe deposited ZK60 alloy, indicating the improvement of corrosion resistance. The tensile deformation test indicates that the Fe deposited film on the ZK60 substrate can sustain 1% tensile strain without any cracks.     

稀土元素Y对变形镁合金ZK60的 组织和性能的影响

在中世纪有5种重要的真理理论,分别是坎特伯里的安瑟尔谟的真理理论、彼得.阿伯拉尔的真理理论、托马斯.阿奎那的真理理论、基于指代思想的真理理论和14世纪的真理语义理论。"正直"这个概念刻画了安瑟尔谟的真理理论,"dicta"是阿伯拉尔真理理论中的真值承担者,托马斯.阿奎那维护根据理智与客观事物之间的相等来获得真理的方法,基于指代思想的真理理论反对通过形而上学的方法获得真理,14世纪的真理理论认为通过语义方法获得真理,并且引入了对命题指代的量化。     

稀土Y对挤压态Mg-5Li合金组织及性能的影响

采用表面覆盖剂及氩气保护的熔炼方法制备了Mg-5Li-x Y(x=0,1,2,3,4)合金,研究了稀土元素Y对挤压态Mg-5Li合金的显微组织及力学性能的影响.研究结果表明,Mg-5Li合金中的Y元素主要是以稀土化合物Mg24Y5的形式存在于合金中;挤压变形后,合金发生了明显的动态再结晶,出现了大量的等轴晶,弥散分布的Mg24Y5相阻碍了动态再结晶过程中的晶粒长大,晶粒明显细化.挤压态Mg-5Li-3Y合金获得了优异的力学性能,其抗拉强度和断裂伸长率分别达到了231.63 MPa和9.35%,合金断裂方式主要为韧性断裂.     

挤压合金Mg-Mn-3．5Y和Mg-Mn-1Y-2．5Nd的高温变形特性

室温挤压合金Mg-1Mn-3．5Y具有高的屈服强度，但其延伸率较低，小于9%。挤压合金Mg-1Mn-1Y-2．5Nd屈服强度比挤压合金Mg-1Mn-3．5Y低，但其延伸率室温下高于25％。高温拉伸后Mg-1Mn-1Y-2．5Nd合金断裂面上出现大量韧窝，有较好的韧性；而合金Mg-1Mn-3．5Y断裂面表现为解理断裂。比较不同温度下的拉伸实验结果，发现Mg-1Mn-1Y-2．5Nd的屈服强度随温度升高，降低比较缓慢，表现出更好的热稳定性。     

热处理对含Y元素AZ31镁合金板材组织和性能的影响

对含Y元素AZ31镁合金板材进行退火处理后的组织和性能进行了研究.结果表明:随着退火温度的升高,镁合金晶粒尺寸逐渐增大,力学性能略有提高然后降低;退火时间对镁合金晶粒尺寸影响不大;在300℃下退火1 h后板材性能达到最佳,抗拉强度为255 MPa,屈服强度为170 MPa,延伸率为24%;经过热处理后镁合金断裂方式为准解理断裂和韧性断裂的复合形式.     

Mg/Al异种材料瞬间液相过冷连接工艺研究

采用瞬间液相过冷连接工艺对AZ31镁合金和5083铝合金进行连接实验,研究保温扩散时间t2对焊缝微观组织及力学性能的影响。利用SEM,EDS,XRD和微观硬度计对接头剖面的微观组织和力学性能进行表征;在拉伸试验机上测试接头拉伸强度,利用SEM对断口形貌进行分析。研究结果表明:采用瞬间液相过冷连接工艺可以实现Mg/Al异种材料的有效连接;随着保温扩散时间t2的增加,接头的抗拉强度随之提高,当t2=30 min时,接头抗拉强度最高达到20.5 MPa;拉伸断口形貌具有明显的脆性断裂的特征,铝合金侧主要有解理面和撕裂棱组成,而镁合金侧属于典型的沿晶断裂形貌;在接头处形成MgAl,Mg2Al3,Mg0.44Al0.56和Mg17Al12金属间化合物,结合界面的微观维氏硬度最高达320。     

稀土镁合金近非平衡液相线铸造研究

近非平衡液相线铸造方法是测量熔体非平衡凝固过程的冷却曲线,确定其非平衡液相线温度,并在此温度附近进行铸造的工艺方法,为实质意义上的近液相线铸造.采用该方法对ZK60稀土系列镁合金进行了研究,结果表明,近非平衡液相线铸造工艺可获得细小均匀的非枝晶结构,是镁合金半固态制浆的有效方法;不同合金元素对以ZK60为基体的合金的非平衡液相线和近液相线铸造组织都有明显影响,Ag,Y,Nd等元素有利于避免浆料中晶内液相的出现,其中混合稀土最有利于初生晶粒的圆整化,而Nd则造成初生晶粒的不均匀,Ag和Y的添加尽管初生晶粒圆整程度不如Nd,但有较均匀的晶粒和较好的枝晶退化效果.     

PM Rene 95合金中夹杂物的微观力学行为

采用人工植入Al2O3夹杂物的试样,通过SEM原位观察及非线性有限元分析,研究了在单轴拉伸条件下P/MRene95合金中夹杂物与基体的相互作用机理.结果表明,不同尺寸及位置的夹杂物对拉伸进程影响不同;夹杂物/基体界面的裂纹萌生及扩展取决于界面附近基体材料的应力状态.