低温快固自交联涂料印花粘合剂的研制

介绍了ＨＳ－Ⅱ低温自交联丙烯酸酯涂料印花粘合剂的制备，采用了核－壳聚合新工艺．该粘合剂适合纯棉和合成纤维的低温涂料印花，印花产品手感柔软，刷洗牢度３级，摩擦牢度３～４级．     

自交联涂料印花粘合剂的研制

研究了ＨＳ－Ⅰ高温自交联丙烯酸酯涂料印花粘合剂的制备．采用种子乳液聚合工艺，同时对单体及其配比、乳化剂、引发剂、聚合反应的时间和温度进行了研究，找到了最佳单体配比和聚合工艺．该粘合剂储存稳定，成膜无色透明，弹性强，适合纯棉与合成纤维进行辊筒印花、圆网和平网印花．印花织物手感柔软，刷洗牢度３～４级，摩擦牢度４～５级，高温焙烘不泛黄．     

纯棉毛巾织物的超细涂料印花工艺探讨

探讨了利用超细涂料对纯棉毛巾织物涂料印花的工艺.对超细涂料印花的焙烘温度和时间,粘合剂用量等因素进行了单因素和正交实验的研究,结果发现粘合剂对摩擦牢度的影响最大,最佳印花工艺条件为粘合剂10%,焙烘150℃×3min.对比普通涂料与超细涂料印花效果发现,超细涂料印花织物的颜色深度大于普通涂料,具有更鲜艳的颜色和更纯正的色光,牢度和手感均好于普通涂料.     

变色涂料的印花工艺研究

选用湿敏型兼有热敏型的变色涂料，配制成四种不同色泽的印花色浆，做了变色印花工艺试验及性能测试．该印花织物可在２０～３５℃，相对湿度４０～９０％的条件下可逆变色，变色效果极为明显．     

聚丙烯酸酯无皂乳液的合成及应用

针对传统聚丙烯酸酯乳液中含有大量的小分子乳化剂,乳液胶膜的耐水性、耐污性差,粘结力及强力下降.并且将该乳液用于涂料印花、涂料染色时,织物的湿摩擦牢度效果不理想等问题,采用极少量(即对单体0.4%)实验室自制的可聚合乳化剂,通过预乳化半连续滴加工艺进行无皂乳液聚合,制成具有柔软性、成膜性和摩擦牢度好的粘合剂,确定了最佳的工艺条件.结果表明,自制涂料印花粘合剂在手感、耐水洗、干摩擦牢度等方面性能优良.     

亚麻织物涂料印花工艺初探

本文针对亚麻织物的特点,通过对涂料、粘合剂、增稠剂的选择及定量试验,对亚麻织物的涂料印花工艺进行了初步探讨,并根据各项牢度测试结果,确定了最佳工艺。     

SAS软件对喷墨印花打样重现性的提高

为减少涂料印花目标色和涂料墨水喷墨印花的颜色差异,将喷墨印花技术用于涂料圆网或平网印花前期的打小样环节中,改变了在图像处理软件中直接输入涂料印花目标样Lab值的传统喷墨印花方法。该方法首先对输入图像处理软件中的Lab值与喷墨印花织物测出的Lab值进行比较,利用SAS软件对数据进行分析,再建立涂料印花目标色与喷墨打印后织物颜色的函数校正关系。结果表明,通过一次或几次SAS软件拟合函数校正,减少了喷墨印花打样颜色与目标色之间的色差,提高了喷墨印花打样与涂料印花的重现性,不仅可以节约打样成本,而且能够更好地配合大生产过程。     

水性预交联聚丙烯酸酯涂料印花粘合剂的合成研究

通过预交联技术合成出水性聚丙烯酸酯涂料印花粘合剂.研究了交联单体、功能单体、乳化剂和引发剂对聚合反应的影响.结果表明,交联单体的选择及用量是预交联技术的关键;功能单体对胶乳粒子大小及分布有较大影响;用阴/非离子复配的乳化剂能使聚合体系达到较好的稳定性;引发剂为单体总量的0.6%.     

自交联型高固体质量分数丙烯酸酯电泳涂料

文章采用了复合引发体系和饥饿加料方式,引入了封端的甲苯二异氰酸酯,并利用曼尼奇反应来实现阳离子化。结果表明,产物具备自交联能力,且涂料固体质量分数达到50%左右,具备电泳性能。该研究实现了自交联性能与高固体质量分数的统一。     

新型有机硅改性涂料印花粘合剂的研制

以甲苯为溶剂,在阻聚剂存在的条件下,用磷钨酸催化甲基丙烯酸和羟基硅油,制备了甲基丙烯酸有机硅酯。通过比较酯交换反应与酯化反应的程度,确定合成有机硅酯的工艺路线。将有机硅酯与苯乙烯、丙烯酸丁酯进行共聚反应合成有机硅改性涂料印花粘合剂。实验确定的有机硅改性涂料印花粘合剂的最佳合成条件为:mPE(苯乙烯)mBA(丙烯酸丁酯)=1 5,反应温度80℃,反应时间3h,甲基丙烯酸有机硅酯用量为10%,引发剂用量为1.2%。     

无皂苯丙乳液粘合剂在涂料印花中的应用

以苯乙烯为硬单体,丙烯酸丁酯和丙烯酸异辛酯为软单体,采用无皂乳液聚合法得到无皂苯丙乳液粘合剂。并将其应用于涂料印花中,对印花工艺进行优化。结果表明,无皂苯丙乳液的用量30％,涂料用量10％,乳化糊用量4％,在145℃焙烘3min时,印花效果较好,棉和涤棉的摩擦牢度、皂洗牢度都能达到工业要求。     

Synthesis of Water-dispersed Polyurethane Adhesive and Its Application in Pigment Printing

Water-dispersed polyurethane (PU) adhesive is a novel and highly efficient adhesive with broad application potential. In this study, the key parameters affecting the synthesis and application of this adhesive were examined, and optimal conditions were identified. The water-dispersed PU adhesive was successfully synthesized, and applied in the fastness test of pigment printing on cotton fabric. The data demonstrated that all the fastnesses of PU adhesive were better than that of the cenventional PA one.     

Synthesis of Ecofriendly Self - crosslinking Adhesive and Its Application in Pigment Printing

Glycidyl acrylate was synthesized successfully utilizing phase - transfer catalyst and was applied to emulsion polymerization of acrylates as the crosslinking agent. Combined with other two kinds of crosslinking agents, a new type of ecofriendly self - crosslinking adhesive was prepared . Factors affecting the preparation such as reaction temperature, initiator, eniulsifiers, reaction time and so on were studied comprehensively. Properties in relation to pigment printing of the prepared adhesives were also tested and compared with two kinds of commercial adhesives that have been widely applied in printing industry.     

新型粘合剂、增稠剂的印染性能

通过对单体、乳化剂及工艺过程的选择,合成了丙烯酸酯类新型粘合剂PBAMM(Ⅰ)和增稠剂PMAEE(Ⅰ)及增稠剂PMAOE(Ⅱ)。所合成的粘合剂Ⅰ具有优良的配伍性能,且印花织物的牢度、色光、强度、手感等优良。增稠剂Ⅰ及Ⅱ既具有优良的增稠性能又有较强的耐电解质性,应用时少剂量即达要求,且能减少印花浆中的火油耗用量。尤其,当粘合剂Ⅰ与增稠剂Ⅰ或Ⅱ配套使用时,更具优越的加和应用性能。     

彩色涂料印花色浆罩印性能的研究

介绍了涂料印花罩印助剂的制备和应用，通过对涂料罩印浆的物理化学性能的研究，探讨了提高罩印效果的途径及罩印助剂颗粒的物理化学性质对罩印效果的影响。     

STUDY ON FACTORS INFLUENCING INK ABSORPTION OF COATED PAPER

1.PREFACECoated paper, which is made up of fiber network andcoating pores, is porous printed material. The ink wastransferred to the sheet during printing. Inkabsorption, which determined the permeability of inkonto the sheet, is an important factor to coated paper.Many printing faults were caused by the unsuiTableof ink absorption of sheet and the printing conditionsused. The more ink absorption could lead to mattedprint, even soaking print or pulverization. While theless ink absorption c…     

阶调印花中新坐标色差评价方法研究

提出了一种用于原色染料网目阶调印花中的新坐标色差评价方法.建立了新坐标色差评价的数学模型,并用实验进行了验证.该方法能准确计算色相差和彩度差,从而保证了阶调印花质量.     

阶调印花中新坐标色差评价方法研究

提出了一种用于原色染料网目阶调印花中的新坐标色差评价方法。建立了新坐标色差评价的数学模型, 并用实验进行了验证。该方法能准确计算色相差和彩度差, 从而保证了阶调印花质量。     

涂料染色粘合剂GH的研制和性能

本文就涂料染色粘合剂GH的制备、乳液稳定性、薄膜材料性能以及染色应用性能等进行了系统的讨论,并与国内外的同类样品作了比较。实验表明,粘合剂GH具有较好的综合性能,尤其是刷洗牢度、抗泳移性、低温染色性和较小的粘搭性。该粘合剂适用于中色染色(涂料用量为10g/l)。