Influence of O_2/Ar ratio on the properties of transparent conductive niobium-doped ZnO films

Niobium-doped ZnO transparent conductive films are deposited on glass substrates by radio frequency sputtering at 300℃.The influence of O2/Ar ratio on the structural,electrical and optical properties of the as-deposited films is investigated by X-ray diffraction,Hall measurement and optical transmission spectroscopy.The lowest resistivity of 4.0×10-4 Ω·cm is obtained from the film deposited at the O2/Ar ratio of 1/12.The average optical transmittance of the films is over 90%.     

Influence of post-annealing on the properties of Ta-doped In<Subscript>2</Subscript>O<Subscript>3</Subscript> transparent conductive films

Ta-doped In₂O₃ transparent conductive oxide films were deposited on glass substrates using radio-frequency (RF) sputtering at 300°C. The influence of post-annealing on the structural, morphologic, electrical and optical properties of the films was investigated using X-ray diffraction, field emission scanning electron microscopy, Hall measurements and optical transmission spectroscopy. The obtained films were polycrystalline with a cubic structure and were preferentially oriented in the (222) crystallographic direction. The lowest resistivity, 5.1×10⁻⁴ Ω cm, was obtained in the film annealed at 500°C, which is half of that of the un-annealed film (9.9×10⁻⁴ Ω cm). The average optical transmittance of the films was over 90%. The optical bandgap was found to decrease with increasing annealing temperature.     

H2/(Ar+H2)流量比对AZO薄膜结构及光电性能的影响

在Ar+H2气氛下,用RF磁控溅射法在室温下制备Al掺杂的ZnO(AZO)薄膜,研究H2/(Ar+H2)流量比对薄膜结构和光电性能的影响。结果表明,在沉积气氛中引入H2可以提高AZO薄膜的结晶质量,降低AZO薄膜的电阻率,提高其霍尔迁移率和载流子浓度;H2/(Ar+H2)流量比为5%时,AZO薄膜的最小电阻率为1.58×10-3Ω.cm,最大霍尔迁移率和载流子浓度分别为13.17cm2.(V.s)-1和3.01×1020 cm-3;AZO薄膜在可见光范围内平均透光率大于85.7%。     

P型透明导电氧化物CuAlO2的研究进展

CuAlO2作为一种天然的P型透明导电氧化物(TCO)成为近年来P型TCO的研究热点. 介绍了CuAlO2近几年最新的研究进展, 简述了不同的制备方法及其优缺点, 综述了对其光电、热电等性能的研究状况, 对CuAlO2掺杂前后性能改变的研究进展做了详细介绍, 并提出了CuAlO2未来的研究方向.     

一种三明治结构透明导电薄膜的制备及光电性能

采用直流磁控溅射法制备了ZAO/Cu/ZAO多层透明导电薄膜,研究了参铝氧化锌(ZAO)薄膜厚度对多层膜晶体结构和光电特性的影响.用X射线衍射仪、原子力显微镜、紫外可见光分光光度计及四探针对样品的晶体结构与光电性能等进行了表征.结果表明,多层膜的平均透过率最高达86%,方块电阻达9/sq;ZAO膜层厚度对多层膜的导电性能影响很小,但严重影响可见光透过率;多层膜中的ZAO层仍呈ZnO晶态结构,且具有明显的c轴取向特征.这种三明治结构是一种性能优良的太阳能透明导电层候选材料.     

P型透明导电氧化物CuAlO2的研究进展

CuAlO₂作为一种天然的P型透明导电氧化物(TCO)成为近年来P型TCO的研究热点. 介绍了CuAlO₂近几年最新的研究进展, 简述了不同的制备方法及其优缺点, 综述了对其光电、热电等性能的研究状况, 对CuAlO₂掺杂前后性能改变的研究进展做了详细介绍, 并提出了CuAlO₂未来的研究方向.     

氧化锌透明导电膜的光电性能研究

采用磁控溅射法在载玻片上制备出Al3 掺杂型ZnO透明导电薄膜.对不同厚度薄膜的光电性能进行了研究.结果表明,所制备的薄膜随着厚度的增加,透过率略有下降;ZnO薄膜在可见光区的吸光度很小,对可见光几乎不吸收.     

磁控溅射在PI/石墨烯基体上制备氧化锌薄膜

聚酰亚胺(PI)/石墨烯复合薄膜兼备了可挠曲性及透明、导电性,可作为柔性透明导电电极用于柔性电子器件中。但附着于PI上的石墨烯易划伤,使其导电性变差。本文采用脉冲直流磁控溅射法,以PI/石墨烯为基体,镀制保护石墨烯的氧化锌薄膜。分别采用原子力显微镜、X射线衍射仪、台阶仪、霍尔效应仪及紫外-可见分光光度计检测PI/石墨烯/ZnO复合薄膜的表面形貌、晶体结构、薄膜厚度及导电、透光性能。结果表明,PI/石墨烯/ZnO复合薄膜结构致密,氧化锌以(002)为择优取向,最低方阻为1.9×104Ω/sq,略低于石墨烯的方阻,可见光区平均透光率达80%。     

透明导电GZO/Cu/GZO多层薄膜的室温生长及性能研究

研究Ga掺杂ZnO(GZO)和Cu薄膜形成的GZO/Cu/GZO多层薄膜体系,以期提高透明导电薄膜的综合性能。GZO/Cu/GZO多层薄膜由直流磁控溅射技术在室温下制备,研究Cu层厚度对多层薄膜结构、电学和光学性能的影响。结果表明GZO/Cu/GZO多层薄膜具有较好的结晶性能。随着Cu层厚度的增加,多层薄膜的可见光透射率有所降低,同时电学性能大幅度提升。在Cu层厚度为7.5 nm时,GZO/Cu/GZO多层薄膜获得最优的光电综合性能指标,且相对于单层GZO薄膜ΦTC因子从7.65×10-5Ω-1增加到1.48×10-3Ω-1。     

外延ZnO压电薄膜的声表面波特性分析

采用RF平面磁控溅射技术在单晶Al2O3衬底上淀积了ZnO薄膜.研究了ZnO薄膜的结构特性及电学性能,XRD结果表明:在Al2O3衬底上沉积的ZnO薄膜是高度c轴取向的.电阻率测试结果表明:在纯氧中高温退火,薄膜的电阻率提高到107Ω·cm量级.对于ZnO Al2O3结构的SAW器件,随着ZnO薄膜厚度的减小,其机电耦合系数降低,但声表面波速率增加.     

Influence of catalyst on structural and morphological properties of TiO2 nanostructured films prepared by sol–gel on glass

Transparent TiO2 thin films have been prepared by the sol-gel method using titanium alkoxides as precursors.Thin films were deposited on glass supports by the dip-coating technique.The TiO2 layer acts as a self-cleaning coating generated from its photocatalysis and photoinduced superhydrophilicity.The crystalline structure of TiO2 films was dominantly identified as the anatase phase,consisted of uniform spherical particles of about 14-50 nm in size,which strongly depends upon catalyst-type and heat treatment temperature.Increasing heat treating temperature can lead to an increase in crystalline size.The results indicated that the sample S.S(sample derived from sol containing sulfuric acid as catalyst) exhibits superhydrophilic nature and better photocatalytic activity,which can be attributed to its higher anatase content and lower crystalline size.Morphological studies,carried out using Atomic Force Microscopy(AFM),confirm the presence of crystalline phase with such a grain size and low surface roughness.Thus,the applied films exhibiting high photocatalytic activity,superhydrophilic behavior,and low surface roughness can be used as an efficient self-cleaning coating on glass and other optical applications.     

恒电流电沉积ZnO薄膜及其光电性能研究

采用恒电流电沉积的方法,在ITO导电玻璃上制备ZnO薄膜.通过X射线衍射仪、扫描电子显微镜等手段,对制备出的ZnO薄膜进行表征,并研究了溶液的pH值对薄膜的光学性质的影响.结果表明,电流密度为0.175mA·cm-2、pH为4.7时,制备出的ZnO薄膜具有纤锌矿结构,薄膜表面较均匀、致密,具有很好的附着力,在可见和近红外波段透过率约为80%,禁带宽度为3.37eV.光电流测试表明薄膜的导电类型为n型.     

ZnO薄膜的制备及其特性研究

采用射频磁控溅射技术生长出高质量（002）晶面取向的ZnO薄膜.通过XRD和AFM研究了射频功率和氧气比例对ZnO薄膜的结构和表面形貌的影响.研究结果显示,射频功率在50W下氧气比例为45%时,所生长的ZnO薄膜可以用于制作高质量的表面声波仪（SAW）.     

工作气压对溅射沉积铜铟镓硒薄膜形态和光学性能的影响

采用射频磁控溅射法,通过直接溅射铜铟镓硒四元合金靶在镀有Mo背电极的soda-lime玻璃衬底上获得铜铟镓硒(CIGS)薄膜.利用X线衍射(X-ray diffraction,XRD)、扫描电子显微镜(scanning electron microscope,SEM)和X线能量色散谱仪(energy dispersive X-ray spectroscopy,EDS)研究薄膜的结构、表面形貌和组织成分的变化,并通过紫外-可见分光光度计(ultraviolet and visible spectrophotometer,UV/VIS)获得薄膜的透过率光谱,研究不同工作气压对CIGS薄膜晶体结构、表面形貌和光学性能的影响.实验结果表明:在工作气压为0.8 Pa时制得的薄膜表面均匀致密,可见光范围内透光率接近于零,nCu/nIn+Ga=0.83,nGa/nIn+Ga=0.3,nSe/nCu+In+Ga=1,证明溅射所得CIGS吸收层薄膜的性能接近高效吸收层的要求.     

衬底温度对ZnO：Al薄膜结构和光透过性能的影响

利用超声喷雾热解方法以不同的沉积温度（450～530℃）在石英衬底上制备出具备较高光学质量的ZnO：Al（AZO）薄膜.通过X射线衍射谱（XRD）研究了薄膜的结构,用扫描电子显微镜（SEM）研究了薄膜的表面形貌,用紫外可见（UV）分光光度计对薄膜的光透过特性进行了测试分析.结果表明：所制备薄膜在可见波段具有较高透过率,并且沉积温度对AZO薄膜的结构和光透过性能有很大影响.在衬底温度为470℃时得到的AZO薄膜具有（002）择优取向,结晶质量最好、光透过率最高,在可见光区平均透过率达到85%以上.     

银锌复合透明抗菌薄膜的制备及其性能研究

采用sol—gel法，以正硅酸乙酯（Si（OC2H5）4）作为反应的前驱体，硝酸锌、硝酸银为抗菌活性成分，柠檬酸为配合剂，无水乙醇为溶剂，HNO3为催化剂，通过浸渍提拉法在普通的玻璃基片上制备银锌复合薄膜，用扫描电镜（SEM）和紫外可见光谱（UV-Vis）对薄膜进行了表征，抑菌圈法评价银锌复合薄膜的抗菌性能，结果表明：透明的银锌复合薄膜具有优良的抗菌性能。     

磁控溅射制备参数对 ZnO:Al电学性能的影响

ZnO:Al(ZAO)透明导电薄膜是一种n型半导体,有高的载离子浓度和大的光学禁带宽度,具有优异的电学和光学性能,有极广的应用前景.本文介绍了ZAO薄膜的广泛用途和今后研究的趋势,并着重分析了磁控溅射制备参数对电学性能的影响.     

IWO缓冲层对MOCVD-ZnO:B薄膜性能的影响研究

金属有机化学气相沉积(MOCVD)技术生长的绒面ZnO透明导电(ZnO-TCO)薄膜应用于Si基薄膜太阳电池上能够形成"陷光结构",以提高薄膜太阳电池效率和稳定性。本文将电子束反应蒸发技术生长的掺W的In2O3(In2O3:W,(IWO)薄膜作为缓冲层,应用于MOCVD-ZnO:B薄膜与玻璃之间,可促进ZnO:B薄膜的生长,并且有效提升薄膜的光散射特性。当IWO缓冲层厚度为20nm时,获得的IWO/ZnO:B薄膜的电阻率为2.07×10-3Ω.cm,迁移率为20.9cm2.V-1.s-1,载流子浓度为1.44×1020 cm-3;同时,薄膜具有的透过率大于85%,且在550nm处绒度较ZnO:B薄膜提高了约9.5%,在800nm处绒度较ZnO:B薄膜提高了约4.5%。     

不同氩气流量下溅射所得TiO_x薄膜的结构和光学性能

为探究不同氩气流量对TiOx薄膜结构和光学性能的影响,采用常温反应磁控溅射法,在K9双面抛光玻璃基底上制备TiOx薄膜样品,利用X线衍射分析样品的晶体结构,通过原子力显微镜观察样品表面结构,使用光栅光谱仪测试样品透射率,并计算得到薄膜沉积速率和消光系数等光学参数.实验结果表明:氩气流量对TiOx薄膜的光学性能具有较为明显的影响,随着氩气流量的增加,薄膜的光学厚度和沉积速率随之增加,而折射率有微小增加,消光系数受氩气流量的影响不大.     

Ba0.65Sr0.35TiO3薄膜的磁控溅射法制备与介电性能研究

用磁控溅射法在Pt/Ti/SiO2/Si衬底上沉积Ba0.65Sr0.35TiO3薄膜.研究沉积气压和衬底温度对BST薄膜结构及介电性能的影响.应用XRD和AFM表征薄膜的物相结构及其表面形貌,通过阻抗分析仪测量薄膜的介电性能.结果表明在3.0 Pa沉积气压和600℃衬底温度下制备的Ba0.65Sr0.35TiO3薄膜有较好的微结构和介电性能.