热轧中厚板氧化铁皮控制技术
引用本文:陈永利,查显文,陈礼清.热轧中厚板氧化铁皮控制技术[J].东北大学学报(自然科学版),2011,32(7):960-963,980.
作者姓名:陈永利  查显文  陈礼清
作者单位:1. 东北大学轧制技术及连轧自动化国家重点实验室,辽宁沈阳,110819
2. 东北大学轧制技术及连轧自动化国家重点实验室,辽宁沈阳110819 中冶东方工程技术有限公司秦皇岛研究设计院,河北秦皇岛066004
基金项目:国家高技术研究发展计划项目(2007AA03Z504)
摘    要:为了探究热轧中厚板氧化铁皮控制方法,分析了氧化铁皮的影响因素并提出相应的控制方法.试验及生产实践结果表明:降低Si和Mn含量,在成分中加入合金元素Gr可以有效抑制氧化铁皮;采用微正压、微氧化气氛快速加热对氧化铁皮有较好抑制作用;保证1 173℃以上的除鳞温度和合理除鳞设备参数,采用高温快轧、低温精轧的轧制节奏可以有效抑制中厚板氧化铁皮;轧制速度和压下率对氧化铁皮厚度和板面粗糙度有显著影响,压下率和轧制速度越大,氧化铁皮厚度和表面粗糙度越小.

关 键 词:热轧中厚板  组织  氧化铁皮  缺陷  

Control Techniques of Oxide Scales in Hot-Rolled Heavy and Medium Plates
CHEN Yong-li,CHA Xian-wen,CHEN Li-qing.Control Techniques of Oxide Scales in Hot-Rolled Heavy and Medium Plates[J].Journal of Northeastern University(Natural Science),2011,32(7):960-963,980.
Authors:CHEN Yong-li  CHA Xian-wen  CHEN Li-qing
Institution:CHEN Yong-li1,CHA Xian-wen1,2,CHEN Li-qing1(1.State Key Laboratory of Rolling and Automation,Northeastern University,Shenyang 110819,China,2.BERIS Qinhuangdao Engineering & Research Corporation,Qinhuangdao 066004,China.)
Abstract:Formation mechanism of iron oxide scales in hot-rolled heavy and medium plates was analyzed to explore the control method of oxide scales.The experimental and industrial results showed that the lower Si and Mn contents,the addition of Gr,the rapid heating with slight positive pressure and partial-pressure oxidization atmosphere,the descaling temperature above 1 173 ℃ and the reasonable equipment parameters of descaler can inhibit the formation of iron oxide scales.Adopting reasonable rolling parameters,high-temperature fast rolling and low-temperature finish rolling can also effectively reduce oxide scales.Rolling speed and reduction ratio can significantly affect the oxide scale thickness and surface roughness.The thickness and surface roughness of oxide scale decrease with the increase of reduction rate and rolling speed.
Keywords:hot-rolled heavy and medium plate  structure  oxide scale  defect  