Structure and magnetic properties of [FePt/Ag]10 multilayer films |
| |
作者姓名: | XUXiaohong WANGFang WUHaishun |
| |
作者单位: | SchoolofChemistryandMaterialsScience,ShanxiNormalUniversity,Linfen041004,China |
| |
摘 要: | FePt/Ag]10 multilayers were deposited on glass substrates by magnetron sputtering. After being annealed at 550℃ for 30 rain, the coercivities of FePt/Ag]10 multilayer films were observably improved. Magnetic properties ofFePt/Ag]10 multilayer films are influenced by the Ag content. The highest coercivity is obtained for those multilayer films that the Ag content is about 25%. The analysis for the remanence curves shows that the lower FePt layer thickness is favorable for decreasing the intergranular interaction. Result of XRD shows that a thick Ag layer can enhance the intensity of FePt(001) peak. A magnetic activation volume of the order of 10^-24 m^3 is obtained by the measurement of magnetic viscosity, showing that it is promising to be ultrahigh density recording media.
|
关 键 词: | [FePt/Ag]10 多层薄膜 化学结构 磁性 矫顽力 磁交换量 薄膜材料 |
收稿时间: | 2004-03-30 |
修稿时间: | 2004-06-26 |
本文献已被 CNKI 维普 万方数据 SpringerLink 等数据库收录! |
| 点击此处可从《中国科学通报(英文版)》浏览原始摘要信息 |
| 点击此处可从《中国科学通报(英文版)》下载免费的PDF全文 |