| 苯乙烯-马来酸酐交替共聚物合成及表征 |
| |
| 引用本文： | 唐炳涛,赵杰,张淑芬,王晓敏.苯乙烯-马来酸酐交替共聚物合成及表征[J].大连理工大学学报,2011,51(3):326-330. |
| |
| 作者姓名： | 唐炳涛 赵杰 张淑芬 王晓敏 |
| |
| 作者单位： | 大连理工大学精细化工国家重点实验室; |
| |
| 基金项目： | 国家自然科学基金青年基金资助项目(20804007); 教育部长江学者与创新团队发展计划资助项目(IRT0711);教育部高等学校博士学科点专项科研基金资助项目(200801411032); 大连理工大学人才引进基金资助项目(893381) |
| |
| 摘 要： | 以过氧化苯甲酰(BPO)为引发剂,甲苯为溶剂,采用溶液沉淀聚合工艺合成了苯乙烯-马来酸酐共聚物,并详细考察了聚合温度、引发剂用量、单体配比及聚合时间对聚合反应的影响.结果表明在温度80℃、引发剂用量0.7%、苯乙烯与马来酸酐配比1:1、时间2 h的条件下,聚合物收率可达96.6%.用13C NMR、IR、GPC、元素分...
|
| 关 键 词： | 苯乙烯 马来酸酐 交替共聚物 |
Synthesis and characterization of styrene-maleic anhydride alternating copolymers |
| |
| TANG Bingtao,ZHAO Jie,ZHANG Shufen,WANG Xiaomin.Synthesis and characterization of styrene-maleic anhydride alternating copolymers[J].Journal of Dalian University of Technology,2011,51(3):326-330. |
| |
| Authors: | TANG Bingtao ZHAO Jie ZHANG Shufen WANG Xiaomin |
| |
| Institution: | TANG Bing-tao*,ZHAO Jie,ZHANG Shu-fen,WANG Xiao-min(State Key Laboratory of Fine Chemicals,Dalian University of Technology,Dalian 116024,China) |
| |
| Abstract: | Styrene-maleic anhydride copolymer was synthesized by solution sediment polymerization method with BPO as initiator and toluene as solvent.The effect of polymerization temperature,dosage of initiator,ratio of monomer and polymerization time on polymerization was researched in detail.The yield of the copolymer can reach 96.6% under the conditions of polymerization temperature 80 ℃,initiator dosage 0.7%,molar ratio of styrene to maleic anhydride 1∶1 and polymerization time 2 h.The structure of the copolymer was confirmed by 13C NMR,IR,GPC and elemental analysis.Also,the thermal stability of the copolymer was tested by TG.Based on the analytical results of HPLC of polymeric residual liquid,elemental analysis and 13C NMR of the copolymer,the structure of styrene-maleic anhydride copolymer is confirmed to be alternating copolymer. |
| |
| Keywords: | styrene maleic anhydride alternating copolymer |