Study on the hydrogen storage property of (TiZr0.1)xCr1.7-yFeyMn0.3 (1.05

The hydrogen storage of (TiZr_0.1)_xCr_1.7-yFe_yMn_0.3 (1.05?<x?<?1.2, 0.2?<y?<?0.6) alloys, prepared by Ar plasma arc melting, were investigated by X-ray diffraction, pressure-composition- temperature (PCT). The results indicated that all (TiZr_0.1)_xCr_1.7-yFe_yMn_0.3 (1.05?≤x?≤?1.2, 0.2?≤y?≤?0.6) alloys were determined as C14-type Laves phase, the cell parameters a, c and unit cell volume of (TiZr_0.1)xCr_1.1Fe_0.6Mn_0.3 (1.05?≤x?≤?1.2) alloys increased with increasing the (TiZr) super-stoichiometry from 1.05 to 1.2, and the value of a/c almost unchanged. The hydrogen absorption and desorption plateau pressure decreased from 5.6, 4.4–2.6, 2.2?MPa with the increase of (TiZr) super-stoichiometry from 1.05 to1.2 at 274?K respectively, and the hydrogen desorption plateau pressure decline was not obvious when the (TiZr) super-stoichiometry exceeded 1.15. The (TiZr_0.1)_1.1Cr_1.1Fe_0.6Mn_0.3 alloy had the best comprehensive properties about the maximum and reversible hydrogen storage capacity was 1.79 and 1.45?wt% respectively. The cell parameters a, c and unit cell volume of (TiZr_0.1)_1.1Cr_1.7-yFe_yMn_0.3(0.2?≤y?≤?0.6) alloys increased as the ratio of Fe/Cr content decreased. The hydrogenation and dehydrogenation plateau pressure decreased from 4.5, 3.4–1.0, 0.9?MPa respectively and the maximum hydrogen storage capacity increased from 1.79 to 2.0?wt% as the Fe content reduced from 0.6 to 0.2 at 274?K. The maximum and the reversible hydrogen storage capacity were about 2.0 and 1.65?wt% as the ratio of Fe/Cr was 0.13 (ie, (TiZr_0.1)_1.1Cr_1.5Fe_0.2Mn_0.3 alloy), its relative molar enthalpy of dissociation hydrogen was 24.30?kJ/mol H₂.