Microstructure evolution and mechanical properties of Ti_2AlNb/TiAl brazed joint using newly-developed Ti–Ni–Nb–Zr filler alloy

Joining of Ti_2AlNb alloy to TiAl intermetallics was conducted by the newly-developed Ti–Ni–Nb–Zr brazing filler alloy.The microstructure evolution of the joints was investigated by scanning electron microscope (SEM),energy dispersive spectrometer (EDS) and electron backscatter diffraction (EBSD).The macro-micro mechanical properties were studied by shear test and nano-indentation test.Typical interfacial microstructures across the brazing seam were Ti_2AlNb substrate,α_2-Ti_3Al+β-Ti,γ-TiAl+Ti_2Ni+TiNi+α_2-Ti_3Al,α_2-Ti_3Al+β-Ti,TiAl substrate.The Ti_2Ni phase were firstly dissolved in the joints brazed at 1000°C for 10 min and then precipitated after a prolonged holding time of 15 min.The nano-indentation test revealed that Ti_2Ni phase exhibited the highest hardness of 12.60 GPa.The joints brazed at 1000°C/15 min presented the maximum shear strength of271 MPa.The dissolution and precipitation behavior of Ti_2Ni phase was also discussed.

Microstructure evolution and mechanical properties of Ti2AlNb/TiAl brazed joint using newly-developed Ti–Ni–Nb–Zr filler alloy

Joining of Ti₂AlNb alloy to TiAl intermetallics was conducted by the newly-developed Ti–Ni–Nb–Zr brazing filler alloy. The microstructure evolution of the joints was investigated by scanning electron microscope (SEM), energy dispersive spectrometer (EDS) and electron backscatter diffraction (EBSD). The macro-micro mechanical properties were studied by shear test and nano-indentation test. Typical interfacial microstructures across the brazing seam were Ti₂AlNb substrate, α₂-Ti₃Al+β-Ti, γ-TiAl+Ti₂Ni+TiNi+α₂-Ti₃Al, α₂-Ti₃Al+β-Ti, TiAl substrate. The Ti₂Ni phase were firstly dissolved in the joints brazed at 1000 °C for 10 min and then precipitated after a prolonged holding time of 15 min. The nano-indentation test revealed that Ti₂Ni phase exhibited the highest hardness of 12.60 GPa. The joints brazed at 1000 °C/15 min presented the maximum shear strength of 271 MPa. The dissolution and precipitation behavior of Ti₂Ni phase was also discussed.