Spin dynamics characteristics of nitrogen vacancy spins in diamond films
using enhanced Raman shift with spin microscopy |
| |
Authors: | Ren Ren Yaru Guo Jin Xu Dandan Xue Bai Yan and Xuan Li |
| |
Institution: | 1. Department of Physics, MOE Key Lab for Non-equilibrium, Xi’an Jiaotong University, Xian 710054, China;2. Institute of Biomedical Engineering, Xi’an Jiaotong University, Xian 710054, China |
| |
Abstract: | The diamond films were deposited on a Si substrate with chemical vapor deposition MCVD using methanehydrogen gas.Raman active phonon and sp~2/sp~3 ratio in diamond/Si(100)films were investigated by Raman spectra in the difference scattering configurations.Furthermore,the Raman scattering spectrum of diamond/Si(100)hetero-junction was measured with different thickness to investigate the spin dynamics of nitrogen vacancy spins.The Fluorescence scanning microscopy indicated that nitrogen vacancy center electron spin was coupled to the host nitrogen nuclear spin by the electron spin resonance.The strong peak of 1332 cm~(-1)displayed the F_(2g)symmetry of diamond,while the broad E_(2g)mode peak of 1550 cm~(-1)was a broad band G mode,and 1150 cm~(-1)peak corresponded to the nano-diamond and disordered graphitic carbon form with disordered SP~2 hybridization.The Raman spectra of the diamond films were observed as a function of the residual stress,crystal size and their orientation.The peaks of 1132 cm~(-1)and 1480 cm~(-1)were associated with hydrogen bonding.The transport of diamond exhibited sp~3 spin related effect.The diamond/Si(100)PDOS is the results of spin-related couple of sp~3,p and d orbital hybridization.The spin dynamics was achieved by the orbital competition,strong crystal field and charge order. |
| |
Keywords: | Diamond films Dynamics of nitrogen vacancy Spin-orbit dynamics Raman shift Spin microscopy |
本文献已被 CNKI ScienceDirect 等数据库收录! |
| 点击此处可从《自然科学进展(英文版)》浏览原始摘要信息 |
| 点击此处可从《自然科学进展(英文版)》下载免费的PDF全文 |