| FeCrAl多孔材料烧结体表面球状物和结壳形成原因研究 |
| |
| 引用本文： | 李昊,孙浩,孙继锋,邱汉迅.FeCrAl多孔材料烧结体表面球状物和结壳形成原因研究[J].上海理工大学学报,2019,40(5):22-26,31. |
| |
| 作者姓名： | 李昊 孙浩 孙继锋 邱汉迅 |
| |
| 作者单位： | 上海理工大学 材料科学与工程学院, 上海 200093;上海材料研究所 上海市工程材料应用与评价重点实验室, 上海 200437,上海材料研究所 上海市工程材料应用与评价重点实验室, 上海 200437,上海材料研究所 上海市工程材料应用与评价重点实验室, 上海 200437,上海理工大学 材料科学与工程学院, 上海 200093 |
| |
| 摘 要： | 以FeCrAl粉末为原料，采用粉末冶金法制备FeCrAl多孔材料，试样烧结后表面出现球状物和结壳现象。采用光学显微镜、扫描电子显微镜和X射线能谱仪等设备，对球状物和结壳进行表征，探讨其形成原因并提出预防措施。结果表明：烧结体表面产生球状物和结壳与材料增碳（C）有关。C来源于黏结剂和石墨发热体，在烧结过程中会促进样品表层烧结，形成壳层；C的进一步渗入会降低表层区域熔点，使表层熔化形成液相，冷却后形成球状物。采用硅钼发热体烧结炉可避免试样表面产生球状物和结壳。
|
| 关 键 词： | FeCrAl 烧结 结壳层 球状物 渗C |
| 收稿时间： | 2018/12/26 0:00:00 |
Study on the Formation of Spheres and Crust on the Surface of Sintered FeCrAl Porous Materials |
| |
| LI Hao,SUN Hao,SUN Jifeng and QIU Hanxun.Study on the Formation of Spheres and Crust on the Surface of Sintered FeCrAl Porous Materials[J].Journal of University of Shanghai For Science and Technology,2019,40(5):22-26,31. |
| |
| Authors: | LI Hao SUN Hao SUN Jifeng and QIU Hanxun |
| |
| Institution: | School of Materials Science and Engineering, University of Shanghai for Science and Technology, Shanghai 200093, China;Shanghai Research Institute of Materials Shanghai Key Laboratory of Engineering Materials Application and Evaluation, Shanghai 200437, China,Shanghai Research Institute of Materials Shanghai Key Laboratory of Engineering Materials Application and Evaluation, Shanghai 200437, China,Shanghai Research Institute of Materials Shanghai Key Laboratory of Engineering Materials Application and Evaluation, Shanghai 200437, China and School of Materials Science and Engineering, University of Shanghai for Science and Technology, Shanghai 200093, China |
| |
| Abstract: | Porous FeCrAl was prepared by powder metallurgy using pre-alloyed FeCrAl powders as raw material. Spheres and crust appeared on the sample surface after sintering. The spheroids and crust were characterized by means of optical microscope, scanning electron microscope and X-ray energy spectrometer. The causes of their formation were discussed, and the precautions were proposed. The results show that the formation of globules and crust on the sintered body surface is related to the carburization (C) of materials. C comes from the binder and the graphite heater, which can promote the sintering of the sample surface and form the crust during the sintering process. The further infiltration of C can reduce the melting point of the surface area, make the surface melt into liquid phase, and form globules after cooling. The formation of globules and crust on the sample surface can be avoided by using silicon-molybdenum heater sintering furnace. |
| |
| Keywords: | FeCrAl sintering crust spheres carburization |
|