| 真空碳热还原酸浸含钛高炉渣制备TiC分析 |
| |
| 引用本文： | 胡蒙均,尹方庆,魏瑞瑞,邓青宇,扈玫珑.真空碳热还原酸浸含钛高炉渣制备TiC分析[J].重庆大学学报(自然科学版),2015,38(6):99-106. |
| |
| 作者姓名： | 胡蒙均 尹方庆 魏瑞瑞 邓青宇 扈玫珑 |
| |
| 作者单位： | 1. 重庆钢铁集团 有限 责任公司,重庆,400080;2. 重庆大学 材料科学与工程学院,重庆,400044 |
| |
| 基金项目： | 国家自然科学基金资助(51404044)；高等学校博士学科点专项科研基金资助项目(20130191110015)。 |
| |
| 摘 要： | 含钛高炉渣中含有20%~30%的TiO_2,是一种附加值较高的二次资源,但在综合利用过程中存在氧化物还原难度大,硅钛难分离,二次污染严重等问题。基于热力学理论基础,采用真空碳热还原联合酸浸工艺处理含钛高炉渣制备TiC。结果表明:真空有助于钛氧化物彻底还原,可实现渣中硅钛彻底分离,减少酸耗量,降低二次污染。真空碳热还原联合酸浸工艺处理含钛高炉渣(TiO_2含量23%左右)制备TiC的最佳条件为:炉渣粒度200目,还原温度1 673K,渣碳质量比100∶38。
|
| 关 键 词： | 真空 碳热还原 酸浸 含钛高炉渣 TiC |
| 收稿时间： | 2015/7/17 0:00:00 |
Preparation of TiC by carbothermal reduction in vacuum and acid leaching process using titanium bearing blast furnace slag |
| |
| HU Mengjun,YIN Fangqing,WEI Ruirui,DENG Qingyu and HU Meilong.Preparation of TiC by carbothermal reduction in vacuum and acid leaching process using titanium bearing blast furnace slag[J].Journal of Chongqing University(Natural Science Edition),2015,38(6):99-106. |
| |
| Authors: | HU Mengjun YIN Fangqing WEI Ruirui DENG Qingyu and HU Meilong |
| |
| Institution: | Chongqing Iron & Steel groupCo., Lt, Chongqing 400080, P.R.China;,College of Materials Science and Engineering, Chongqing University, Chongqing 400044, P.R.China,College of Materials Science and Engineering, Chongqing University, Chongqing 400044, P.R.China,College of Materials Science and Engineering, Chongqing University, Chongqing 400044, P.R.China and College of Materials Science and Engineering, Chongqing University, Chongqing 400044, P.R.China |
| |
| Abstract: | Titanium bearing blast furnace slag with 20%-30% titanium dioxide is a valuable second resource.The main problems to utilize the resource are the reduction of the titanium oxides,the separation of titanium and silicon and the second pollution.The main aim of the research is to prepare TiC by the united process of carbothermal reduction in vacuum and acid leaching based on the thermodynamics calculation.The results show that decreasing pressure of the system is helpful for the reduction of the titanium oxides.Titanium and silicon in slag can be separated completely.The second pollution decreases due to evaporation of Mg and SiO produced in vacuum condition.The optimum conditions for the united process to prepare TiC are slag size of 200 mesh,temperature of 1 673 K,and the mass ratio of slag to reductant of 100∶38. |
| |
| Keywords: | vacuum carbothermal reduction acid leaching titanium bearing blast furnace slag TiC |