Production and characterization of high porosity porous Fe-Cr-C alloys by the space holder leaching technique |
| |
Authors: | Da-rong Tian Yu-hua Pang Liang Yu Li Sun |
| |
Institution: | 1. School of Metalurgical Engineering, Xi'an University of Architecture and Technology, Xi'an 710055, China;2. AVIC Xi’an Aircraft Industry Group Company Ltd., Xi’an 710000, China |
| |
Abstract: | Spherical carbamide particles were employed to produce porous Fe–Cr–C alloy with high porosity and large aperture via the space-holder leaching technique. A series of porous samples were prepared by regulating the processing parameters, which included the car-bamide content and the compaction pressure. The pore characteristics and compression properties of the produced samples were investigated. The samples were characterized by scanning electron microscopy, image analysis, and compression tests. The results showed that the macro-porosity and the mean pore size were in the ranges 40.4%–82.4% and 0.6–1.5 mm, respectively. The compressive strength varied be-tween 25.38 MPa and 127.9 MPa, and was observed to decrease with increasing total porosity. |
| |
Keywords: | porous metal powder metallurgy cellular manufacturing porosity compressive strength |
本文献已被 万方数据 SpringerLink 等数据库收录! |
| 点击此处可从《矿物冶金与材料学报》浏览原始摘要信息 |
| 点击此处可从《矿物冶金与材料学报》下载免费的PDF全文 |