橡胶沥青混合料的疲劳性能
引用本文:黄卫东,王翼,高川,李昆.橡胶沥青混合料的疲劳性能[J].同济大学学报(自然科学版),2009,37(11).
作者姓名:黄卫东  王翼  高川  李昆
作者单位:1. 同济大学道路与交通工程教育部重点实验室,上海,201804
2. 深圳高速工程顾问有限公司,广东深圳,518034
基金项目:国家自然科学基金资助项目 
摘    要:参考美国AASHTO TP8标准要求,根据中国沥青混合料的成型现状,采用MTS(material test system)控制加载,选择改进的三分点加载小梁弯曲疲劳试验评价了亚利桑那州体系下的橡胶沥青混合料的疲劳性能.试验结果表明:橡胶沥青混合料的疲劳寿命与应变水平有着很好的线性关系;使用了间断级配和高沥青用量的橡胶沥青混合料的疲劳性能明显好于一般AC-13级配下的SBS(苯乙烯-丁二烯-苯乙烯嵌段共聚物)改性沥青混合料和基质沥青混合料;橡胶沥青混合料优异的疲劳性能与高温稳定性与沥青及特殊的级配有密切关系.

关 键 词:橡胶沥青  疲劳性能  改性沥青  沥青混合料  级配

Fatigue Properties of Asphalt Rubber Mixtures
HUANG Weidong,WANG Yi,GAO Chuan and LI Kun.Fatigue Properties of Asphalt Rubber Mixtures[J].Journal of Tongji University(Natural Science),2009,37(11).
Authors:HUANG Weidong  WANG Yi  GAO Chuan and LI Kun
Institution:Key Laboratory of Road and Traffic Engineering of the Ministry of Education, Tongji University,Shanghai 201804,China;Key Laboratory of Road and Traffic Engineering of the Ministry of Education, Tongji University,Shanghai 201804,China;Shenzhen Expressway Engineering Consultants Co.Ltd,Shenzhen 518034,China;Key Laboratory of Road and Traffic Engineering of the Ministry of Education, Tongji University,Shanghai 201804,China
Abstract:According to AASHTO TP8 in American standard specification, three point bending fatigue loading test method was modified to evaluate the fatigue properties of asphalt rubber (AR) mixture according to Arizona specification.Material test system was used to strain-control mode. Test result shows that the relation between fatigue life and strain level of AR gap-graded mixture is in a good linearity.Compared to traditional AC- 13 gradation mixture which two conventional binders including polymer-modified asphalt (PMA) and conventional asphalt are used, AR gap-graded mixture presents a better fatigue performance. Rutting test is also used to evaluate the high temperature performance, AR gap-graded mixture whose asphalt content is 1.6 times higher than PMA mixture's still shows the same high temperature performance as PMA mixture. The excellent fatigue performance and high temperature performance of AR mixture is mainly due to three reasons, high crumb rubber content in asphalt makes the AR super high performance; gap gradation makes the mixture accommodate high asphalt content; high asphalt and crumb rubber contents in asphalt make the AR mixture excellent fatigue performance.
Keywords:asphalt rubber  fatigue performance  polymermodified asphalt  asphalt mixture  gradation