| POSS掺杂改性聚氨酯水性分散体乳液的研究 |
| |
| 引用本文： | 张其荣,杨正龙,浦鸿汀,袁俊杰.POSS掺杂改性聚氨酯水性分散体乳液的研究[J].同济大学学报(自然科学版),2009,37(10). |
| |
| 作者姓名： | 张其荣 杨正龙 浦鸿汀 袁俊杰 |
| |
| 作者单位： | 1. 同济大学,汽车学院,上海201804;同济大学,先进土木工程材料教育部重点实验室,上海,200092
2. 同济大学,先进土木工程材料教育部重点实验室,上海,200092 |
| |
| 基金项目： | 国家自然科学基金资助项目，上海市纳米专项基金资助项目，光大环保创新基金资助项目 |
| |
| 摘 要： | 采用化学改性方法制备了一种POSS掺杂改性的聚氨酯水性分散体乳液,并采用投射电镜等多种测试手段对POSS掺杂聚氨酯分散体及其涂膜的微观结构、热、光和力学等性能进行表征和研究.结果表明,该乳液具有良好的室温贮存稳定性能(>90 d),POSS与水性聚氨酯分散体具有良好的相容性和协同增强效应.POSS的掺杂改性不仅能够提高聚氨酯涂膜的耐热性能,显著提高水性聚氨酯涂膜的硬度和耐水性,同时该掺杂聚氨酯涂膜还具有优异的抗紫外光能力.
|
| 关 键 词： | 聚氨酯水性分散体 掺杂改性 乳液 抗紫外光性能 |
Study of POSS Modified Polyurethane Aqueous Dispersions Emulsions |
| |
| ZHANG Qirong,YANG Zhenglong,PU Hongting and YUAN Junjie.Study of POSS Modified Polyurethane Aqueous Dispersions Emulsions[J].Journal of Tongji University(Natural Science),2009,37(10). |
| |
| Authors: | ZHANG Qirong YANG Zhenglong PU Hongting and YUAN Junjie |
| |
| Institution: | School of Automotive Engineering,Tongji University,Shanghai 201804,China; Key Laboratory of Advanced Civil Engineering Materials of the Ministry of Education,Tongji University,Shanghai 200092,China;Key Laboratory of Advanced Civil Engineering Materials of the Ministry of Education,Tongji University,Shanghai 200092,China;Key Laboratory of Advanced Civil Engineering Materials of the Ministry of Education,Tongji University,Shanghai 200092,China;Key Laboratory of Advanced Civil Engineering Materials of the Ministry of Education,Tongji University,Shanghai 200092,China |
| |
| Abstract: | Polyurethane aqueous dispersions chemically doped by polyhedral oligomeric silsesquioxane(POSS) were prepared in this paper.The resulting polyurethane dispersions and their thin films were characterized and investigated by transmission electron microscopy(TEM),scanning electron microscope(SEM) based on the particle size measurements,thermo gravimetric analysis(TGA),UV-Vis and basic mechanical tests.The results show that the POSS has good compatibility and synergistic enhancement performance with polyurethane dispersions,and the resulting doping polyurethane dispersions emulsions have good solution stability at room temperature (> 90 d).By introducing POSS,polyurethane dispersions films have enhanced heat resistance,water resistance and mechanical strength as well as much more UV resistance than pure polyurethane film. |
| |
| Keywords: | POSS |