高速电弧喷涂FeCrAl/WC复合涂层研究
引用本文:胡军志,马世宁,陈学荣,徐滨士.高速电弧喷涂FeCrAl/WC复合涂层研究[J].同济大学学报(自然科学版),2001,29(12):1447-1450.
作者姓名:胡军志  马世宁  陈学荣  徐滨士
作者单位:装甲兵工程学院材料科学与工程系,
基金项目:"九五"国家重点科技攻关项目(96-A 22-04-05);清华大学摩擦学国家重点实验室基金资助项目
摘    要:将自行研制的FeCrAl/WC粉芯丝材利用高速电弧喷涂技术成功地制备出FeCrAl/WC复合涂层,用EDS,XRD和成分分析系统得到FeCrAl/WC涂层的组成为FeCr的质量分数约为84%;WC,W2C及少量的(FeCr)2O3的Al2O3的质量分数约为16%。涂层的工艺性能和力学性能表明FeCrAl/WC复合涂层具有高结合强度、高致密度和较多氧化物的特点。涂层的高温冲蚀性能结果表明,在650℃高温环境下,FeCrAl/WC复合涂层的抗冲蚀磨损性能高于20号钢,并表现出良好的全攻角冲蚀磨损抗力,能够解决燃煤锅炉管道的高温燃气-飞灰高温冲蚀磨损问题。

关 键 词:高速电弧喷涂  FeCrAl基复合涂层  冲蚀磨损  粉芯丝材  Al基复合涂层
文章编号:0253-374X(2001)12-1447-04
修稿时间:2001年5月16日

Development of FeCrAl/WC Intermetallic Coating Produced by High Velocity Arc Spraying
HU Jun-zhi,MA Shi-ning,CHEN Xue-rong,XU Bin-shi.Development of FeCrAl/WC Intermetallic Coating Produced by High Velocity Arc Spraying[J].Journal of Tongji University(Natural Science),2001,29(12):1447-1450.
Authors:HU Jun-zhi  MA Shi-ning  CHEN Xue-rong  XU Bin-shi
Abstract:A novel cored wire for producing FeCrAl/WC intermetallic coating by arc spraying was developed.High velocity arc wire spray technology was successfully applied to prepare the FeCrAl/WC coating.It shows that the cored wire arc sprayed FeCrAl/WC coating consists of 84?Cr and 16%WC,W 2C,(FeCr) 2O 3 and Al 2O 3 by energy dispersive X-ray(EDX),X-ray diffraction(XRD),scanning electron microscope(SEM) and image analyzer.Technical parameters and mechanics of FeCrAl/WC coating had been investigated.The results indicate that the coating has high bonds,high compacting and many fractions.As compared with water wall tube material of power station boiler,the erosion-corrosion resistance at elevated temperature of FeCrAl/WC coating is higher than that of 20 steel.At the same time,the coating is of excellent erosion-corrosion resistance under every impactive angle.The results indicate that erosive condition of high temperature flue gas and fly ash mixture in boiler tube of pulverized coal fired power station can be solved by FeCrAl/WC coating.
Keywords:high velocity arc wire  FeCrAl/WC intermetallic coating  erosion-corrosion  cored wire