| 六钛酸钾晶须掺杂改性气凝胶的结构和性能 |
| |
| 引用本文： | 林本兰,崔升,沈晓冬,冷映丽,腾凯明,江国栋.六钛酸钾晶须掺杂改性气凝胶的结构和性能[J].南京工业大学学报(自然科学版),2012,34(1):20-23. |
| |
| 作者姓名： | 林本兰 崔升 沈晓冬 冷映丽 腾凯明 江国栋 |
| |
| 作者单位： | 1. 南京工业大学材料科学与工程学院,江苏南京210009;南京工业大学学报编辑部,江苏南京210009
2. 南京工业大学材料科学与工程学院,江苏南京,210009 |
| |
| 基金项目： | 国家自然科学基金委员会-中国工程物理研究院联合基金资助项目，江苏省自然科学基金重点资助项目 |
| |
| 摘 要： | 以六钛酸钾晶须（PTW）为遮光剂,掺入SiO2气凝胶中降低气凝胶的热导率。研究偶联剂的种类和添加量、PTW掺入量对气凝胶热导率、密度和比表面积等性能的影响。采用X线衍射仪（XRD）、傅立叶红外光谱仪（FT-IR）、扫描电子显微镜（SEM）对气凝胶进行表征。结果表明:0.5 mL KH550对10 g PTW进行表面改性后,将PTW按照质量分数28.57%掺入SiO2气凝胶中可使其热导率降至0.023 55 W/（m·K）。PTW在气凝胶中保持原有的晶体结构,SiO2仍保持无定形网络结构。
|
| 关 键 词： | SiO2气凝胶 六钛酸钾晶须 掺杂 遮光剂 热导率 |
Microstructure and properties of PTW-doped SiO2 aerogels |
| |
| LIN Benlan
,
CUI Sheng
,
SHEN Xiaodong
,
LENG Yingli
,
TENG Kaiming
,
JIANG Guodong.Microstructure and properties of PTW-doped SiO2 aerogels[J].Journal of Nanjing University of Technology,2012,34(1):20-23. |
| |
| Authors: | LIN Benlan CUI Sheng SHEN Xiaodong LENG Yingli TENG Kaiming JIANG Guodong |
| |
| Institution: | 1 (1.College of Materials Science and Technology,Nanjing University of Technology,Nanjing 210009,China; 2.Editorial Board of Journal,Nanjing University of Technology,Nanjing 210009,China) |
| |
| Abstract: | Titanium potassium whisker（PTW） was used as opacifier to reduce the thermal conductivities of SiO2 aerogels.The effects on thermal conductivity,density,specific surface area with category and dosage of coupling agent,and dosage of PTW were investigated.The aerogels were characterized by X-ray diffraction（XRD）,Fourier transform infrared spectroscopy（FT-IR）,and scanning electron microscope （SEM）.The results showed that 10 g PTW was modified by 0.5 mL KH550,and then 28.57%PTW in SiO2 aerogels could reduce the thermal conductivity to be 0.023 55 W/（m·K）.PTW remained the crystal structure in SiO2 aerogels,and SiO2 kept its amorphous network structure. |
| |
| Keywords: | silica aerogel titanium potassium whisker(PTW) PTW-doped opacifier thermal conductivity |
| 本文献已被 CNKI 万方数据 等数据库收录！ |
|