二步冷轧对铁素体不锈钢深冲性能和织构的影响

比较了一步冷轧和二步冷轧对铁素体不锈钢深冲性能和织构的影响.结果显示,采用一步冷轧(冷轧压下率90%)后,获得了高的平均r值(rm=1.92),且45°方向的r值要大于轧向和横向的r值,导致了材料的Δr呈负值(Δr=-0.31);在总压下率一定的情况下,采用二步冷轧后,薄板的平均r值变化不大(rm=1.90),但材料的平面各向异性很小(Δr=0.14).对两种工艺的再结晶织构分析表明,一步冷轧后薄板生成了强烈的γ织构,但是织构的峰值明显偏离了{111}轴,位于{223}〈582〉处;二步冷轧后薄板则生成了均匀的γ再结晶织构.

Effect of Two-Step Cold Rolling on Deep Drawability and Texture of Ferritic Stainless Steel

The effects of one-step and two-step cold rolling scheduh on deep drawability and texture of ferritic stainless Steel were investigated comparatively.The results showed that the high average plastic strain ratio r_m=1.92,especially the diagonal r-value at 45°which is higher than either longitudinal or transverse r-value were achieved after the one-step cold rolling with a percentage reduction up to 90%.Thus.the value of planar anisotropy parameter △_r becomes negative,i.e.,△7.=-0.31.With the total reduction kept constant,the average r-value of the sheet as the products from the two-step cold rolling fluctuates little(r_m=1.90)with △_r=0.14,a very small value.The analysis results of recrystallization texture revealed that in the sheet from one-step cold rolling an intensified γ texture forms,and its peak value deviates from{111}axial orientation but shift to the orientation{223}(582).However,in the sheet from two-step cold rolling a homogeneous γ recrystallization texture forms.