The Al–Al_2O_3–MgO composites with added aluminum contents of approximately 0wt%, 5wt%, and 10wt%, named as M_1, M_2, and M_3, respectively, were prepared at 1700°C for 5 h under a flowing N_2 atmosphere using the reaction sintering method. After sintering, the Al–Al_2O_3–MgO composites were characterized and analyzed by X-ray diffraction, scanning electron microscopy, and energy-dispersive X-ray spectroscopy. The results show that specimen M_1 was composed of MgO and MgAl_2O_4. Compared with specimen M_1, specimens M_2 and M_3 possessed MgAlON, and its production increased with increasing aluminum addition. Under an N_2 atmosphere, MgO, Al_2O_3, and Al in the matrix of specimens M_2 and M_3 reacted to form MgAlON and AlN-polytypoids, which combined the particles and the matrix together and imparted the Al–Al_2O_3–MgO composites with a dense structure. The mechanism of MgAlON synthesis is described as follows. Under an N_2 atmosphere, the partial pressure of oxygen is quite low; thus, when the Al–Al_2O_3–MgO composites were soaked at 580°C for an extended period, aluminum metal was transformed into AlN. With increasing temperature, Al_2O_3 diffused into AlN crystal lattices and formed AlN-polytypoids; however, MgO reacted with Al_2O_3 to form MgAl_2O_4. When the temperature was greater than(1640 ± 10)°C, AlN diffused into Al_2O_3 and formed spinel-structured AlON. In situ MgAlON was acquired through a solid-solution reaction between AlON and Mg Al_2O_4 at high temperatures because of their similar spinel structures.
|