| 制备介孔复合环境材料的酸洗刻蚀工艺 |
| |
| 引用本文： | 李天昕,林海,宋存义,徐玉琴.制备介孔复合环境材料的酸洗刻蚀工艺[J].北京科技大学学报,2004,26(3):237-239. |
| |
| 作者姓名： | 李天昕 林海 宋存义 徐玉琴 |
| |
| 作者单位： | 北京科技大学土木与环境工程学院,北京,100083 |
| |
| 摘 要： | 探索了一种制备介孔复合环境材料的方法--破坏式造孔与有机复合相结合,使最终产品可大量吸附污染水体中的各种污染物并具有一定的杀菌功能.该方法通过酸洗刻蚀,达到了去除原材料中的杂质和刻蚀孔径的目的,所制备的中间产品24h吸湿率为原材料的2倍,染料吸附量为原材料的1.6倍.
|
| 关 键 词： | 沸石 破坏式造孔 酸洗刻蚀 介孔复合环境材料 有机物 介孔复合环境材料 酸洗刻蚀 刻蚀工艺 Materials Environmental Composite Mesoporous Preparation Technique Etching 吸附量 染料 吸湿率 中间产品 孔径 杀菌功能 污染物 污染水体 结合 复合相 |
| 修稿时间： | 2003年11月11日 |
Acid Etching Technique for Preparation of Mesoporous Composite Environmental Materials |
| |
| LI Tianxin,LIN Hai,SUN Cunyi,XU Yuqing Civil and Environmental Engineering School,University of Science and Technology Beijing,Beijing ,China.Acid Etching Technique for Preparation of Mesoporous Composite Environmental Materials[J].Journal of University of Science and Technology Beijing,2004,26(3):237-239. |
| |
| Authors: | LI Tianxin LIN Hai SUN Cunyi XU Yuqing Civil and Environmental Engineering School University of Science and Technology Beijing Beijing China |
| |
| Institution: | LI Tianxin,LIN Hai,SUN Cunyi,XU Yuqing Civil and Environmental Engineering School,University of Science and Technology Beijing,Beijing 100083,China |
| |
| Abstract: | A method for preparation of mesoporous composite materials was investigated which is the combi-
nation of destructive pore-making technique and organic composite method. The final product made by the method
possesses excellent absorbent property for both small inorganic molecules and big organic molecules in polluted
water, and it is also a kind of bactericide. By the acid etching technique, many impurities in matrix materials were
removed and pore canals were etched. The moisture absorption rate of the semifinshed product for 24h is 2 times
as large as that of the raw material, and the adsorption amount for dye is 1.6 times. |
| |
| Keywords: | zeolite destructive pore-making technique acid etching technique mesoporous composite environmental material organic substance |