Effect of temperature and stress on high temperature creep behavior of Ni3Al-based single crystal superalloy |
| |
Institution: | 1. National Center for Materials Service Safety, University of Science and Technology Beijing, Beijing, 100083, China;2. Beijing Institute of Aeronautical Materials, Beijing, 100095, China;3. Research Institute of Aero-engine, Beihang University, Beijing, 100191, China |
| |
Abstract: | The creep behavior and dislocations mechanism of the Ni3Al-based single crystal alloy IC6SX with 001] orientation were investigated under the testing conditions of 1100 ?°C/137 ?MPa, 1100 ?°C/120 ?MPa and 1070 ?°C/137 ?MPa. It was observed that the temperature and stress had a significant effect on the high temperature creep life of the single crystal alloy. As the temperature was reduced from 1100 ?°C to 1070 ?°C, the creep life increased from 65.07 ?h to 313.8 ?h. As the stress was reduced to 120 ?MPa, the creep life increased to 243.3 ?h. Under the high temperature and low stress condition the dislocations entered the γ′ phase by climbing caused by the atomic diffusion, instead of slipping. |
| |
Keywords: | Single crystal superalloy Creep properties Microstructure Dislocations configuration |
本文献已被 ScienceDirect 等数据库收录! |
| 点击此处可从《自然科学进展(英文版)》浏览原始摘要信息 |
| 点击此处可从《自然科学进展(英文版)》下载免费的PDF全文 |
|