La2O3–Al2O3 –SiO2
glass-infiltrated 3Y-TZP all-ceramic composite for the dental restora tive application |
| |
作者姓名: | Shenyong Shi Qinghong Zhang Hongzhi Wang Yaogang Li |
| |
摘 要: | The 3 mol% yttria stabilized tetragonal zirconia polycrystals (3Y-TZP) powder had three particle size distributions, while the fine one was lower than 100 nm. The 3Y-TZP compact
was prepared by dry-pressing under pressures ranged from 10 to 30 MPa and then presintered at 1250°C for 2 h. The matrix dry-pressed under the pressure of 20 MPa had a porosity of 16.7% and could be easily processed by computer aided design and computer aided manufacturing (CAD/CAM), and which had been infiltrated by the La2O3–Al2O3–SiO2 glass at 1200°C for 4 h. The flexural strength and fracture toughness of the composite were 710.7 MPa and 6.51 MPa m1/2, respectively. The low shrinkage (0.3%) of the composite can satisfy the net-shape fabrication standard. XRD results illustrated that zirconia in the La2O3–Al2O3–SiO2 glass-infiltrated 3Y-TZP all-ceramic composite was mainly in the tetragonal phase. SEM and EDS results indicated that the pores of the matrix were almost filled by the La2O3–Al2O3 –SiO2 glass
|
收稿时间: | 19 November 2011 |
本文献已被 ScienceDirect 等数据库收录! |
| 点击此处可从《自然科学进展(英文版)》浏览原始摘要信息 |
| 点击此处可从《自然科学进展(英文版)》下载免费的PDF全文 |