| Y对Fe50- x Mo14Cr15C15B6Y x非晶合金 非晶形成能力及耐腐蚀性能的影响 |
| |
| 引用本文： | 周正,王鲁,王富耻,张海峰,程焕武,柳彦博,徐赛华.Y对Fe50- x Mo14Cr15C15B6Y x非晶合金 非晶形成能力及耐腐蚀性能的影响[J].北京理工大学学报,2008,28(5):455-458. |
| |
| 作者姓名： | 周正 王鲁 王富耻 张海峰 程焕武 柳彦博 徐赛华 |
| |
| 作者单位： | 1. 北京理工大学,材料科学与工程学院,北京,100081
2. 中国科学院,金属研究所,辽宁,沈阳,110015 |
| |
| 摘 要： | 采用单辊法制备Fe50-xMo14Cr15C15B6Yx(x=0,2)非晶合金条带,利用X射线衍射、差热分析、透射电镜和电化学极化曲线方法对非晶合金的结构、非晶形成能力(GFA)、热稳定性、晶化过程及腐蚀行为等进行了研究和表征.结果表明:Fe50-xMo14Cr15C15B6Yx合金能够形成非晶合金,随着Y元素的添加,其非晶相含量、非晶形成能力及热稳定性显著提高.晶化处理后,析出的主要晶体相为α-Fe,Fe23B6,Cr23C6和Fe3Mo3C等.Fe50-xMo14Cr15C15B6Yx非晶合金在质量分数为3.5%NaCl水溶液中呈现出极强的耐腐蚀能力,远优于常用耐蚀不锈钢Cr18Ni9Ti,并且随着Y元素的加入,非晶合金的耐腐蚀能力进一步提高,具有更宽的钝化区间及更低的腐蚀电流密度.
|
| 关 键 词： | Fe基非晶合金 非晶形成能力 热稳定性 耐腐蚀性 |
| 文章编号： | 1001-0645(2008)05-0455-04 |
| 收稿时间： | 2007/12/17 0:00:00 |
| 修稿时间： | 2007年12月17 |
Effects of Yttrium on the Glass-Forming Ability and Corrosion Resistance of Fe50- x Mo14Cr15C15B6Y x Amorphous Alloys |
| |
| ZHOU Zheng,WANG Lu,WANG Fu-chi,ZHANG Hai-feng,CHENG Huan-wu,LIU Yan-bo and XU Sai-hua.Effects of Yttrium on the Glass-Forming Ability and Corrosion Resistance of Fe50- x Mo14Cr15C15B6Y x Amorphous Alloys[J].Journal of Beijing Institute of Technology(Natural Science Edition),2008,28(5):455-458. |
| |
| Authors: | ZHOU Zheng WANG Lu WANG Fu-chi ZHANG Hai-feng CHENG Huan-wu LIU Yan-bo and XU Sai-hua |
| |
| Institution: | School of Materials Science and Engineering, Beijing Institute of Technology, Beijing 100081, China;School of Materials Science and Engineering, Beijing Institute of Technology, Beijing 100081, China;School of Materials Science and Engineering, Beijing Institute of Technology, Beijing 100081, China;Institute of Metal Research, The Chinese Academy of Science, Shenyang, Liaoning 110015, China;School of Materials Science and Engineering, Beijing Institute of Technology, Beijing 100081, China;School of Materials Science and Engineering, Beijing Institute of Technology, Beijing 100081, China;School of Materials Science and Engineering, Beijing Institute of Technology, Beijing 100081, China |
| |
| Abstract: | |
| |
| Keywords: | Fe-based amorphous alloy glassforming ability thermal stability corrosion resistance |