| 2 000 m3球罐焊缝裂纹分析及处理办法 |
| |
| 引用本文： | 岑树海.2 000 m3球罐焊缝裂纹分析及处理办法[J].广西大学学报(自然科学版),2004,29(3):187-189. |
| |
| 作者姓名： | 岑树海 |
| |
| 作者单位： | 广西锅炉压力容器检验所,广西,南宁,530022 |
| |
| 摘 要： | 对2000m^3。球罐开罐检验时发现15处裂纹．最长一条3100mm．通过分析．指出裂纹产生的原因．并介绍了对缺陷的处理办法．
|
| 关 键 词： | 球罐 裂纹 缺陷处理 |
| 文章编号： | 1001-7445(2004)03-0187-03 |
| 修稿时间： | 2004年4月20日 |
Analyses and cures of the cracks in the welds of 2000 m3 spherical tank |
| |
| CEN Shu-hai.Analyses and cures of the cracks in the welds of 2000 m3 spherical tank[J].Journal of Guangxi University(Natural Science Edition),2004,29(3):187-189. |
| |
| Authors: | CEN Shu-hai |
| |
| Abstract: | Fifteen cracks were found in 2 000 m~3 spherical tank during opening for examination. The length of the longest one is 3 100 mm.By defects being analyzed, the causes of the cracks producing were point out, and the methods for manage the defects were also given. |
| |
| Keywords: | Spherical tank Crack Manage defects |