Hot deformation behavior and the processing map of Zr–1.0Be alloy in single α phase |
| |
作者姓名: | Zhihao Feng Xiaojun Jiang Yunkai Zhou Chaoqun Xi Xinyu Zhang Mingzhen M Riping Liu |
| |
摘 要: | The hot deformation behavior,hot workability and dynamic recrystallization evolution of Zr-1.0(wt%) Be alloy in single a phase were investigated by conducting hot compression tests.The strain rates ranging from 10~(-3) s~(-1) to 10° s~(-1) and testing temperatures varying from 650 ℃to 850℃ were used.Flow stress was found to increase with increasing strain rate and decrease with the increment of the deformation temperature.A constitutive equation of flow behavior was established to describe the dependence of flow stress on strain rate and deformation temperature.The activation energy for deformation of Zr-1.0Be alloy was determined to be Q= 301 kJ/mol.The processing map of Zr-1.0Be alloy was constructed at strain rates ranging from 10~(-3) s~(-1) to 10° s~(-1) and deformation temperatures varying from 650 ℃ to 850 ℃ at the true strain of 0.7.A processing map was used to identify the best domains of thermal processing,including a domain at a temperature of 650 ℃ and strain rate of 10~(-3) s~(-1) as well as another domain at deformation temperatures ranging from 800 ℃ to 850 ℃ and strain rates varying from 10~(-3) s~-~(-1) to 10~(-1) s~(-1).Microscopic analysis of Zr-l.OBe alloy showed that the flow instability and kink were very obvious at low temperatures and high strain rates.At high temperatures and low strain rates,the dynamic recrystallization became the main softening mechanism during hot working.
|
本文献已被 CNKI 等数据库收录! |
| 点击此处可从《自然科学进展(英文版)》浏览原始摘要信息 |
| 点击此处可从《自然科学进展(英文版)》下载免费的PDF全文 |