Pyrolysis of Polytrimethylene Terephthalate （PTT） Fiber by Pyrolysis Gas Chromatography-Mass Spectroscopy

Pyrolysis of polytrimethylene terephthalate (PTT) fiber has been investigated by pyrolysis gas chromatography-mass spectroscopy in the temperature range from 400℃ to 750℃ in order to observe the possible effect of the temperature on its composition of pyrolysates. At 400℃, pyrolysis of molecular chain could occur, only 13 pyrolysates could be identified. The trimethylene moieties bound to the macromolecular core by ester bonds are cleaved at around 400℃. At 550℃ -750℃, pyrolysis of molecular chain could completely take place, 46 pyrolysates could be found. As the temperature increases, the compositions of pyrolysate are distinctly increased. Several compounds, especially benzoic acid, monopropenyl-p-phthalate, 2 - propenyl benzoate, di - 2 - propenyl ester, 1,4 -benzenedicarboxylic acid, benzene, 1, 5 - hexadiene, biphenyl and 1, 3 - propanediol dibenzoate could be formed. The thermal degradation mechanism, which is determined by structure and amount of the thermal decomposition products, are described. During pyrolysis of polytrimethylene terephthalate, polymeric chain scissions take place a peeling reaction as a successive removal of the dimer units from the polymeric chain. The chain scissions are followed by the elimination reaction, linkage action and secondary reactions, which bring about a variety fragment.

Pyrolysis of Polytrimethylene Terephthalate (PTT) Fiber by Pyrolysis Gas Chromatography-Mass Spectroscopy

Pyrolysis of polytrimethylene terephthalate (PTT) fiber has been investigated by pyrolysis gas chromatography-mass spectroscopy in the temperature range from 400℃ to 750℃ in order to observe the possible effect of the temperature on its composition of pyrolysates. At 400℃, pyrolysis of molecular chain could occur, only 13 pyrolysates could be identified. The trimethylene moieties bound to the macromolecular core by ester bonds are cleaved at around 400℃. At 550℃ -750℃, pyrolysis of molecular chain could completely take place, 46 pyrolysates could be found. As the temperature increases, the compositions of pyrolysate are distinctly increased. Several compounds, especially benzoic acid, monopropenyl-p-phthalate, 2 - propenyl benzoate, di - 2 - propenyl ester, 1,4 -benzenedicarboxylic acid, benzene, 1, 5 - hexadiene, biphenyl and 1, 3 - propanediol dibenzoate could be formed. The thermal degradation mechanism, which is determined by structure and amount of the thermal decomposition products, are described. During pyrolysis of polytrimethylene terephthalate, polymeric chain scissions take place a peeling reaction as a successive removal of the dimer units from the polymeric chain. The chain scissions are followed by the elimination reaction, linkage action and secondary reactions, which bring about a variety fragment.