| 微乳法制备纳米硅酸钙 |
| |
| 引用本文： | 胡长文,李会峰,任玲,孙灵娜.微乳法制备纳米硅酸钙[J].北京理工大学学报,2006,26(4):361-364. |
| |
| 作者姓名： | 胡长文 李会峰 任玲 孙灵娜 |
| |
| 作者单位： | 北京理工大学,理学院,北京,100081;北京理工大学,理学院,北京,100081;北京理工大学,理学院,北京,100081;北京理工大学,理学院,北京,100081 |
| |
| 基金项目： | 中国科学院资助项目
,
高等学校博士学科点专项科研项目 |
| |
| 摘 要： | 利用溶剂热的方法,在阳离子表面活性剂CTAB(十六烷基三甲基溴化胺)的存在下,制备出了不同形貌的硅酸钙纳米晶粒.通过改变水与表面活性剂的浓度的比值,发现对产物硅酸钙形貌的控制有着重要的影响,并对硅酸钙的生成机理做了初步的探讨,认为水与表面活性剂的浓度比值在反应物的浓度逐渐增大时,胶团的内部有更多的反应物聚集,使产物尺寸变大,促进了产物的晶化,易形成棒状的结构;反之,易得到球形的纳米晶.
|
| 关 键 词： | 微乳液 表面活性剂 硅酸钙 纳米结构 |
| 文章编号： | 1001-0645(2006)04-0361-04 |
| 收稿时间： | 09 6 2005 12:00AM |
| 修稿时间： | 2005年9月6日 |
Microemulsion-Mediated Synthesis of Calcium Silicate Nanostructures |
| |
| HU Chang-wen,LI Hui-feng,REN Ling and SUN Ling-na.Microemulsion-Mediated Synthesis of Calcium Silicate Nanostructures[J].Journal of Beijing Institute of Technology(Natural Science Edition),2006,26(4):361-364. |
| |
| Authors: | HU Chang-wen LI Hui-feng REN Ling and SUN Ling-na |
| |
| Institution: | School of Science, Beijing Institute of Technology, Beijing 100081, China |
| |
| Abstract: | Controlled synthesis of calcium silicate nanostructures with morphologies of spheres and whiskers were successfully achieved by cationic surfactant-CTAB-microemulsion-mediated solvothermal method.Various comparison experiments showed that the molar concentration ratio between water and CTAB and the concentration of reactants play important roles in the morphological control of calcium silicate nanostructures.A mechanism was proposed for the selective formation of various morphologies.A higher molar ratio and increased concentration of reactants favor more reactants aggregating in the water pool,leading to larger size of the products and accelerate the crystallizing process,resulting in whiskers in the nanostructures.On the contrary,a lower molar ratio favors spherical products. |
| |
| Keywords: | microemulsion surfactant calcium silicate nanostructures |