PbTe热电材料的合金化研究
引用本文:陶小马,秦鹏,王自茹,谭旺,王戎丞,欧阳义芳.PbTe热电材料的合金化研究[J].广西科学,2015,22(5):481-484.
作者姓名:陶小马  秦鹏  王自茹  谭旺  王戎丞  欧阳义芳
作者单位:广西大学物理科学与工程技术学院, 广西南宁 530004,广西大学物理科学与工程技术学院, 广西南宁 530004,广西大学物理科学与工程技术学院, 广西南宁 530004,广西大学物理科学与工程技术学院, 广西南宁 530004,广西大学物理科学与工程技术学院, 广西南宁 530004,广西大学物理科学与工程技术学院, 广西南宁 530004
基金项目:国家自然科学基金项目(11047031,51201039)和广西自然科学基金项目(2011GXNSFC018003)资助。
摘    要:目的]探索PbTe热电材料的合金化方法。方法]利用机械合金化方法和高频熔炼方法快速制备PbTe热电材料。首先,通过调整Pb和Te成分配比,球磨时间,制备出品质较好的PbTe热电材料;其次,利用高频熔炼的方法制备PbTe材料;最后对所制备的样品进行X射线衍射(XRD)和扫描电镜(SEM)测试和分析,比较两种方法制备样品的优缺点。结果]机械合金化制备的PbTe样品退火时,细化的晶粒开始回复和再结晶,结晶度明显增加,但是仍然低于高频熔炼的样品,且退火后,块状PbTe材料中存在大量的缺陷和晶格的畸变。结论]通过机械合金化制备的PbTe样品结晶度明显低于高频炉制备的样品。

关 键 词:PbTe热电材料  机械合金化  高频熔炼
收稿时间:2015/7/20 0:00:00

Alloying Investigation of PbTe Thermoelectric Materials
TAO Xiao-m,QIN Peng,WANG Zi-ru,TAN Wang,WANG Rong-cheng and OUYANG Yi-fang.Alloying Investigation of PbTe Thermoelectric Materials[J].Guangxi Sciences,2015,22(5):481-484.
Authors:TAO Xiao-m  QIN Peng  WANG Zi-ru  TAN Wang  WANG Rong-cheng and OUYANG Yi-fang
Institution:College of Physical Science and Technology, Guangxi University, Nanning, Guangxi, 530004, China,College of Physical Science and Technology, Guangxi University, Nanning, Guangxi, 530004, China,College of Physical Science and Technology, Guangxi University, Nanning, Guangxi, 530004, China,College of Physical Science and Technology, Guangxi University, Nanning, Guangxi, 530004, China,College of Physical Science and Technology, Guangxi University, Nanning, Guangxi, 530004, China and College of Physical Science and Technology, Guangxi University, Nanning, Guangxi, 530004, China
Abstract:Objective] Alloying methods were explored for PbTe thermoelectric materials.Methods] High energy mechanical ball milling method and high frequency melting method were used to prepare PbTe thermoelectric materials.Firstly, the fractions of the samples and the milling time were adjusted to obtain the high quality samples.Secondly, the high frequency melting method was used to prepare the PbTe samples.Finally, the X-ray diffraction (XRD) and scanning electron microscope (SEM) were employed to obtain the crystal information and micro-morphology.Results] The crystallinity of the PbTe prepared by mechanical alloying was obviously lower than that of high frequency melting.After annealing, the crystallinity of mechanical alloying was also lower than that of high frequency melting, but the crystallinity of mechanical alloying was increased during the annealing.The annealed bulk PbTe had lots of defects and lattice distortion.Conclusion] The crystallinity of the PbTe prepared by mechanical alloying was obviously lower than that of high frequency melting.
Keywords:PbTe thermoelectric materials  mechanical alloying  high frequency melting