| 盐酸溶液中有机磷缓蚀剂DPPM对Q235钢的缓蚀性能研究 | |
| 引用本文： | 谢斌,朱莎莎,李玉龙,邹立科,谢峰,陈能.盐酸溶液中有机磷缓蚀剂DPPM对Q235钢的缓蚀性能研究[J].四川理工学院学报(自然科学版),2013,26(2):28-31. |
| 作者姓名： | 谢斌 朱莎莎 李玉龙 邹立科 谢峰 陈能 |
| 作者单位： | 1. 四川理工学院功能材料研究所,四川自贡643000;材料腐蚀与防护四川省重点实验室,四川自贡643000 2. 四川理工学院功能材料研究所,四川自贡,643000 3. 内江师范学院化学化工学院,四川内江,641100 |
| 基金项目： | 材料腐蚀与防护四川省重点实验室基金项目，四川理工学院研究生创新基金项目，四川省应用基础研究项目 |
| 摘 要： | 合成了有机磷缓蚀剂1,1-双(二苯膦基)甲烷(DPPM),采用电化学极化曲线法研究了DP-PM在1.0 mol·L-1HCl溶液中对Q235钢的缓蚀作用,并考察了DPPM浓度、HCl浓度、试验温度和缓蚀液放置时间对DPPM缓蚀性能的影响。研究结果表明DPPM为混合型缓蚀剂,在30℃时,DPPM浓度为80 mg·L-1的1 mol·L-1HCl溶液中,缓蚀剂DPPM对Q235钢的缓蚀率达到了97.43%。DPPM的缓蚀率随腐蚀体系温度升高而降低,同样随体系酸度增大而降低,但随时间的延长,其缓蚀性变化不大。 |
| 关 键 词： | DPPM 缓蚀性 HCl溶液 Q235钢 |
Study on Inhibition of Organophosphorus Inhibitor DPPM for Q235 Steel in Hydrochloric Acid Solution |
|
| XIE Bin , ZHU Sha-sha , LI Yu-long , ZOU Li-ke , XIE Feng , CHEN Neng.Study on Inhibition of Organophosphorus Inhibitor DPPM for Q235 Steel in Hydrochloric Acid Solution[J].Journal of Sichuan University of Science & Engineering:Natural Science Editton,2013,26(2):28-31. | |
| Authors: | XIE Bin ZHU Sha-sha LI Yu-long ZOU Li-ke XIE Feng CHEN Neng |
| Institution: | 1(1.Institute of Functional Materials,Sichuan University of Science & Engineering,Zigong 643000,China;2.Material Corrosion and Protection Key Laboratory of Sichuan Province,Zigong 643000,China;3.School of Chemistry and Chemical Engineering,Neijiang Normal University,Neijiang 641100,China) |
| Abstract: | The organophosphorus inhibitor of compound,bis(diphenylphosphino)methane(DPPM),is synthesized,and its inhibition performance is studied by potentiodynamic polarization for Q235 steel in HCl solution.In addition,the influence factors of corrosion inhibition,which include the DPPM concentration,HCl concentration,system temperature,and immersion time of the inhibitor solution have been performed.The studies show that the DPPM is a mixed-type inhibitor and its inhibition efficiency for Q235 steel is up to 97.43 % in 1.0 mol·L-1 HCl solution with 80 mg·L-1 inhibitor DPPM at 30°C.The inhibition efficiency for Q235 steel decreases with the increasing of temperature,and decreases with the increasing of HCl concentration as well,but the inhibition efficiency has a little change with the increasing of immersion time. |
| Keywords: | DPPM corrosion inhibition HCl solution Q235 steel |