熔融还原型熔体对炉衬侵蚀的研究

研究了熔融还原熔体对耐火内衬的侵蚀速度，侵蚀程度和引起内衬的微观结构变化。结果表明，内衬侵蚀的主要因素是熔体与内衬中氧化物间的化学反应，侵蚀最严重的部位是渣铁界面处及渣表面处。铁氧化物浓度越高，侵蚀速度就越高，温度越高，内衬的侵蚀速度也越快。

Erosion of Smelting Reduction Melt on Refractory Lining

The melt of smelting reduction with iron bath Possessed high oxidizability andlow basicity. This paper studied the erosion rate and extent of molten slag and iron on different kindsrefractories and the micro-structure changing.It was shown that the main factor of corrosion liningwas the reaction between melt and oxide existing in lining.The serious zone was the interfacebetween slag and iron bath and slag surface. The greater the concentration of iron oxide,the higherthe erosion rate is.So is the temperature.