Nd掺杂ZnS催化剂的制备及其对有机染料的降解

用液相沉淀法制备不同比例Nd掺杂的ZnS纳米颗粒,用X射线衍射仪对制备的样品进行物相分析.以降解溴酚蓝为模型反应,通过吸收和光致发光光谱对其进行了发光性能的研究,讨论了影响溴酚蓝降解率的主要因素.结果表明,在100℃下老化1 h,制得的光催化剂具有较高的光催化活性,该复合光催化材料可用于有机染料废水的降解处理.     

Au/Cu_(1.94)S/ZnS纳米复合物的制备及其光催化性能研究

在油胺中合成Cu1.94S/ZnS,并将其分散到乙醇溶液中在磁力搅拌下与金纳米粒子复合,制备了Au/Cu1.94S/ZnS三元纳米复合物,利用X射线衍射仪(XRD)、透射电子显微镜(TEM)、紫外可见分光光度计(UV-Vis)等分析测试手段对所得产物进行表征,考察了在可见光下Au/Cu1.94S/ZnS纳米复合物对染料RhB的光催化降解性质.结果显示:Au/Cu1.94S/ZnS纳米复合物具有优异的光降解性能.     

粉末ZnS样品的高压原位阻抗谱研究

采用高压力下的原位阻抗谱测量技术,研究了晶界对粉末ZnS电阻的影响.数据分析结果显示:在11 GPa处,ZnS粉末的电阻主要是由于晶界引起的.对于岩盐相的ZnS,其残余电阻也是来自于晶界的影响.在14 GPa处,阻抗谱由双半弧变成一个椭圆型半弧对应于ZnS粉末的高压相转变.     

Eu3+掺杂ZnS纳米材料的制备及发光性能研究

低温水浴法制备不同掺杂浓度(摩尔百分比1％～7％)的ZnS:Eu纳米颗粒.采用X射线衍射仪对制备的样品进行物相分析,通过吸收和光致发光光谱对其进行了发光性能的研究.实验结果表明,所制备的样品均为立方相的ZnS:Eu,Eu3+占据了晶格的非对称反演中心,红光发射来源于Eu3+的5 D0→7 F2的跃迁.掺杂量为6％、热处...     

CdTe/ZnS 量子点荧光可逆调控研究ctDNA 与吡柔比星的相互作用

水相合成了谷胱甘肽修饰的CdTe/ZnS 量子点(GSH-CdTe/ZnS QDs). 从原子力显微镜照片可以看出, 合成的核壳型GSH-CdTe/ZnS QDs 具有良好的分散性. 当吡柔比星与GSH-CdTe/ZnS QDs 相互作用时, 吡柔比星吸附在GSH-CdTe/ZnS QDs 的表面, 通过光诱导电子转移的方式猝灭GSH-CdTe/ZnS QDs 的荧光. 然后向GSH-CdTe/ZnS QDs-吡柔比星体系中加入ctDNA, 吡柔比星从GSH-CdTe/ZnS QDs 表面脱落后嵌入ctDNA 双螺旋结构中, 光诱导电子转移过程被阻断, GSH-CdTe/ZnS QDs 的荧光恢复. 根据GSH-CdTe/ZnSQDs 荧光的猝灭和恢复, 实现了量子点荧光的可逆调控. 结合共振瑞利散射和紫外吸收光谱, 讨论了GSH-CdTe/ZnS QDs 吡柔比星-ctDNA 的相互作用机理, 建立了一种研究蒽醌类抗癌药物与核酸相互作用的光谱方法.     

溶剂热法制备ZnS纳米线束

采用单一前驱体溶剂热法,在聚乙烯吡咯烷酮(PVP)作表面活性剂条件下,成功合成了ZnS纳米线束.利用X射线衍射(XRD)、透射电子显微镜(TEM)、傅里叶红外变换吸收光谱及光致发光测试对样品的结构、形貌及物理性能进行了分析与表征.结果表明,所得产物为纯的六面体纤维锌矿ZnS纳米线束,直径在20~30 nm,长度为1.5~2.0μm,并对ZnS纳米线束的形成机理进行了探讨.     

ZnS/PVP纳米纤维的制备及性质研究

通过静电纺丝的方法成功制备了ZnS/PVP纳米纤维。通过扫描电子显微镜可知,纤维的直径大约在400 nm,纤维中的无机物为立方ZnS晶体,从荧光光谱图中可以知道,发射峰的位置在415nm。     

Fluorescent immunosensor based on fluorescence resonance energy transfer between CdSe/ZnS quantum dots and Au nanorods for PRRSV detection

An ultrasensitive and selective sandwich-type fluorescent immunosensor based on fluorescence resonance energy transfer (FRET) between CdSe/ZnS quantum dots (QDs) and Au nanorods (AuNRs) was developed for the rapid detection of porcine reproductive and respiratory syndrome virus (PRRSV). Modified CdSe/ZnS QDs and AuNRs were bioconjugated with primary antibodies M and GP5, respectively. When the target antigen was present, a well-known sandwich-type form CdSe/ZnS QDs-M antibody-antigen-GP5 antibody-AuNRs was produced, and thus reducing the distance between the QDs and NRs. As a result, FRET occurred and the fluorescence intensity of CdSe/ZnS QDs decreased, and this decrease was used to determine the antigen concentration. Ultrasensitive detection of PRRSV at low concentrations in swine serum was achieved with a limit of detection of 0.55 TCID₅₀/mL and a linear detection range of 10¹–3.5 ?× ?10⁴ TCID₅₀/mL. Therefore, the fluorescent immunosensor is selective and highly sensitive; specifically, it can detect PRRSV at low concentrations in swine serum over a large concentration range. This proposed detection method can facilitate the development of high-performance fluorescent immunosensors for the detection of PRRSV and other antigens.     

添加锌电解阳极泥对ZnS浸出过程的影响

在锌焙烧烟尘热酸浸出过程中,来自于铁酸锌溶解的三价铁离子被用作焙烧烟尘中ZnS浸出的氧化剂.为了提高锌的浸出率,研究了在浸出过程中加入锌电解阳极泥对ZnS浸出的影响.考察的浸出条件包括阳极泥加入量、温度、硫酸浓度和反应时间.试验结果表明,阳极泥中的MnO2有助于焙烧烟尘中ZnS的氧化浸出.在最佳的条件下,通过加入阳极泥(锰加入量为焙烧烟尘质量的4%)可将锌的浸出率由94%提高到97%以上.     

厚度对ZnS薄膜结构和应力的影响

用射频磁控溅射法在单晶Si基片上制备了4种不同厚度的ZnS膜,采用XRD和光学干涉相移法对薄膜的微结构和应力进行研究。结构分析表明,不同厚度的ZnS膜均呈多晶状态,并有明显的(220)晶面择优取向,晶体结构为立方晶型(闪锌矿)结构;随着薄膜厚度的增加,平均晶粒尺寸随之增大;薄膜的晶格常数在不同厚度下均比标准值稍大。应力分析表明,随着膜厚的增加,ZnS膜的应力差减小,在厚度为768 nm时的选区范围内应力差最小,应力分布较均匀。