脉冲等离子渗氮预处理后对AISI304奥氏体不锈钢疲劳行为的综合分析

This study aims to draw an exact boundary for microstructural and mechanical behaviors in terms of pulsed plasma nitriding conditions. The pulsed plasma nitriding treatment was applied to AISI 304 austenitic stainless steel at different temperatures and durations. Results reveal that nitriding depth increased as process temperature and duration increase. The nitriding depth remarkably increased at 475°C for 8 h and at 550°C for 4 h. An austenite structure was transformed into a metastable nitrogen-oversaturated body-centered tetragonal expanded austenite (S-phase) during low-temperature plasma nitriding. The S-phase was converted to CrN precipitation at 475°C for 8 h and at 550°C for 4 h. Surface hardness and fatigue limit increased through plasma nitriding regardless of process conditions. The best surface hardness and fatigue limit were obtained at 550°C for 4 h because of the occurrence of CrN precipitation.     

Mechanical and thermal properties of AA7075/TiO2/Fly ash hybrid composites obtained by hot forging

In the present paper, multiple reinforcements TiO2 and fly ash were utilized for the fabrication of AA7075 matrix based hybrid composites using stir casting technique followed by hot forging. In hybrid composites, the fly ash content was fixed to 3 wt% while that of TiO2 was varied from 2.5 to 10 wt%. Scanning electron microscopy images revealed homogenous dispersion of both the reinforcements in AA7075 matrix.Compression test was conducted to study the mechanical behaviour of hybrid composites. The hybrid composites showed increase in compressive strength with the incorporation of multiple reinforcements and further increased with the increase in the weight fractions of TiO2 particles. The coefficient of thermal expansion was measured between 50 and 250 ℃ with a high precision thermal mechanical analyser. The thermal coefficient of hybrid composites decreased with the addition of TiO2 and fly ash. However a slight decrease in thermal conductivity of hybrid composites was observed when compared to that of AA7075 alloy.