硅油基纳米Fe_3O_4-Co复合磁流体的制备及性能

针对传统Fe3O4磁流体比饱和磁化强度低、传热性差的缺点,以采用自制直流电弧等离子蒸发设备制备的纳米钴粉为磁性颗粒,添加到硅油基Fe3O4磁流体中,研究钴粉的添加量对磁流体比饱和磁化强度、密度、黏度及摩擦学性能的影响。研究结果表明:纳米Co/Fe3O4质量比从1/3增大到6/3时,复合磁流体的密度和黏度均有一定程度提高,且纳米钴粉的加入能明显提高复合磁流体的比饱和磁化强度,当纳米钴粉的加入量达到Fe3O4的2倍时,其比饱和磁化强度由0.43 A·m2/kg增大到2.91 A·m2/kg。同时,从摩擦因数和磨斑直径的角度分析,制备的新型复合磁流体能明显改善基础油载液的摩擦学性能。此外,新型复合磁流体能显著改善机械密封件的密封性能,且具有一定的修复作用。     

Effect of Ni addition on the glass-forming ability and soft-magnetic properties of FeNiBPNb metallic glasses

The effect of Ni addition on the glass-forming ability (GFA) and soft-magnetic properties of an (Fe1-xNix)75.5B14.5P7Nb3 (x=0-0.6) alloy system were investigated. We found that the addition of Ni was effective in allowing the alloy to approach a eutectic point as well as increasing the thermal stability of the supercooled liquid. By increasing the amount of Ni,the supercooled liquid region (ΔTx),the reduced glass transition temperature Trg (Tg/Tl) and the Y parameter [Tx/(Tg+Tl)] increased from 49 to 75 K,0...     

非平衡等离子体表面改性二茂铁磁性高分子的电磁性能研究

二茂铁磁性高分子(OPM,主要成分:Cr配位1,1'-二甲酰二茂铁1,8-萘二胺缩聚物)作为一类新型的功能高分子,表现出许多独特的电磁特性,但在某些苛刻条件下仍难以获得很好的应用.利用非平衡等离子体超常的化学行为,以低温空气等离子体对OPM进行表面修饰;红外数据显示经过改性后的OPM结构发生了变化,其高分子链上引入了—COOH、—OH、—NH2等基团,而这些极性基团的引入又导致其介电常数值也增大;同时,这些极性基团还能引起表面Fe离子环境的晶体电场变化,进而对其磁参数产生了影响,改性后的OPM饱和磁化强度有所降低,而其剩磁及矫顽力却又一定程度的增加.可见,经过非平衡等离子体改性后的OPM其电磁参数可进一步调整,可在某些特定的场合获得应用.     

铝合金表面Ni-Cu-P化学镀层的性能研究

试验分析了铜离子浓度c(Cu2+)对沉积速度、镀液稳定性以及镀层结构与性能的影响.用SEM、XRD、VSM表征镀层的表面形貌、组织结构及磁性能.Ni-Cu-P镀层的结晶性随c(Cu2+)增加而提高,并出现明显的衍射峰位角移现象.反应激活能随pH值增加而减小,随c(Cu2+)增加而增加.500℃保温2 h,Ni-Cu-P合金发生晶化转变,出现Ni3P、Cu3P结晶相.Cu元素的加入,使得Ni-Cu-P镀层具有高的热稳定性以及低的残磁性.     

Synthesis, characterization and magnetic properties of near monodisperse Fe3O4 sub-microspheres

Near monodisperse Fe3O4 sub-microspheres with an average diameter of 170 nm have been synthesized by a solvothermal reduction method, using K3[Fe（CN）6] as the raw material in the absence of any surfactants at 200~C℃ for 24 h. The products were detected by XRD, FESEM, TEM, and XPS. The investigation of the reaction parameters indicates that ethylene glycol plays a key role both as reducing agent and solvent. In addition, the reaction time and temperature also have important influences on the final product. The hysteresis loop of the near monodisperse Fe3O4 sub-microspheres shows a ferromagnetic behavior with saturation magnetization of 60.8 emu/g and coercivity of 124.7Oe.     

Ni-Zn铁氧体的制备及电磁性能

对化学共沉淀法制备的NixZn1-xFe2O4（x=0.1～0.9,（△x=0.2）铁氧体,用X-射线衍射分析仪（XRD）、透射电子显微镜（TEM）、扫描电子显微镜（SEM）、热重分析仪、四探针测试仪、振动样品磁强计（VSM）及阻抗/材料分析仪等分别测试了样品的结构、形貌和电磁性能。结果表明,样品的饱和磁化强度（Ms）和磁损耗（Tanδm）随Ni含量的增加呈现先增大后减小,最大值分别为23.74（x=0.7）和170emu/g（x=0.5）。     

掺杂EuSr_2Ru_(1-x)Nb_xCu_2O_8体系的磁性和超导电性

通过对EuSr2 Ru1-xNbxCu2 O8体系的结构、磁化强度和电阻进行观测 ,结果发现 :EuSr2 RuCu2 O8样品呈现超导电性和铁磁性共存 .其超导临界温度为Tconset≈ 35K ,Tc(ρ =0 ) =10K ,铁磁相变温度为TM=130 .2K ;Nb部分替代Ru同时导致铁磁相变温度和超导临界温度的下降 ,前者进一步说明了EuSr2 RuCu2 O8体系中磁有序仅来源于Ru的磁矩 ,而超导临界温度的下降则是由于CuO2 平面载流子浓度下降所致 .     

对向靶溅射α″-Fe_(16)N_2薄膜结构及其热稳定性

用对向靶反应溅射法制备了α″- Fe1 6 N2 薄膜 ,用 X射线衍射 (XRD)、透射电子显微镜(TEM)和振动样品磁强计 (VSM)对α″- Fe1 6 N2 的结构、磁性以及结构的热稳定性进行了分析讨论 .结果表明 ,随退火温度的升高 ,α″- Fe1 6 N2 相逐渐分解为 α″- Fe和 γ′- Fe4N两相 .对磁性的分析表明 ,造成饱和磁化强度存在较大差异的原因与其内在的结构差别有很大的关系 .     

αFe磁化特征的唯象分析

利用铁磁性分子场理论的基础上,通过引入热无序能、冷无序能、与自发磁化相关的有序能之间的竞争机制下,引入了有效分子场系数.利用考虑与温度相关的有效分子场系数λ(T)的分子场理论研究了αFe的磁化特征,得到了与实验相符的结论,解释了铁磁性物质的约化自发磁化强度与温度的关系,解释了C/χ-T曲线在磁相变温度附近向上弯曲的原因,解释了顺磁居里温度θP大于铁磁居里温度TC的实验结果,解释了铁磁性物质中的有序-无序竞争与宏观磁性的关系.