研究了稀土、过渡元素复合氧化物加少量贵金属汽车尾气三效催化剂的性能 ,包括蜂窝状第一载体粉碎后制备样品的性能、整块蜂窝状催化剂经粉碎后实验室测定的三效活性与组装成反应器安装在长安奥拓车上的净化性能     

Study on Semi-solid Rheocasting Forming for Magnesium Alloy by Mechanical Stirring

In this paper the effect of pouring temperature of magnesium melt, preheating temperature of the barrel of screw mixer and shear rate on the solidified microstructures of semi-solid slurry was investigated by mechanical stirring method. The appropriate processing parameters of slurry preparation were obtained. The mold filling for thin walled casting was examined. Results indicated that the solid volume fraction of non-dendritic structure increased with decrease in pouring temperature of magnesium melt and ...     

金属氧化物对聚氯乙烯热降解性能的影响

研究了二氧化锰(MnO2)和氧化铁(Fe2O3)对聚氯乙烯(PVC)热降解和热氧化降解过程的影响。电导率测试得出：PVC在空气和氮气环境下热降解时，都表现出自诱导脱氯化氢反应特征，而MnO2一定程度上消除了PVC热降解时自加速反应特征，Fe2O3实质性地改变了氯化氢释放规律，随时间的推移，使氯化氢释放量缓慢线性增加。热失重法与差热分析量热法显示MnO2和Fe2O3均阻止了氯化氢挥发释放过程，且加速了PVC主链断裂与挥发过程。     

红土镍矿HCl浸出液中Mg的回收和浸出剂再生

简述了近年来红土镍矿HCl浸出液中Mg的回收及浸出剂再生工艺的研究现状,介绍了对浸出液采用MgCl₂溶液的水解、硫酸盐水合物的结晶、碱式MgCl₂的沉淀、纳米级Mg（OH）₂的制备以及MgCl₂溶液的雾化干燥与焙烧等处理方法和应用进展.     

过渡金属氧化物改性KNN基无铅压电陶瓷研究进展

过渡金属氧化物不仅可用作助熔剂,改善陶瓷的烧结特性,同时也可作为掺杂物在陶瓷材料中进行离子取代,改善陶瓷的性能.本文详细叙述了过渡金属氧化物对KNN基无铅压电陶瓷烧结特性、微观结构、介电性能、压电性能、铁电性能的影响.分析总结过渡金属氧化物在改善KNN基无铅压电陶性能方面所起的主要作用,为今后助熔剂改性KNN基无铅压电陶瓷的研究提供参考.     

Mg-Zr处理对FH40级船板钢铸态夹杂物特征的影响

采用定量金相及SEM-EDS手段对Mg,Zr及Mg-Zr处理FH40级船板铸钢中夹杂物粒径分布、平均粒径、总数量、总面积及成分、形貌等特征进行系统研究.结果表明,Mg,Zr及Mg-Zr处理后铸锭夹杂物平均粒径下降,夹杂物总数量增加.Mg的质量分数为0024%时,夹杂物中MgO平均质量分数为1257%,变质不充分;Mg的质量分数增加至0072%后,夹杂物中MgO平均质量分数为3558%,实现了氧化铝向MgO·Al2O3的充分变质,且夹杂物粒径明显减小.003%Zr处理后,铸锭夹杂物以Al2O3+MnS,Al-Zr-O+MnS为主;低Mg+高Zr,高Mg+低Zr,高Mg+高Zr处理炉次试验钢铸锭中均发现了含Zr夹杂物,其中高Mg+高Zr炉次形成了ZrO2夹杂,该类夹杂物被MgO·Al2O3包裹,团聚现象明显.     

聚苯胺/氧化石墨烯导电复合材料的制备

通过原位聚合非二次掺杂制备了高导电性聚苯胺/氧化石墨烯复合材料.采用盐酸为掺杂酸,研究了聚苯胺/氧化石墨烯的微观形貌;探讨了盐酸浓度及氧化石墨烯（GO）用量对反应过程和复合材料导电性的影响.结果表明：聚苯胺（PANI）以球状物的形式均匀地包覆在GO表面;盐酸浓度超过0.5 mol·L-1,反应诱导期明显缩短,复合材料的导电性显著提高.在聚合体系中加入GO可延长聚合反应诱导期,但随着GO用量的增加反应诱导期缩短.当盐酸浓度为0.5 mol·L-1,GO与苯胺单体质量比超过2％时,制备的PANI/GO复合材料中GO形成导电通路,电导率较纯PANI提高一个数量级,达到1.4S·cm-1.     

高压固溶处理对AZ91D铸造镁合金组织的影响

采用高压设备对AZ91D铸造镁合金进行高压固溶处理,研究高压固溶处理对AZ91D铸造镁合金组织的影响。研究结果表明,高压固溶处理可显著细化AZ91D铸造镁合金的晶粒,平均晶粒尺寸为58μm。同时,在晶粒内部,可见互相平行或交叉的孪晶,孪晶的厚度为1~5μm。高压固溶处理后的组织仍由α-Mg和β-Mg17Al12相组成,但是β-Mg17Al12相主要是以颗粒状分布于晶界。     

The enhanced corrosion resistance of UMAO coatings on Mg by silane treatment

The surface silanization was carried out on ultrasonic micro-arc oxidation(UMAO) coatings on pure magnesium using KH550 as silane coupling agent(SCA). The surface morphology, chemical bonds and corrosion resistance of the silane films were investigated by scanning electron microscope(SEM), Fourier transform infrared spectroscopy(FTIR) and electrochemical workstation, respectively. The results showed that hybrid coatings were successfully prepared on pure magnesium by UMAO-Na OH(1 mol/L, 2 mol/L, 3 mol/L)-SCA processing. The organic films with Si–O–Mg bonds are helpful for the reduction of the pores in UMAO coatings. The pores decreased with increasing Na OH concentration. Compared with single UMAO treatment, the corrosion potentials(Ecorr) of magnesium plates with UMAO-Na OH(1 mol/L,2 mol/L, 3 mol/L)-SCA treatment increased by 29 m V, 53 m V and 75 m V, respectively, meanwhile the corrosion current density(Icorr) reduced one to two orders of magnitude. It indicated that the corrosion resistance of the coatings was improved by silane treatment.     

铸态镁合金大压下轧制对组织和边裂的影响

主要研究了道次压下率和轧制道次数对AZ31B扁锭坯大压下轧制所制备板材边裂以及微观组织的影响.轧制工艺为350℃下两道次或四道次大压下轧制.金相观察、边裂统计和XRD织构分析表明:当总压下率达到37%时,轧板开始出现边裂;并且裂纹深度随着压下率的增大而增加.随着压下率的增加,孪晶明显增多.当总压下率达到54%时,大部分区域已完成再结晶;进一步增大压下率,组织中出现变形局域化现象;当总压下率为82%,轧制道次增多时,边裂出现一定程度减弱,同时基面织构分布由双峰变为单峰.