管节点疲劳裂纹扩展规律和寿命估算

对Ｔ型管节点的疲劳试验进行分析，研究疲劳裂纹的扩展规律，用“柔度法”计算应力强度因子范围ΔＫ，确定材料常数ｃ，ｍ，提出并运用“直线－曲线模式法”估算管节点疲劳寿命，结果与试验吻合，具有一定的实用参考价值。     

Joint Strength with Soldering of Al2O3 Ceramics After Ni-P Chemical Plating

Ni-P alloy was chemically plated on Al2O3 ceramics to produce uniform alloy coatings at temperatures below 70~C. Cu metal was electroplated onto the Ni-P coating to facilitate the soldering and shorten the chemical plating time. Then, the electroplated ceramic specimens were soldered with 60 wt.% Sn-40 wt.% Pb solder in active colophony. The highest shear strength was acquired after the heat treatment at 170℃ for 15 min. The joint fractures mostly propagated along the interface between the ceramics and the Ni-P coating, with some fracture in both the ceramics and the Ni-P coating near the interface and some along the interface between the Cu and Ni-P coatings. The results show that ceramic surface roughness and the chemical plating parameters influence the coating quality, and that suitable heat treatment before the soldering also improves the adhesion between the ceramics and Ni-P coatings, thus strengthening the joints.     

桥头跳车的成因及处理方法

桥头跳车会增加行车风险并且会大大增加每年的养护费用．本文作者根据多年的养护管理及施工经验，对桥头跳车的成因从设计、施工及运营使用几方面进行了分析并提出了几种处理方法，尤其是对桥头搭板和土工格栅网两种目前工程界常用方法从设计机理到施工实践进行了比较详细的论述，同时对设计机理方面引入了相应的数学模型．     

Microstructure transition of Al-Cu eutectic alloy during containerless rapid solidification

Droplets of Al-32.7%Cu eutectic alloy were rapidly solidified during containerless processing in a 3 m drop tube. The microstructural evolution of Al-Cu eutectic alloy depends strongly on droplet size. The eutectic growth morphology changes from regular lamellar eutectic to a kind of anomalous eutectic with the decrease in droplet size. This microstructural transition was analyzed within the current theories of eutectic growth. The results indicate that there exists a critical velocity for eutectic growth beyond which anomalous eutectic appears. The coupled zone of the Al-Cu eutectic alloy system has been calculated on the basis of the Trivedi-Magnin-Kurz(TMK) eutectic growth and the Lipton-Kurz-Trivedi(LKT)/Boettinger-Coriell-Trivedi(BCT) dendrite growth models, which provides a further interpretation for the morphological transition.     

钙和钡对钢脱氧及夹杂变性的理论分析

在比较了各种常用脱氧剂单质脱氧能力的基础上，对钙合金、钡合金夹杂的变性能力进行了理论分析和探讨，并对钡合金的脱氧和夹杂物变性工艺提出了建议。     

电磁相分离法制备自生表层复合材料

采用电磁相分离法制备出以初生富铁相（AlSiFeMn复杂金属间化合物）为增强相，表层硬度为HB62．25，基体硬度为HB59．00的Al-11.70%Si-1.20?-1.50%Mn合金自生表层复合材料，增强相的显微硬度为HV 842。87，大小为20－80μm，该表层复合材料同基体材料相比，耐磨性提高了57．41％，所用方法工艺过程简单，成本低，为解决材料在服役环境中不同部位，不同性能的问题提供了新途径。     

家兔髋关节软骨扫描电镜观察

应用扫描电镜对家兔髋关节软骨观察发现:月状面软骨表面和股骨头软骨表面均具由纤维编织而成的网状层,月状面软骨顶部,纤维交错,网状层形态结构复杂而又丰厚;前部与后部次之,股骨头顶部,关节软骨表面的网状层显著低矮、致密,并有一矩形凹陷;下部,网状层呈斑块状,高低错落。     

铜基合金中马氏体穿晶行为的研究

在形状记忆合金中,存在马氏体穿晶生长现象,它是热弹马氏体相变在小角晶界的行为。     

Experimental Study on the Milling of a Ti Beta 21S

Ti Beta 21S (Ti-15Mo-2.7Nb-3Al-0.2Si) was devel op ed by TIMET in 1989. It is a metastable beta titanium alloy that offers subs tantial weight reductions over other engineering materials. Compared with common beta Ti alloys, it offers the high specific strength, good cold formability, im proved oxidation resistance, elevated temperature strength, creep resistance, an d thermal stability. Besides the common characters of titanium alloy, such as po or heat diffusivity, low elastic modulus, Ti Beta 21S has ...     

热力学分析在连续镀锌过程中的应用

热力学分析结合相图研究可用于解决生产实际问题。在连续镀锌过程中，锌液中铝是一种很重要的添加元素。它对镀锌质量有直接的影响。但锌池中铝含量的测量与控制还存在困难。在对Fe-Zn-Al三元体系Fe溶解度曲线的热力学分析的基础上，用Matlab编制了事家图形用户界面的程序，把热力学分析应用于计算锌池中的有效铝含量，将有助于热镀锌工业实现对铝含量的控制。