Ti – Cu– Zr–Fe– Nb ultrafine structur e-dendrite composites with good mechanical properties and biocompat ibility

Ti-Cu-Zr-Fe-Nb ultrafine structure-dendrite composites were designed by inducing Nb and more Ti to a Ti-Cu-Zr-Fe glass-forming alloy composition and prepared by copper mold casting.The composite alloys consist of β-Ti dendrites and ultrafine-structured CuTi₂ and CuTi phases as well as a trace amount of glassy phase.The volume fraction of β-Ti dendrites increases with the increase in content of Nb which acted as the β-Ti phase stabilizer in the alloys.The composites exhibit high compressive yield strength exceeding1200 MPa,maximum strength around 1800 MPa and low Young’s modulus around 48 GPa.The plasticity of the alloys is strongly influenced by the volume fraction and morphology of the dendritic β-Ti phase,and the compressive plastic strain was enlarged from 5.9%for the 4 at%Nb alloy to 9.2%for the 8 at%Nb alloy.The preliminary cell culture experiment indicated good biocompatibility of the composite alloys free from highly toxic elements Ni and Be.These Ti-based composite alloys are promising to have potential structural and biomedical applications due to the combination of good mechanical properties and biocompatibility.     

二氧化硅／银复合材料研究

载银复合颗粒作为一种重要的功能材料具有广泛的应用前景。本文以二氧化硅颗粒为载体,利用超声波化学镀银方法,制备出银／二氧化硅复合颗粒,并对产品进行了银含量分析和XRD、SEM表征,重点研究了复合颗粒的抗菌性能。通过实验知道载银二氧化硅复合材料对大肠杆菌的最小抑菌浓度分别为0.2g／L－0.3g／L,从实验数据看出,银含量低的对抗菌性能有更好的效果。     

复方丹参滴丸对慢性充血性心力衰竭心室重构的抑制作用

目的 观察复方丹参滴丸对慢性充血性心力衰竭（CHF）患者心室重构的抑制作用。方法 CHF患者68例,随机分为对照组和治疗组。对照组3-4例,常规使用血管紧张素转换酶抑制剂、口受体阻滞剂、利尿剂和地高辛治疗;治疗组3-4例,在对照组基础上加用复方丹参滴丸,每次10丸,每日3次,疗程18月。治疗前、后进行超声心动图检查,测量并计算左室舒张末期内径（LVEDd）、左室收缩末期内径（LVEDs）、室间隔厚度（IVSd）、左室后壁厚度（LVPWd）、左室射血分数（LVEF）、左室心肌质量（LVW）、左室心肌质量指数（LVMI）。比较组内治疗前后上述超声心动图指标的变化和组间差异。结果 治疗组和对照组治疗18月后,两组LVEDd、LVEDs、IVSd、LVPWd、LVM、LVMI、LVEF均有明显改善,治疗前后差异有统计学意义（P〈0．05）。治疗组和对照组比较,治疗后,治疗组的IVSd、LVPWd、LVM、LVMI较对照组改善更明显,两组间差异有统计学意义（P〈0．05）。结论 在常规药物治疗的基础上加用复方丹参滴丸,能进一步改善CHF的心室重构。     

一组常温纤维素分解菌稳定复合系的创建及其功能

从自然降解、腐烂的天然纤维素材料中分离、筛选获得生长速度快、透明圈较大、性状稳定的纤维素单菌23株。经纤维素分解力测定、回筛,获得一组由14株高效稳定纤维素分解菌组成的常温纤维素分解菌稳定复合系。该复合系常温下96 h内对麦秆粉的总分解力高达40.7%。     

In-situ reduced graphene oxide-polyvinyl alcohol composite coatings as protective layers on magnesium substrates

A simple and feasible method was developed to fabricate in-situ reduced graphene oxide-polyvinyl alcohol composite(GO-PVA) coatings as protective layers on magnesium substrates.Polyvinyl alcohol was used as an in-situ reductant to transform GO into reduced GO.Contiguous and uniform GO-PVA coatings were prepared on magnesium substrates by dip-coating method,and were further thermally treated at 120 ℃ under ambient condition to obtain in-situ reduced GO-PVA coatings.Owing to the reducing effect of PVA.thermal treatment at low temperature led to effective in-situ reduction of GO as confirmed by XRD,Raman,FTIR and XPS tests.The corrosion current density of magnesium substrates in 3.5 wt%NaCl solution could be lowered to its 1/25 when using in-situ reduced GO-PVA coatings as protective layers.     

聚乙烯醇对型煤热解的影响研究

以聚乙烯醇(PVA)为粘结剂与粉煤混合制成型煤,在热重分析仪上进行热解.实验数据表明:随着PVA含量的增加,反应活性指数R增大,反应速率加快,且低位发热量增大.通过FTIR光谱、BET、工业分析等方法分析说明,PVA的加入,增加了型煤的微孔结构,提高了燃料层间的传热和传质;型煤中羟基含量增多,促进了热解过程中苯酚的生成,使气态产物CO含量增多.     

Nomex蜂窝夹芯板冲击损伤试验研究

针对某型飞机上应用的Nomex蜂窝夹芯板,通过冲击损伤试验,研究了蜂窝夹芯板厚度对其抗冲击损伤能力的影响、试件损伤面积与冲击能量之间的关系以及穿透损伤对夹芯板轴压承载性能的影响。结果表明:20 mm与8 mm厚度板在分别承受40 J与25 J冲击能量时出现穿透损伤,厚板比薄板具有更高的抗冲击损伤能力;相同冲击能量时,20 mm厚板损伤面积比8 mm板的小;随冲击能量的增大,两种板的损伤面积逐渐增大;当冲击能量超过一定值时,8 mm板损伤面积增速明显加快;20 mm蜂窝夹芯板冲击后的剩余强度为完好件的56.7%,8 mm蜂窝夹芯板冲击后的剩余强度为完好件的67.5%。     

复合材料薄层板常温固化收缩及翘曲变形

研究了常温下树脂基复合材料层合板固化时的收缩以及翘曲变形,结果表明：薄层板各层不同的树脂含量是翘曲变形的主要因素;对称的铺层结构能有效的降低复合材料薄层板收缩与变形。采用有限元加以分析,有限元计算结果与实验结果相近,可以利用有限元的分析计算近似地预估变形。     

振冲碎石桩在粘陛土地层中的施工尝试

振冲碎石桩在加固粗颗柱、无粘性土地层,提高地基承载力方面已得到了广泛的应用,但在利用振冲碎石桩处理回填土中粘性软弱土层方面的应用还存在一定的施工难点。本文结合工程实践的效果,详细地介绍了如何避免粘性软弱土层对振冲碎石桩施工带来的不良影响所采取的一系列工程措施,为粘性软弱土层的工程处理提供了可借鉴的经验。     

混杂纤维混凝土应用在组合梁中的物理特性及对比实验研究

为了进一步明确混杂纤维混凝土物理特性优势,首先对其组合结构中应用与承载力进行了计算分析,接着对受弯承载力的计算完成了修正提议,在混杂纤维混凝土梁承载力的计算中,建立了纤维布直线关系的材料力学模型,得出高性能纤维补强混凝土板不仅可以增强复合梁的承载力,且有利于减缓裂缝和提高组合梁的延性,在对混杂纤维混凝土的极限应变分析中得出其应变能达到1 500以上,可以有效提高组合梁的截面延性,综合分析可得纤维混凝土同普通混凝土相比其抗折强度明显提高40%左右,抗冲击韧性明显提高50%左右,韧性得到了大幅度的提高。通过与多种其他混凝土的实验特性比较,充分验证了上述特性优势。这一研究对纤维混凝土的推广应用具有显著的实际价值。