High-pressure polymorph of TiO2-II from the Xiuyan crater of China

Abundant TiO2-II, a high-pressure polymorph of titanium dioxide, was found in the gneiss fragments of impact-produced breccias from the Xiuyan crater. Rutile in the gneiss was severely fragmented and fine-grained clasts less than 2 ~tm in size had been transformed to TiO2-II. Irregular thin layered TiO2-II is also observed in coarse-grained ruffle fragments, where the TiO2-II layers distributes along fractures and cracks in rutile, About 30 percent of rutile in the gneiss had been transformed to TiO2-II. Fine grains of TiO2-II display light bluish grey to light yellow brown in plane-polarized reflected light. Crystallographic investigation shows that TiO2-II has an orthorhombic structure with space group Pbcn. The cell parameters are a=4.543（1）/~, b=5.491（9）/~ and c=4.895（2） ,~. Its empirical formula calculated on the basis of two oxygen atoms can be written as （Tio.985Feo.oosNbo.oor- Si0.003Zr0.0Ol）l.0O302, or simply formula TiO2. According to the shock effects of quartz and feldspars, the peak shock pressure and post-shock temperature in the TiO2-II-bearing gneiss are estimated to be between 35 and 43 GPa and 300-900~C, respectively. The finding of TiO2-II in the shock-metamorphosed gneiss provides another mineral physics evidence for shock origin of the Xiuyan crater.     

Carbothermal reduction process of the Fe-Cr-O system

Understanding the reduction behaviors and characteristics of the end products of Fe-Cr-O systems is very important not only for maximizing the recovery of metals from stainless steel dust but also for the subsequent reuse in metallurgical process. The present work first predicted the possible products thermodynamically when FeCr₂O₄ was reduced by C. The reduction behaviors by graphite of three kinds of Fe-Cr-O systems, i.e., FeCr₂O₄, Fe₂O₃+Cr₂O₃, and Fe+Cr₂O₃, were then investigated in 1350–1550℃. Further, the microstructures of final products and element distribution conditions were examined. The results suggest that, thermodynamically, the mass of products for the carbothermal reduction of FeCr₂O₄ is a strong function of temperature, and the initial carbon content is used. More Fe-Cr-C solution and less residual carbon content are obtained at higher temperatures and lower n_C:n_O ratios (the initial molar ratio of C to O in the sample). Experimental data show that the sample amount tends to affect the reduction rate, and the residual carbon content strongly depends on n_C:n_O. With regard to the phases present in products during the reaction process, metal carbides tend to form in the initial stage, whereas Fe-Cr-C solution forms when the degree of reduction is sufficiently high.     

Chenguodaite （Ag9FeTe2S4）： a new tellurosulfide mineral from the gold district of East Shandong Peninsula,China

Chenguodaite, approved by IMA-CNMMN （2004-042a）, was discovered in the Bunan quartz vein-type gold deposit in the gold district of East Shandong Peninsula. The mineral occurs in high grade Au-Ag-Cu ores, coexisting with galena, chalcopyrite, hessite, electrum, unnamed Ag6TeS2 and AglsFeBiTe3Se, enclosed and replaced by native silver and acanthite. In the reflected light microscope, the mineral has light gray color, indistinguishable anistropism and hardness around 2-3. The color indices of chenguodaite relative to ICE C illuminator are： x=0.3027, y=0.3076, Y=25.78%,λd=474 nm, Pe=3.68%, similar to those of canfieldite. The average chemical composition from 16 microprobe analyses is Ag8.97Fe1.00Te1.99S4.04, idealized to AggFeTe2S4. The polycrystalline X-ray diffraction of chenguodaite by Gandolfi camera and synchrotron oscillation photography results in 67 reflections with the 12 strongest being （relative intensity in bracket）： 6.742（69）, 6.416（39）, 5.951（33）, 3.265（100）, 2.981（24）, 2.649（22）, 2.25（24）, 2.188（71）, 2.142（22）, 2.123（31）, 2.044（23）, 1.949（33）, which are indexed to a primitive orthorhombic cell with a=12.769 （2） A, b= 14.814（2） A, c= 16.233 （1） A, V= 3070.6 A^3, Z= 9, Dcal.=6.85 g/cm^3. The name is for the late Prof. Chen Guoda, a famous Chinese geologist and the founder of Diwa-Geodepression theory of tectonics.     

FeO影响CaO-SiO_2-MgO-Al_2O_3-Cr_2O_3体系中含铬尖晶石晶体析出的热力学分析

不锈钢渣中的铬以尖晶石矿物相状态赋存时不易溶出,有利于钢渣的资源化利用。本文基于熔体非平衡凝固理论,采用热力学数据库FactSage 7.0研究了FeO添加量对CaO-SiO_2-MgO-Al_2O_3-Cr_2O_3不锈钢渣体系中尖晶石晶体析出温度、析出量、化学组成及铬元素赋存状态的影响规律。模拟计算结果表明,尖晶石晶体为高温析出相,主要由MgCr_2O_4和FeCr_2O_4组成;随着FeO添加量不断增多,尖晶石晶体的析出温度逐渐降低,其最终析出量逐渐增加,析出物中FeCr_2O_4所占比例增加而MgCr_2O_4相对减少;铬元素的赋存状态未受FeO添加量变化影响,仍以尖晶石固溶体形式存在。     

Facile synthesis of nanosized sodium magnesium hydride, NaMgH3

The ternary magnesium hydride NaMgH 3 has been synthesised via reactive milling techniques.The method employed neither a reactive H2 atmosphere nor high pressure sintering or other post-treatment processes.The formation of the ternary hydride was studied as a function of milling time and ball:powder ratio.High purity NaMgH 3 powder(orthorhombic space group Pnma,a 5.437(2),b 7.705(5),c 5.477(2) ;Z 4) was prepared in 5 h at high ball:powder ratios and characterised by powder X-ray diffraction(PXD),Raman spectroscopy and scanning electron microscopy/energy dispersive X-ray spectroscopy(SEM/EDX).The products formed sub-micron scale(typically 200-400 nm in size) crystallites that were approximately isotropic in shape.The dehydrogenation behaviour of the ternary hydride was investigated by temperature programmed desorption(TPD).The nanostructured hydride releases hydrogen in two steps with an onset temperature for the first step of 513 K.     

Corrosion behavior of ferritic ODS steel prepared by adding YH_2 nanoparticles in supercritical water at 600 °C

The corrosion behavior of the ferritic oxide dispersion strengthened(ODS)steel(14Cr-3Al-2W-0.1Ti)prepared by adding YH_2nanoparticles(NPs)was investigated in supercritical water(SCW)at 600°C for 1500 h.The mass gain of the ODS steel(215.5 mg/dm~2)was lower than that of SUS430 steel(357.2 mg/dm~2).A dual oxide layer generated on the surface of ODS steel after corrosion in SCW.The outer layer was composed of Fe_2O_3and Fe_3O_4,while the inner layer composed of the spinel-type FeCr_2O_4together with Al_2O_3.The generation of Y_2Ti_2O_7NPs in the ODS steel by adding YH_2NPs prohibits the formation of Y-Al-O particles and leaves more Al available to form a continuous protective oxide scale to improve the corrosion resistance.Moreover,the Y_2Ti_2O_7NPs act as efficient barriers to suppress the outward diffusion of metal atoms.This novel ODS steel shows potential applications in supercritical water.     

Synthesis and characterization of a three-ring bent-core compound

To investigate the vacuum-deposited films of the banana-shaped mesogens, we prepared a three-ring bent-core （that is, banana-shaped） compound m-bis（4-p-octoxysryrenyl）benzene （m-OSB） and used it as a prototype for studying the related film physics. Herein the synthesis and the structural characterization of m-OSB are reported.^13C and ^1H NMR spectra and ^1R spectrum confirm that m-OSB has a symmetric and all-trans conformation. The results of differential scanning calorimetry, polarizing optical microscopy and X-ray diffractometry indicate that no liquid crystalline phase but two crystalline phases are present in this material： phase Ⅰ （T〈66℃） and phase Ⅱ （66~C〈T〈157℃）; an isotropic state is observed at above 157℃. Combining the X-ray diffraction and the electronic diffraction, we assign the room-temperature crystalline phase I to orthorhombie system and P212121 space group with cell parameters of a = 7.43A°. b=6.34A°, c=72.07A°, and α=β=γ=90°. Molecular modeling reveals that the molecules in the unit cell adopt a layered structure with an antiferro-eleetrie alignment. The structure of phase Ⅱ is very similar to that of phase Ⅰ. Nonlinear optical measurement shows that m-OSB is active for the second harmonic generation （SHG）. Such characterization of the bulk material is necessary for the understanding of the growth and microstructures in the films.     

Mn-ion-enhanced red spectral emission from yttrium aluminum garnet doped cerium phosphor

Mnions were co-doped in yttrium aluminum garnet doped cerium(YAG:Ce) phosphors as a co-activator and host lattice element using the co-precipitation method.These ions broadened the emission spectra of the pure YAG:Ce phosphor,which is caused by the 2E-4A2,5E-5T2 or 1T2-5T2 transition.From our X-ray diffraction results,we observed that Ce3+(1.032 ) was substituted at the Y3+(0.900 ) site,and Mn4+(0.538 ) and Mn3+(0.67 ) were substituted at the Al3+(0.535 ) site.The chromaticity color co-ordinates of YAG:Ce0.06 is(0.203,0.167),and the indices of YAG:Ce0.06,Mn0.04 and YAG:Ce0.06,Mn0.08 are(0.249,0.181) and(0.233,0.194),respectively.The manganese co-doped yttrium aluminum garnet doped cerium blended with the YAG:Ce phosphor showed improved white light emission.     

Crystallographic studies on the binding of coenzyme analogs to D-glyceraldehyde-3-phosphate dehydrogenase fromPalinurus versicolor

In contrast with the coezyme, two coenzyme analogs, ADP-ribose and SNAD, bind non-cooperatively to D-glyceraldehyde-3-phosphate dehydrogenase (GAPDH).Palinurus versicolor (PV) GAPDH complexed with ADP-ribose and SNAD has been crystallized by the method of sitting-drop vapor diffusion. X-ray diffraction data analysis reveals that both crystals belong to the same space group (C2), and have similar cell dimensions: a =152.80 Å,b =100.35 Å, c =128.31 Å,β =110.28° and a =153.41 Å,b =100.51 Å,c =128.44 Å,β =110.48°, respectively. It is estimated that the asymmetric unit in each crystal contains 4 subunits. This is a novel crystal form which is quite different from that previously reported for holoand apo-GAPDH from the same source. The result suggests that the binding of the two coenzyme analogs to GAPDH may lead to some significant conformational changes, which are different from those induced by the coenzyme binding. The self-rotation function indicates that the tetramer of these two GAPDH complexes also has good 222 symmetry. The structural analysis and the comparison with holoand apo-GAPDH may give a clue to the cooperative mechanism of the enzyme.     

High-pressure and high-temperature synthesis of MgB2 and its superconductivity

The single-phase sample of MgB₂ was prepared successfully at the temperature of 900℃ and under the pressure of 3 GPa. The structure of the sample was investigated using powder X-ray diffraction and Rietveld analysis. The results show that the structure of the sample belongs to the hexagonal structure with space group of P6/mmm, a=3.0861(5) Å, c=3.5222(8) Å. The magnetic and resistance measurements indicate that the superconducting transition temperature T_c is 39 K.     

Crystal structure determining of 7-ADCA based on X-ray powder diffraction

Traditionally, crystal structure data can be collected and determined from single-crystal X-ray diffraction. However, in the fields of organic and macromolecular crystallography, it is often difficult or impractical to grow single crystals with suitable sizes and purity. Therefore, it will be benefited from the newly growing analytical tool that combining X-ray powder diffraction based on polycrystalline samples and ab initio calcula- tion[1]. 7-ADCA is one of the most important intermediate…     

Formation mechanism of an aluminium-based chemical conversion coating on AZ91D magnesium alloy

An environmentally clean aluminium-based conversion coating on AZ91D magnesium alloy was studied in aluminium nitrate solutions. The morphology, composition, structure, and formation mechanism of the coating were investigated in detail using scanning electron microscopy/energy dispersion spectrometry, X-ray diffraction, transmission electron microscopy, and electrochemical corrosion tests. The results show that the conversion coating is composed of magnesium, aluminium, and oxygen, and shows an amorphous structure. In the initial stage of coating formation, the grain-like nucleus is composed of Al₁₀O₁₅·xH₂O, (Al₂O₃)_5.333, Al₂O₃, AlO(OH), MgAl₂O₄, (Mg_0.88Al_0.12)(Al_0.94Mg_0.06)₂O₄, and (Mg_0.68Al_0.32)(Al_0.84Mg_0.16)₂O₄. The conversion coating formed in the 0.01 mol/L aluminium nitrate solution for 15 min can improve the corrosion resistance of the magnesium alloy greatly. The discussion reveals that the possible formation mechanism for the aluminium-based conversion coating is the reduction reaction on micro-cathodic sites due to the electrochemically heterogeneous magnesium alloy substrate.     

Synthesis and crystal structure of hydroquinone-β-cyclodextrin complex

The title inclusion complex with the formula [(C₄₂H₇₀O₃₅)₂·(C₆O₂H₆)₃·(H₂O)_21.2(CH₃OH)₂] has been crystallized and characterized by single crystal X-ray analysis. The complex crystallizes in the triclinic system, space group P1, with a = 1.5500 (1), b = 1.5536(1), c = 1.8246(1) nm, α = 113.17(2), β = 99.12(2), γ = 103.37(3)o, V = 3.7739 (4) nm³, Z = 1; D_c = 1.343 g/cm³, μ = 0.124 mm^-1, F(000) = 1594, R = 0.0795 and S = 0.9639. Two independent molecules of β -cyclodextrin (β -CD) form a “head-to-head” dimer. The fairly important factor of the position and stability of the guest in the host cavity is the solvation of the polar group of the guest.     

Phase analysis and thermal conductivity of in situ O′-sialon/β-Si3N4 composites

Typical O??-sialon-based ceramics, with a formula of Si_2?x Al _x O_1+x N_2?x , where x was set as 0.25, were fabricated by in-situ synthesis. Si₃N₄, Al₂O₃, and SiO₂ powders were used as raw materials, and MgO and Y₂O₃ were added as sintering additives. All the samples were sintered at different temperatures under a nitrogen pressure of 0.25?C0.30 MPa, and their microstructure, phase content, and thermal conductivity were evaluated. The effects of O??-sialon and ??-Si₃N₄ on the thermal conductivity were analyzed by numerical calculation in detail. In the case of the similar porosity, the thermal conductivity of O??-sialon-based ceramics decreased with the ratio of O??-sialon/??-Si₃N₄ increasing. When the ratio was 12, the thermal conductivity of O??-sialon ceramics sintered at 1360°C was 1.197 W·m^?1·K^?1.     

Structure and effect of diamagnetism on manganese lithium phosphate glass to cathode materials application

1-x(Li₂O–2P₂O₅)-xMnO₂ glasses where x ?= ?0.2, 0.3 and 0.4 ?mol%, respectively, were synthesized by melted-quenching method. The Mn and P oxidation states and local structures around Mn and P-ions including Mn–O and P–O bonding distances and coordination numbers have been studied via X-ray absorption near edge structure (XANES) and extended X-ray absorption fine structure (EXAFS), respectively. XANES results exhibit a coexistence of oxidation state of Mn²⁺ and Mn³⁺ with a mean value of 2.82. Moreover, Mn and P K-edge EXAFS show the Mn–O and P–O bonding distances of approximately 2.083–2.094 ?Å and 1.766–1.774 ?Å, respectively. A paramagnetism was found for all Mn–P glasses. Additionally, the coercive field (H_c) and remnant magnetization (M_r) increased with increasing Mn contents. However, the low specific capacitances are seriously obtained (<40 ?F ?g^?1) suggesting the effect of natural diamagnetism of lithium phosphate based-glass unlike the borate based-glasses which originally exhibit paramagnetism.     

In situ reaction mechanism of MgAlON in Al-Al2O3-MgO composites at 1700℃ under flowing N2

The Al-Al₂O₃-MgO composites with added aluminum contents of approximately 0wt%, 5wt%, and 10wt%, named as M₁, M₂, and M₃, respectively, were prepared at 1700℃ for 5 h under a flowing N₂ atmosphere using the reaction sintering method. After sintering, the Al-Al₂O₃-MgO composites were characterized and analyzed by X-ray diffraction, scanning electron microscopy, and energy-dispersive X-ray spectroscopy. The results show that specimen M₁ was composed of MgO and MgAl₂O₄. Compared with specimen M₁, specimens M₂ and M₃ possessed MgAlON, and its production increased with increasing aluminum addition. Under an N₂ atmosphere, MgO, Al₂O₃, and Al in the matrix of specimens M₂ and M₃ reacted to form MgAlON and AlN-polytypoids, which combined the particles and the matrix together and imparted the Al-Al₂O₃-MgO composites with a dense structure. The mechanism of MgAlON synthesis is described as follows. Under an N₂ atmosphere, the partial pressure of oxygen is quite low; thus, when the Al-Al₂O₃-MgO composites were soaked at 580℃ for an extended period, aluminum metal was transformed into AlN. With increasing temperature, Al₂O₃ diffused into AlN crystal lattices and formed AlN-polytypoids; however, MgO reacted with Al₂O₃ to form MgAl₂O₄. When the temperature was greater than (1640 ±10)℃, AlN diffused into Al₂O₃ and formed spinel-structured AlON. In situ MgAlON was acquired through a solid-solution reaction between AlON and MgAl₂O₄ at high temperatures because of their similar spinel structures.     

Growth, structural, optical, thermal and dielectric properties of a novel semi-organic nonline ar optical crystal: Dichloro-diglycine zinc II

Dichloro-diglycine zinc II(DCDGZ II),a semi-organic nonlinear optical material has been synthesized and single crystals were grown from the aqueous solution up to dimensions 20×10×3 mm3.The title compound,DCDGZ II(C4H10Cl2N2O4Zn H2O) crystallizes into monoclinic structure with the space group of C2/c.The unit-cell parameters were found to be a=14.4191(7),b=6.9180(2),c=12.9452(6) and Z=4.In the crystal structure,DCDGZ II layer is building up alternatingly with layers of water in which the zinc ions lie on a twofold axis.Theoretical calculations for polarizability,which are useful for device fabrication were made using Clausius–Mosotti equation and Penn analysis and the results were compared.Fourier transform infrared(FTIR) spectroscopic studies were performed for the identification of the different functional groups presented in the compound.The UV–vis–NIR absorption spectrum reveals that the lower UV cut-off wavelength is 240 nm.The optical band gap of the crystal was estimated as 2.2 eV.The surface morphology,thermal behaviour,dielectric properties have been studied using SEM,TG/DTA and LCR HITESTER analyzer.The nonlinear optical property of the crystal was also confirmed using Kurtz powder technique.     

Development of Fe(III)-containing ether-functionalized imidazolium ionic liquids for aryl Grignard cross-coupling of alkyl halides

A series of Fe(Ⅲ)-containing imidazolium-based ionic liquids containing ether substituents,including[C3OMim][FeCl4](1,[C3OMim]=1-(2-methoxyethyl)-3-methylimidazolium),[C3OiPim][FeCl4](2,[C3OiPim]=1-isopropyl-3-(2-methoxyethyl)imidazolium),[C3OBim][FeCl4](3,[C3OBim]=1-butyl-3-(2-methoxyethyl)imidazolium),[(C3O)2im][FeCl4](4,[(C3O)2im]=1,3-bis(2-methoxyethyl)imidazolium),[C3OMim][FeBr4](5)and[(C3O)2im][FeBr4](6),were prepared and characterized by elemental analysis,Raman spectroscopy and electrospray ionization mass spectrometry.The catalytic performances of 1–6 and related Fe(III)-based catalysts in the cross-coupling of aryl Grignard reagents with alkyl halides bearing-hydrogens were studied,revealing that mono(ether)functionality improves the catalytic activity and that bis(ether)functionality improves the reusability.After simply decanting the product contained in the ethereal layer,complex 4,which containing bis(ether)-functionalized imidazolium cation,could be successfully recycled seven times.     

Reaction condition optimization and kinetic investigation of roasting zinc oxide ore using (NH<Subscript>4</Subscript>)<Subscript>2</Subscript>SO<Subscript>4</Subscript>

An orthogonal test was used to optimize the reaction conditions of roasting zinc oxide ore using (NH₄)₂SO₄. The optimized reaction conditions are defined as an (NH₄)₂SO₄/zinc molar ratio of 1.4:1, a roasting temperature of 440°C, and a thermostatic time of 60 min. The molar ratio of (NH₄)₂SO₄/zinc is the most predominant factor and the roasting temperature is the second significant factor that governs the zinc extraction. Thermogravimetric–differential thermal analysis was used for (NH₄)₂SO₄ and zinc mixed in a molar ratio of 1.4:1 at the heating rates of 5, 10, 15, and 20 K·min-1. Two strong endothermic peaks indicate that the complex chemical reactions occur at approximately 290°C and 400°C. XRD analysis was employed to examine the transformations of mineral phases during roasting process. Kinetic parameters, including reaction apparent activation energy, reaction order, and frequency factor, were calculated by the Doyle–Ozawa and Kissinger methods. Corresponding to the two endothermic peaks, the kinetic equations were obtained.     

Kinetic studies of the decomposition reaction of adducts of dinuclear Fe(Ⅱ)/O2

Kinetic studies of the decomposition reaction of dinuclear Fe(Ⅱ) adducts [Fe₂(N-Et-HPTB){O₂P(OPh)₂}](Cl- O₄)₂ (1) and [Fe₂(N-Et-HPTB) {O₂P(Ph)₂}] (ClO₄)₂ (2) with O₂ have been carried out at low temperature using UV-vis spectra. The decomposition reaction of Fe(Ⅱ)/O₂ adducts was first-order in the experimental conditions, and the activation parameters were obtained. ?H^¹ = 85.62 kJ·mol^-1, ?S¹ = 19.43 J·mol^-1·K^-1 for compound (1) and ?H^¹ = 97.97 kJ·mol^-1, ?S^¹ = 55.68 J·mol^-1·K^-1 for compound (2). These results are similar to those of dioxygen adducts of other metals complexes and natural enzymes such as methane mono- oxygenase (MMOH).