Effect of Al_2O_(3sf) addition on the friction and wear properties of(SiC_p+Al_2O_(3sf))/Al2024 composites fabricated by pressure infiltration

Aluminum(Al) 2024 matrix composites reinforced with alumina short fibers(Al_2O_(3sf)) and silicon carbide particles(SiC_p) as wear-resistant materials were prepared by pressure infiltration in this study. Further, the effect of Al_2O_(3sf) on the friction and wear properties of the as-synthesized composites was systematically investigated, and the relationship between volume fraction and wear mechanism was discussed. The results showed that the addition of Al_2O_(3sf), characterized by the ratio of Al_2O_(3sf) to SiC_p, significantly affected the properties of the composites and resulted in changes in wear mechanisms. When the volume ratio of Al_2O_(3sf) to SiC_p was increased from 0 to 1, the rate of wear mass loss(K_m) and coefficients of friction(COFs) of the composites decreased, and the wear mechanisms were abrasive wear and furrow wear. When the volume ratio was increased from 1 to 3, the COF decreased continuously; however, the K_m increased rapidly and the wear mechanism became adhesive wear.     

Influence of nano-Al<Subscript>2</Subscript>O<Subscript>3</Subscript>-reinforced oxide-dispersion-strengthened Cu on the mechanical and tribological properties of Cu-based composites

The mechanical and tribological properties of Cu-based powder metallurgy (P/M) friction composites containing 10wt%–50wt% oxide-dispersion-strengthened (ODS) Cu reinforced with nano-Al₂O₃ were investigated. Additionally, the friction and wear behaviors as well as the wear mechanism of the Cu-based composites were characterized by scanning electron microscopy (SEM) in conjunction with energy-dispersive X-ray spectroscopy (EDS) elemental mapping. The results indicated that the Cu-based friction composite containing 30wt% ODS Cu exhibited the highest hardness and shear strength. The average and instantaneous friction coefficient curves of this sample, when operated in a high-speed train at a speed of 300 km/h, were similar to those of a commercial disc brake pad produced by Knorr-Bremse AG (Germany). Additionally, the lowest linear wear loss of the obtained samples was (0.008 ± 0.001) mm per time per face, which is much lower than that of the Knorr-Bremse pad ((0.01 ± 0.001) mm). The excellent performance of the developed pad is a consequence of the formation of a dense oxide composite layer and its close combination with the pad body.     

In-situ fabrication of Al(Zn)-Al2O3 graded composite using the aluminothermic reaction during hot pressing

In this study, the fabrication of multilayer Al(Zn)–Al₂O₃ with different volume fractions of Al₂O₃ was investigated. Al and ZnO powders were milled by a planetary ball mill, after which five-layer functionally graded samples were produced through hot pressing at 580℃ and 90 MPa pressure for 30 min. Formation of reinforcing Al₂O₃ particles occurred in the aluminum matrix via the aluminothermic reaction. Determination of the ignition temperature of the aluminothermic reaction was accomplished using differential thermal and thermogravimetric analyses. Scanning electron microscopy, energy dispersive spectroscopy, and X-ray diffractometery analyses were utilized to characterize the specimens. The thermal analysis results showed that the ignition temperatures for the aluminothermic reaction of layers with the highest and lowest ZnO contents were 667 and 670℃, respectively. Microstructural observation and chemical analysis confirmed the fabrication of Al(Zn)–Al₂O₃ functionally graded materials composites with precipitation of additional Zn in the matrix. Moreover, nearly dense functionally graded samples demonstrated minimum and maximum hardness values of HV 75 and HV 130, respectively.     

CuCrW(Al<Subscript>2</Subscript>O<Subscript>3</Subscript>) nanocomposite: mechanical alloying,microstructure, and tribological properties

The effect of alumina nanoparticle addition on the microstructure and tribological properties of a CuCrW alloy was investigated in this work. Mechanical alloying was carried out in a satellite ball mill. The tribological properties of the samples were evaluated using pin-on-disk wear tests with different pins (alumina, tungsten carbide, and steel pins). The results indicated that the tungsten carbide pin had a lower coefficient of friction than the alumina and steel pins because of its high hardness and low surface roughness. In addition, when the sliding rate was decreased, the weight-loss rate increased. The existence of alumina nanoparticles in the nanocomposite led to a lower weight-loss rate and to a change in the wear mechanism from adhesive to abrasive.     

Static synthesis of high-quality MCM-22 zeolite with high SiO2／Al2O3 ratio

We demonstrate a synthesis method to broaden the range of SiO2/Al2O3 ratio (30-100) of high-silica MCM-22 zeolites by prolonging the aging time of the gel before the crystallization. The synthesis conditions such as silica sources, chemical compositions of initial gel and aging time of gel were investigated in detail.High quality MCM-22 products with various morphologies have been synthesized by optimize their synthesis conditions.Our results show that increasing of the aging time can make the gel be homogenization and promote their nucleus formation,which may avoid the formation of impurity phase and thus broaden the range of SiO2/Al2O3 ratio.     

Microstructures and properties of Al<Subscript>2</Subscript>O<Subscript>3</Subscript> dispersion-strengthened copper alloys prepared through different methods

Al₂O₃ dispersion copper alloy powder was prepared by internal oxidation, and three consolidation methods—high-velocity compaction (HVC), hot pressing (HP), and hot extrusion (HE)—were used to prepare Al₂O₃ dispersion-strengthened copper (Cu–Al₂O₃) alloys. The microstructures and properties of these alloys were investigated and compared. The results show that the alloys prepared by the HP and HE methods exhibited the coarsest and finest grain sizes, respectively. The alloy prepared by the HVC method exhibited the lowest relative density (98.3% vs. 99.5% for HP and 100% for HE), which resulted in the lowest electrical conductivity (81% IACS vs. 86% IACS for HP and 87% IACS for HE). However, this alloy also exhibited the highest hardness (77 HRB vs. 69 HRB for HP and 70 HRB for HE), the highest compressive strength (443 MPa vs. 386 MPa for HP and 378 MPa for HE), and the best hardness retention among the investigated alloys. The results illustrate that the alloy prepared by the HVC method exhibits high softening temperature and good mechanical properties at high temperatures, which imply long service life when used as spot-welding electrodes.     

Tribological properties of La2O3 and CeO2 doped CoCrW coatings deposited by supersonic plasma spraying

A novel supersonic plasma spraying was used to prepare rare earth oxides doped CoCrW coatings. X-ray diffractometer, contact surface profiler, hardness tester, micro-friction and -wear tester and en- vironmental scanning electron microscope equipped with energy dispersive X-ray spectroscopy were employed to investigate the phase structure, surface morphology, microhardness, friction and wear properties of the sprayed coatings. The results show that rare earth oxide doped coatings have high microhardness and excellent tribological properties. Furthermore, the friction and wear mechanisms of sprayed coatings are also discussed.     

Microstructure and properties of mullite-based porous ceramics produced from coal fly ash with added Al<Subscript>2</Subscript>O<Subscript>3</Subscript>

Using coal fly ash slurry samples supplemented with different amounts of Al₂O₃, we fabricated mullite-based porous ceramics via a dipping-polymer-replica approach, which is a popular method suitable for industrial application. The microstructure, phase composition, and compressive strength of the sintered samples were investigated. Mullite was identified in all of the prepared materials by X-ray diffraction analysis. The microstructure and compressive strength were strongly influenced by the content of Al₂O₃. As the Al/Si mole ratio in the starting materials was increased from 0.84 to 2.40, the amount of amorphous phases in the sintered microstructure decreased and the compressive strength of the sintered samples increased. A further increase in the Al₂O₃ content resulted in a decrease in the compressive strength of the sintered samples. The mullite-based porous ceramic with an Al/Si molar ratio of 2.40 exhibited the highest compressive strength and the greatest shrinkage among the investigated samples prepared using coal fly ash as the main starting material.     

Novel mechanism for the modification of Al<Subscript>2</Subscript>O<Subscript>3</Subscript>-based inclusions in ultra-low carbon Al-killed steel considering the effects of magnesium and calcium

Many researchers have explored the inclusion modification mechanism to improve non-metallic inclusion modifications in steelmaking. In this study, two types of industrial trials on inclusion modifications in liquid steel were conducted using ultra-low-carbon Al-killed steel with different Mg and Ca contents to verify the effects of Ca and Mg contents on the modification mechanism of Al₂O₃-based inclusions during secondary refining. The results showed that Al₂O₃-based inclusions can be modified into liquid calcium aluminate or a multi-component inclusion with the addition of a suitable amount of Ca. In addition,[Mg] in liquid steel can further reduce CaO in liquid calcium aluminate to drive its evolution into CaO-MgO-Al₂O₃ multi-component inclusions. Thermodynamic analysis confirmed that the reaction between[Mg] and CaO in liquid calcium aluminate occurs when the MgO content of liquid calcium aluminate is less than 3wt% and the temperature is higher than 1843 K.     

Reinforcing effect of graphene on the mechanical properties of Al<Subscript>2</Subscript>O<Subscript>3</Subscript>/TiC ceramics

Multilayer graphene (MLG)-reinforced Al₂O₃/TiC ceramics were fabricated through hot pressing sintering, and the reinforcing effect of MLG on the microstructure and mechanical properties of the composites was investigated by experiment and simulation. The simulation of dynamic crack initiation and propagation was investigated based on the cohesive zone method. The results show that the composite added with 0.2wt% MLG has excellent flexural strength and high fracture toughness. The major reinforcing mechanisms are the synergistic effect by strong and weak bonding interfaces, MLG pull-out, and grain refinement resulting from the addition of MLG. In addition, the aggravating of crack deflection, branching, blunting, and bridging have indispensable contribution to the improvement of the as-designed materials.     

Effects of metal binder on the microstructure and mechanical properties of Al<Subscript>2</Subscript>O<Subscript>3</Subscript>-based micro-nanocomposite ceramic tool material

The Al₂O₃-(W,Ti)C composites with Ni and Mo additions varying from 0vol% to 12vol% were prepared via hot pressing sintering under 30 MPa. The microstructure was investigated via X-ray diffraction (XRD) and scanning electron microscopy (SEM) equipped with energy dispersive spectrometry (EDS). Mechanical properties such as flexural strength, fracture toughness, and Vickers hardness were also measured. Results show that the main phases Al₂O₃ and (W,Ti)C were detected by XRD. Compound MoNi also existed in sintered nanocomposites. The fracture modes of the nanocomposites were both intergranular and transgranular fractures. The plastic deformation of metal particles and crack bridging were the main toughening mechanisms. The maximum flexural strength and fracture toughness were obtained for 9vol% and 12vol% additions of Ni and Mo, respectively. The hardness of the composites reduced gradually with increasing content of metals Ni and Mo.     

Effects of Fe<Subscript>2</Subscript>O<Subscript>3</Subscript> on the properties of ceramics from steel slag

Ferric oxide is one of the key factors affecting both the microstructure and the properties of CaO-MgO-SiO₂-based ceramics. Research on this effect is significant in the utilization of iron-rich solid wastes in ceramics. Ceramic samples with various Fe₂O₃ contents (0wt%, 5wt%, and 10wt%) were prepared and the corresponding physical properties and microstructure were studied. The results indicated that Fe₂O₃ not only played a fluxing role, but also promoted the formation of crystals. Ceramics with 5wt% of Fe₂O₃ addition attained the best mechanical properties with a flexural strength of 132.9 MPa. Iron ions were dissolved into diopside, consequently causing phase transformation from diopside and protoenstatite to augite, thereby contributing to the enhancement of its properties. An excess amount of Fe₂O₃ addition (10wt% or more) resulted in deteriorated properties due to the generation of an excess volume of liquid and the formation of high-porosity structures within ceramics.     

Cu-Zn-Al2O3 nanocomposites:study of microstructure,corrosion,and wear properties

Alumina nanoparticles were added to a Cu-Zn alloy to investigate their effect on the microstructural, tribological, and corrosion properties of the prepared alloys. Alloying was performed using a mixture of copper and zinc powders with 0vol% and 5vol% of α-Al nanopowder in a satellite ball mill. The results showed that the Cu-Zn solid solution formed after 18 h of mechanical alloying. The mechanically alloyed powder was compacted followed by sintering of the obtained green compacts at 750℃ for 30 min. Alumina nanoparticles were uniformly distributed in the matrix of the Cu-Zn alloy. The tribological properties were evaluated by pin-on-disk wear tests, which revealed that, upon the addition of alumina nanoparticles, the coefficient of friction and the wear rate were reduced to 20% and 40%, respectively. The corrosion properties of the samples exposed to a 3.5wt% NaCl solution were studied using the immersion and potentiodynamic polarization methods, which revealed that the addition of alumina nanoparticles reduced the corrosion current of the nanocomposite by 90%.     

Preparation and radar-absorbing properties of Al<Subscript>2</Subscript>O<Subscript>3</Subscript>/TiO<Subscript>2</Subscript>/Fe<Subscript>2</Subscript>O<Subscript>3</Subscript>/Yb<Subscript>2</Subscript>O<Subscript>3</Subscript> composite powder

Al₂O₃/TiO₂/Fe₂O₃/Yb₂O₃ composite powder was synthesized via the sol-gel method. The structure, morphology, and radar-absorption properties of the composite powder were characterized by transmission electron microscopy, X-ray diffraction analysis and RF impedance analysis. The results show that two types of particles exist in the composite powder. One is irregular flakes (100-200 nm) and the other is spherical Al₂O₃ particles (smaller than 80 nm). Electromagnetic wave attenuation is mostly achieved by dielectric loss. The maximum value of the dissipation factor reaches 0.76 (at 15.68 GHz) in the frequency range of 2-18 GHz. The electromagnetic absorption of waves covers 2-18 GHz with the matching thicknesses of 1.5-4.5 mm. The absorption peak shifts to the lower-frequency area with increasing matching thickness. The effective absorption band covers the frequency range of 2.16-9.76 GHz, and the maximum absorption peak reaches -20.18 dB with a matching thickness of 3.5 mm at a frequency of 3.52 GHz.     

SiC_p/Al_2O_(3f) 混杂增强 2024Al 复合材料摩擦磨损性能的研究

研究了２０２４铝合金、ＳｉＣｐ／Ａｌ２Ｏ３ｆ混杂增强２０２４Ａｌ复合材料与汽车刹车材料对磨时的摩擦磨损性能．借助扫描电镜对磨损形貌的观察,分析了材料的磨损机理．在本研究的试验条件下,２０２４铝合金的磨损极为严重,ＳｉＣｐ／Ａｌ２Ｏ３ｆ混杂增强２０２４Ａｌ复合材料的耐磨性能良好．由于ＳｉＣｐ／Ａｌ２Ｏ３ｆ混杂增强２０２４Ａｌ复合材料的密度较低,因而该材料在汽车工业中有广泛的应用前景．     

Effect of reinforcement content on the adhesive wear behavior of Cu10Sn5Ni/Si3N4 composites produced by stir casting

The main objective of this paper was to fabricate Cu10Sn5Ni alloy and its composites reinforced with various contents of Si₃N₄ particles (5wt%, 10wt%, and 15wt%) and to investigate their dry sliding wear behavior using a pin-on-disk tribometer. Microstructural examinations of the specimens revealed a uniform dispersion of Si₃N₄ particles in the copper matrix. Wear experiments were performed for all combinations of parameters, such as load (10, 20, and 30 N), sliding distance (500, 1000, and 1500 m), and sliding velocity (1, 2, and 3 m/s), for the alloy and the composites. The results revealed that wear rate increased with increasing load and increasing sliding distance, whereas the wear rate decreased and then increased with increasing sliding velocity. The primary wear mechanism encountered at low loads was mild adhesive wear, whereas that at high loads was severe delamination wear. An oxide layer was formed at low velocities, whereas a combination of shear and plastic deformation occurred at high velocities. The mechanism at short sliding distances was ploughing action of Si₃N₄ particles, which act as protrusions; by contrast, at long sliding distances, direct metal-metal contact occurred. Among the investigated samples, the Cu/10wt% Si₃N₄ composite exhibited the best wear resistance at a load of 10 N, a velocity of 2 m/s, and a sliding distance of 500 m.     

Preparation and luminescence properties of YeO3：Er^3＋/TiO2 with high specific surface area

The three composites Y2O3 :Er3+ , Y2O3 :Er3+ /Yb 3+ andY2O3 :Er3+ /TiO2 were prepared using coprecipitation and sol-gel techniques. Their morphology, specific surface area, porosity, UV-vis. absorption spectra and fluorescence spectra were measured using SEM, TEM, surface analysis, UV-vis. absorption and photoluminescence spectrophotometry. SEM and TEM showed that samples prepared using coprecipitation were dispersed, while Y2O3 :Er3+ /TiO2 particles possessed a mesoporous surface and average diameter of ab...     

Dissolution of Al<Subscript>2</Subscript>TiO<Subscript>5</Subscript> inclusions in CaO-SiO<Subscript>2</Subscript>-Al<Subscript>2</Subscript>O<Subscript>3</Subscript> slags at 1823 K

Al-Ti-O inclusions always clog submerged nozzles in Ti-bearing Al-killed steel. A typical synthesized Al₂TiO₅ inclusion was immersed in a CaO-SiO₂-Al₂O₃ molten slag for different durations at 1823 K. The Al₂TiO₅ dissolution paths and mechanism were revealed by scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS). Decreased amounts of Ti and Al and increased amounts of Si and Ca at the dissolution boundary prove that inclusion dissolution and slag penetration simultaneously occur. SiO₂ diffuses or penetrates the inclusion more quickly than CaO, as indicated by the w(CaO)/w(SiO₂) value in the reaction region. A liquid product (containing 0.7–1.2 w(CaO)/w(SiO₂), 15wt%–20wt% Al₂O₃, and 5wt%–15wt% TiO₂) forms on the inclusion surface when Al₂TiO₅ is dissolved in the slag. Al₂TiO₅ initially dissolves faster than the diffusion rate of the liquid product toward the bulk slag. With increasing reaction time, the boundary reaches its largest distance, the Al₂TiO₅ dissolution rate equals the liquid product diffusion rate, and the dissolution process remains stable until the inclusion is completely dissolved.     

Chemical quenching and inhibition of positronium in Cr<Subscript>2</Subscript>O<Subscript>3</Subscript>/Al<Subscript>2</Subscript>O<Subscript>3</Subscript> catalysts

The pore structure of Cr2O3/Al2O3 catalysts and the surface chemical properties of these pores were characterized by positron lifetime and coincidence Doppler broadening (CDB) measurements. Four lifetime components could be resolved from the positron lifetime spectrum, with two long lifetime components and two short lifetime components. The two long lifetimes τ4 and τ3 are attributed to ortho-positronium (o-Ps) annihilation in large pores and microvoids, respectively. With increasing Cr2O3 content, both τ4 and its intensity I4 show sharp decrease, while τ3 and its intensity I3 keep nearly unchanged. The Doppler broadening S parameters also show sharp decrease with increasing Cr2O3 content. Detailed analysis of the CDB spectrum reveals that the parapositronium (p-Ps) intensity also decreases with increasing Cr2O3 content. This indicates that the change of o-Ps lifetime τ4 is due to the chemical quenching by Cr2O3 but not spin-conversion of positronium. The decrease of o-Ps intensity I4 indicates that Cr2O3 also inhibits positronium formation.     

Novel approaches to produce Al2O3– TiC/TiCN– Fecomposite powders directly from ilmenite

Al2O3 –TiC/TiCN–Fe composite powders were successfully prepared directly from ilmenite at 1300–1400℃.The effects of Al/C ratio,sintering atmosphere,and reaction temperature and time on the reaction products were investigated.Results showed that the nitrogen atmosphere was bene cial to the reduction of ilmenite and the formation of Al2O3 –TiC/TiCN–Fe composite powders.When the reaction temperature was between 600 and 1100℃,the intermediate products,TiO2,Ti3O5 and Ti4O7 were found,which changed to TiC or TiCN at higher temperature.Al/C ratio was found to affect the reaction process and synthesis products.When Al addition was 0.5 mol,the Al2O3 phase did not appear.The content of carbon in TiCN rose when the reaction temperature was increased.