超高强度冷轧双相钢组织与性能

在Gleeble-3500热模拟试验机上进行冷轧超高强度双相钢的连续退火工艺研究,利用光学显微镜、扫描电镜、透射电镜和拉伸试验研究了连续退火过程中各个参数对1 000 MPa级冷轧双相钢组织性能的影响.结果表明:试验用钢在退火温度800℃下保温80 s,可以得到抗拉强度为1030MPa、延伸率为14%超高强双相钢;随着退火温度的升高,屈服强度和抗拉强度降低.当退火温度为830℃时,显微组织中粒状的非马氏体组织明显增多.过时效温度低于300℃时,屈服强度和抗拉强度变化不大;当过时效温度超过300℃时,抗拉强度急剧下降,屈服强度先降低后升高,在过时效温度为360℃时开始出现屈服平台.     

冷轧双相钢再加热过时效热处理实验研究

为提升DP590冷轧双相钢综合力学性能,利用CAS-300Ⅱ型连退模拟试验机,通过模拟退火实验,研究了冷轧双相钢再加热过时效工艺(R-OA工艺)中,不同再加热温度对其组织性能的影响,并与传统冷轧双相钢的生产工艺的组织性能进行分析对比,结果表明:R-OA工艺较传统工艺相比,马氏体周围有较多M-A岛组织;R-OA工艺再加热温度超过350℃时,实验钢屈服强度小于290 MPa,屈强比0.42,抗拉强度超过701 MPa,延伸率大于31.8%。     

过时效温度对低成本冷轧双相钢组织性能的影响

通过建立合理的热处理工艺窗口,将低附加值的钢种升级为具有高强塑性的高附加值双相钢产品.以常规C-Mn钢热轧板坯为原料,经过热轧及冷轧后,进行连续退火实验.实验钢经过不同的冷却后过时效制度,形成了铁素体和马氏体组成的微观组织.当过时效温度在320℃以下时,避免了贝氏体组织的出现,并且马氏体相的体积分数随温度的降低而增加.实验钢的抗拉强度与马氏体相含量成正比,屈服强度和延伸率与其成反比,在320℃过时效处理下可获得最佳的综合力学性能,强塑积为182546MPa%.     

低碳中锰热轧TRIP钢退火工艺及组织演变

研究了第三代高强度高塑性TRIP钢的退火工艺对性能的影响和组织演变规律.热轧后形成的原始马氏体与临界退火时形成的残余奥氏体使TRIP钢具有良好的强度和塑性.结果表明:实验用钢可获得1000MPa以上的抗拉强度和30%以上的断后延伸率,且强塑积30 GPa.%;退火温度和保温时间对钢的力学性能具有显著影响,热轧TRIP钢临界退火温度为630℃,保温时间18 h时,实验用钢能获得最佳的综合力学性能.     

控轧温度区间对含Nb热轧多相钢组织和性能的影响

以含Nb微合金化试验钢为研究对象,通过3个不同精轧温度区间的轧制+层流冷却、空冷、超快冷的TMCP工艺获得了含有铁素体、贝氏体、马氏体以及少量残余奥氏体的显微组织.分析了控轧温度区间对含Nb微合金化试验钢显微组织和力学性能的影响.结果表明,在控冷工艺参数相近的情况下,随着精轧开轧温度和终轧温度的降低,试验钢的抗拉强度减小,屈服强度、延伸率和强塑积增大.其中采用850～800℃的温度区间精轧+层流冷却、空冷、超快冷的TMCP工艺时,试验钢的屈服强度、延伸率和强塑积分别达到了513MPa,35%和25235MPa.%的最大值.     

合金元素及热处理工艺对1000MPa级TRIP钢性能的影响

为了获得强度高(1 000 MPa)、塑性好的相变诱发塑性(TRIP)钢,通过拉伸实验、SEM、TEM和XRD等方法研究了合金元素及贝氏体等温温度对实验钢的影响.结果表明:随着等温温度的升高,强度先下降后上升.延伸率与强塑积都随着温度的升高先上升,在400℃出现峰值后下降.等温温度低于320℃或高于480℃时,抗拉强度最高,达到1 000 MPa以上,强塑积达到22 080 MPa.%;400℃等温时,延伸率和强塑积最高,分别达到31%和27 150 MPa.%.Al部分取代Si后,实验钢强度下降.再加入0.5%Cu,强度明显上升,延伸率下降,强塑积达到25 085 MPa.%.说明在一定热处...     

冷轧双相钢不停炉连续退火生产工艺改进

不停炉生产冷轧双相钢是控制成本、提高合同交付率的关键技术。对某钢厂连续退火机组生产双相钢前必须停炉的方法进行了分析和改进,结果表明,连续退火机组TV值越小,过时效段降温速度越快;降低快冷段出口温度可显著地降低过时效温度。通过对生产组织的优化,实现了不停炉生产冷轧双相钢。     

时效温度对890MPa级含铜钢组织与性能的影响

根据纳米析出强化机制,设计了一种屈服强度为890MPa的超高强海洋工程用钢——NEU890钢.在相同固溶条件下,研究了时效温度对NEU890钢显微组织、室温拉伸性能、-40℃ Charpy冲击功的影响.用透射电子显微镜分析纳米级析出相分布,并计算出其强度贡献值.结果表明,固溶态试样屈服强度为852MPa,500℃时效屈服强度达到峰值1026MPa,呈现典型时效析出强化特征.NEU890钢的脆性时效温度区间为300~500℃.当时效温度为550~600℃时,NEU890钢的屈服强度为994~910MPa,-40℃冲击功为108~166J,可满足EQ91钢拉伸和冲击性能指标要求.     

影响冷轧DP590组织性能的连续退火工艺

为确定最优的退火工艺制度,对某钢厂冷轧DP590钢种连续退火工艺进行模拟试验,对该钢种在不同退火温度、快冷速度、过时效温度工艺条件下的组织和性能进行分析.结果表明:800℃退火时双相钢组织中马氏体比例为10％～15％,得到理想的双相钢的性能和组织;冷速提高可获得强化效果明显的板条马氏体,快冷段冷却速度在2(25℃/s时材料具有综合的性能指标;过高的过时效温度,发生贝氏体转变过时效温度为260～290℃可获得较为理想的组织和性能.     

退火温度对430不锈钢冷轧板组织和力学性能的影响

针对现场生产的430不锈钢冷轧板,通过高温连续退火实验研究了退火温度对材料显微组织、强度、塑性以及各向异性性能的影响.通过实验得到了合理的两段式加热连续退火工艺:选取中间温度为600℃,加热II段的加热速率为2.3℃·s-1,最高加热温度为840℃.随着退火温度的升高,薄板的屈服强度和硬度呈明显的两阶段降低趋势,延伸率呈"S"型趋势增加,平均塑性应变比基本保持不变(1.25左右),而轧制平面各向异性指数有一定的降低.针对430不锈钢冷轧板分别建立了屈服强度与退火软化率和延伸率之间的定量关系.     

两相区退火温度对高铝低硅TRIP 钢组织性能的影响

对高铝低硅TRIP钢进行两相区退火,通过分析退火后实验钢的微观结构和力学性能,建立了加工硬化指数与相组成的关系,探讨了残余奥氏体稳定性对力学性能的影响.结果表明,随着两相区退火温度的升高,实验钢中贝氏体含量逐渐降低,残余奥氏体含量先增大后降低,并在930℃退火时达到最大.随着两相区退火温度的升高,实验钢的抗拉强度逐渐降低,延伸率先增大后降低,930℃退火时抗拉强度为665MPa,延伸率达到最大,为30%,强塑积约为20GPa·%.EBSD统计和拉伸试验的结果表明,两相区退火温度为930℃时,残余奥氏体稳定性适中,从而在拉伸过程中不断地提供加工硬化,推迟颈缩的发生,大幅度提高塑性.     

临界区退火对含磷低硅TRIP钢组织性能的影响

在实验条件下对含磷TRIP(transformation inducedplasticity)钢进行临界区退火研究，主要研究了不同退火条件对实验钢组织和力学性能的影响.通过添加P元素降低钢中的Si含量，可改善表面质量，解决镀锌问题，且P价格低廉，成本降低.结果表明:随等温时间增加，贝氏体含量增加，抗拉强度增加；在两种等温温度下，残余奥氏体量都是呈先增加后降低的趋势，780℃等温时在180s时得到最大的残余奥氏体量22%，800℃等温时在90s时得到最大的残余奥氏体量20%；780℃等温180s时获得最佳力学性能，强塑积达22854MPa·%，P的加入并未引起力学性能损失，各项力学性能优良.     

Effects of overaging temperature on the microstructure and properties of 600 MPa cold-rolled dual-phase steel

C–Mn steels prepared by annealing at 800°C for 120 s and overaging at 250–400°C were subjected to pre-straining (2%) and baking treatments (170°C for 20 min) to measure their bake-hardening (BH2) values. The effects of overaging temperature on the microstructure, mechanical properties, and BH2 behavior of 600 MPa cold-rolled dual-phase (DP) steel were investigated by optical microscopy, scanning electron microscopy, and tensile tests. The results indicated that the martensite morphology exhibited less variation when the DP steel was overaged at 250–350°C. However, when the DP steel was overaged at 400°C, numerous non-martensite and carbide particles formed and yield-point elongation was observed in the tensile curve. When the overaging temperature was increased from 250 to 400°C, the yield strength increased from 272 to 317 MPa, the tensile strength decreased from 643 to 574 MPa, and the elongation increased from 27.8% to 30.6%. Furthermore, with an increase in overaging temperature from 250 to 400°C, the BH2 value initially increases and then decreases. The maximum BH2 value of 83 MPa was observed for the specimen overaged at 350°C.     

预处理组织对低碳钢IQ&P工艺下组织及性能影响

采用γ单相区和γ+α双相区轧制并淬火工艺以及双相区再加热-淬火-碳配分( IQ&P)工艺,研究预处理组织对低碳钢室温状态多相组织特征及力学性能的影响规律. 实验用低碳钢经两种工艺轧制并淬火处理,获得马氏体和马氏体+铁素体的预处理组织,再经双相区IQ&P工艺处理后均获得多相组织. 马氏体预处理钢的室温组织由板条状亚温铁素体、块状回火马氏体以及一定比例的针状未回火马氏体和8. 2%的针状残余奥氏体组成;马氏体+铁素体预处理钢由板条状亚温铁素体、块状和针状未回火马氏体以及14. 3%的短针状或块状残余奥氏体组成. 在相同的双相区IQ&P工艺参数下,预处理组织为马氏体的钢抗拉强度为770 MPa,伸长率为28%,其强塑积为21560 MPa·%;而预处理组织为马氏体+铁素体的钢抗拉强度为834 MPa,伸长率增大到36. 2%,强塑积达到30190 MPa·%,获得强度与塑性的优良结合.     

Effect of continuous annealing parameters on the mechanical properties and microstructures of a cold rolled dual phase steel

A cold rolled dual phase (DP) steel with the C-Si-Mn alloy system was trial-produced in the laboratory, utilizing a Gleeble-3800 thermal simulator. The effects of continuous annealing parameters on the mechanical properties and microstructures of the DP steel were investigated by mechanical testing and microstructure observation. The results show that soaking between 760 and 820℃ for more than 80 s, rapid cooling at the rate of more than 30℃/s from the quenching temperature between 620 and 680℃, and overaging lower than 300℃ are beneficial for the mechanical properties of DP steels. An appropriate proportion of the two phases is one of the key factors for the favorable properties of DP steels. If the volume fraction of martensite and, thereby, free dislocations are deficient, the tensile strength and n value of DP steels will decrease, whereas, the yield strength will increase. But if the volume fraction of martensite is excessive to make it become a dominant phase, the yield and tensile strength will increase, whereas, the elongation will decrease obviously. When rapid cooling rate is not fast enough, pearlite or cementite will appear, which will degrade the mechanical properties. Even though martensite is sufficient, if it is decomposed in high temperature tempering, the properties will he unsatisfied.     

Al对HP40合金高温力学性能的影响

通过中频感应炉熔炼制备出铝质量分数分别为5%、7.5%、10%的HP40合金,在900℃下测试各合金的高温拉伸性能,并在扫描电镜下观察各合金的断口形貌.结果表明:随着Al质量分数的增加,合金的高温屈服强度、抗拉强度均先升高后降低,合金的延伸率先降低后增加.铝质量分数为5%的HP40合金具有最佳的高温力学性能,其900℃下的屈服强度为125MPa,抗拉强度为132MPa,延伸率为12%.