固体卤化物的抑尘性能

用试验方法分别测定了含ＮａＣｌ，ＣａＣｌ２，ＭｇＣｌ２３种卤化物的粉尘试样在自然环境中昼夜周期吸湿、放湿的行为，并统计分析了试样吸湿率与吸湿剂含量、空气中的温度、湿度等因素之间的关系．其研究结果对卤化物抑制路面、地面和各种散体堆放场等的扬尘具有重要的实际意义．     

卤化物与水玻璃复合物的抑尘性能

在恒温箱中测定了粉尘试样添加ＣａＣｌ２或ＭｇＣｌ２和水玻璃后的含水率与环境温度、湿度、有效抑尘时间等因素之间的关系．研究结果表明：（１）当环境温度低于３１℃，相对湿度高于６０％，粉尘试样中ＣａＣｌ２和水玻璃含量的质量分数分别达到２０％和１０％（ＭｇＣｌ２和水玻璃含量的质量分数为２３％和１１．５％）时，试样的含水率就能保持大于５％（质量分数）；（２）当环境温度低于４０℃，相对湿度高于５０％，粉尘试样中ＣａＣｌ２和水玻璃含量的质量分数分别达到２６％和１３％（ＭｇＣｌ２和水玻璃含量的质量分数为３０％和１５％）时，试样的含水率就能保持大于５％（质量分数）；（３）ＣａＣｌ２或ＭｇＣｌ２与水玻璃复合后，其粘尘功能进一步增强，而且其溶液的弱酸性得到进一步降低。     

Ca_8Mg（SiO_4）_4Cl_2中Ce~（3＋）的光谱与晶体学格位

合成了新型蓝色光致发光材料Ｃａ８Ｍｇ（ＳｉＯ４）４Ｃｌ２：Ｃｅ（３＋），并对其进行了光谱测试．分析了Ｃｅ（３＋）在Ｃａ８Ｍｇ（ＳｉＯ４）４Ｃｌ２晶体中应占据的晶体学格位．测试结果表明，在紫外光激发下，Ｃａ８Ｍｇ（ＳｉＯ４）４Ｃｌ２：Ｃｅ（３＋）的发射光谱为一峰位在４１０ｎｍ～４２５ｎｍ之间的宽谱带，经分析确认作为发光中心的Ｃｅ（３＋）占据Ｃａ８Ｍｇ（ＳｉＯ４）４Ｃｌ２晶体中多面体八配位的Ｃａ（Ⅱ）格位．     

钢包精炼渣成分的最优化

本文用正交设计方法对用于钢包精炼的ＣａＯ－ＳｉＯ２－Ａｌ２Ｏ３－ＭｇＯ－ＣａＦ２渣系成分进行优化，试验表明影响炉渣泡沫稳定性能的因素依次为碱度，ＣａＦ２，Ａｌ２Ｏ３和ＭｇＯ的含量，最佳的精炼渣组成为：ＣａＯ３９．３％，ＳｉＯ２１９．７％，Ａｌ２Ｏ３２５％，ＭｇＯ６％，ＣａＦ２１０％（Ｂ＝２）     

斑节对虾组织的原代培养

选用Ｌ－１５,添加１０％～２０％ＦＢＳ,渗透压用ＮａＣｌ等调节,ｐＨ７．０,在２８℃下,原代培养斑节对虾的多种组织,发现淋巴器官,造血器官和血淋巴的组织细胞在较宽范围的培养基渗透压条件下能贴壁生长形成细胞单层．每升培养基添补７．５０ｇＮａＣｌ,０．３２ｇＫＣｌ,１．０２ｇＭｇＣｌ２６Ｈ２Ｏ,０．４９ｇＭｇＳＯ４７Ｈ２Ｏ,２．００ｇＣａＣｌ２２Ｈ２Ｏ和０．３０ｇ葡萄糖调节渗透压时,上述３种组织细胞生长最好     

CaCl2*6H2O-MgCl2*6H2O多温截面的研究

用步冷曲线法研究并绘制了ＣａＣｌ２·６Ｈ２Ｏ－ＭｇＣｌ２·６Ｈ２Ｏ多温截面图,实验显示该截面有两个四相转熔反应,其转熔温度分别为２５．０℃和２２．０℃．结果表明,ＣａＣｌ２·６Ｈ２Ｏ－ＭｇＣｌ２·６Ｈ２Ｏ混合盐可用于低温相变储热．     

细晶氧化铝瓷研究

实验研究ＣａＯ－ＭｇＯ－ＳｉＯ２熔块对Ａｌ２Ｏ３瓷烧结的作用结果表明：在２０％ｗｔ％ＣａＯ，３０ｗｔ％ＭｇＯ，５０ｗｔ％ＳｉＯ２区域附近的熔块能很好地促进Ａｌ２Ｏ３瓷的低温烧结；除了第２相对晶界的钉扎作用以及固溶作用外，ＭｇＯ在烧结中的作用能维持ＣａＯ／ＳｉＯ２比，即维持烧结系统中的液相量；Ｌａ２Ｏ３，Ｓｍ２Ｏ３能使Ａｌ２Ｏ３瓷的烧结温度下降大约３０℃，其表面显微结构也有所改善。     

盐类对光解水放氢反应的影响

报道ＮａＣｌ，ＫＣｌ，ＭｇＣｌ２和ＣａＣｌ２对光解水放氢影响的某些结果．在所研究的ＴｉＯ２，Ｋ２ＰｔＣｌ６，ＥＤＴＡ酸（或还原铁粉）的反应系统中，ＭｇＣｌ２，ＣａＣｌ２对产氢的影响大于ＮａＣｌ和ＫＣｌ，ＮａＣｌ对产氢的影响大于ＫＣｌ．与没有盐类存在时相比，加入盐类可使放氢增至２倍以上．海水中的Ｋ＋，Ｎａ＋，Ｃａ＋＋和Ｍｇ＋＋浓度均落在对反应速度变化较敏感的浓度区域，而且用ＮａＣｌ，ＫＣｌ，ＭｇＣｌ２和ＣａＣｌ２４种盐类模拟海水，也可以使放氢量提高至２倍以上，提示这类反应可能在生物进化中的重要地位．     

CaO,SiO,Al2O3和MgO四元渣系脱硫

根据石钢生产条件,研究了ＣａＯ、ＳｉＯ２、Ａｌ２Ｏ３和ＭｇＯ四元渣系脱硫性能,实验结果表明：炉渣碱度在１．１０－１．２０之间,ＭｇＯ≯１０％,Ａｌ２Ｏ３≯１５％时能获得最佳的脱硫效果。     

电熔再结合镁铬砖的精炼渣浸实验研究

用试样旋转法在１６００℃下实验研究了ＣａＯ－ＳｉＯ２－Ａｌ２Ｏ３－ＭｇＯ－ＣａＦ２（３％）型精炼渣组成对电熔再结合镁铬砖的侵蚀影响，渣浸试样电镜分析的结果表明，随渣碱度（ＣａＯ／ＳｉＯ２）的增大，试样的侵蚀增加；碱度大于１．８时，试样在冷却过程中粉化，由于尖晶石保护层的生成，渣中Ａｌ２Ｏ３含量的增加能减少侵蚀，随渣中ＭｇＯ含量的增加，试样的侵蚀减少，在此基础上，讨论了对提高镁铬砖炉衬有利的炉外精炼     

CaO-SiO_2-MgO-H_2O体系的热力学研究

本文研究了ＣａＯ－ＳｉＯ２－ＭｇＯ－Ｈ２Ｏ体系的热力学,结果表明：ＳｉＯ２ 优先与ＣａＯ水热形成水化硅酸钙,多余的ＳｉＯ２ 才会与ＭｇＯ直接水热形成水化硅酸镁。当没有ＳｉＯ２ 时,ＭｇＯ才会水化形成Ｍｇ（ＯＨ）２。     

MgO/MgCl_2摩尔比与添加剂对菱苦土制品强度的影响

论述通过正交试验法对MgO和氯化镁摩尔比以及硅粉对菱苦土磨具强度的影响规律.在菱苦土结合剂中,活性MgO含量对制品的性能影响极大,同样,合适的卤水密度也很重要,MgCl2浓度过高时,过多的MgCl2与MgO生成复盐,磨具体积收缩产生裂纹.MgCl2浓度过小时,材料硬化不充分,强度不够.当MgO/MgCl2的摩尔比为4～6时,磨具能获得最大的强度,此时主要的微观结构是5MgO.MgCl2.8H2O.硅粉能与氯氧镁水泥中的MgO发生化学反应,形成硅酸盐凝胶,可提高磨具的致密度和强度,改善耐水性.     

New pyrometallurgical process of EAF dust treatment with CaO addition

The non-carbothermic zinc pyrometallurgical processing of electric arc furnace (EAF) dust was investigated on a laboratory scale. The main objective of this process was to convert highly stable zinc ferrite (ZnFe₂O₄), which accounts for more than half of total zinc in the EAF dust, into ZnO and Ca₂Fe₂O₅ by CaO addition. The EAF dust was mixed with CaO powder in various ratios, pressed into pellets, and heated in a muffle furnace in air at temperatures ranging from 700 to 1100℃ for a predetermined holding time. All ZnFe₂O₄ was transformed into ZnO and Ca₂Fe₂O₅ at a minimum temperature of 900℃ within 1 h when sufficient CaO to achieve a Ca/Fe molar ratio of 1.1 was added. However, at higher temperatures, excess CaO beyond the stoichiometric ratio was required because it was consumed by reactions leading to the formation of compounds other than ZnFe₂O₄. The evaporation of halides and heavy metals in the EAF dust was also studied. These components could be preferentially volatilized into the gas phase at 1100℃ when CaO was added.     

准东煤掺烧油页岩后矿物质的转化迁移研究

研究准东煤和油页岩混合燃料在100 MW锅炉燃烧过程中的矿物质演变规律,解决火力发电厂大比例和大规模掺烧准东煤引起的沾污和结渣问题。对现场试验收集的入炉煤、飞灰和炉渣样品进行化学分步萃取、XRD、灰成分等分析。结果表明,在100 MW机组锅炉燃用准东煤掺混15%油页岩的混合燃料,油页岩灰分中镶嵌或者包裹的可燃物燃烧后,炉渣将形成多孔和酥松形态,从炉渣的结构方面缓解准东煤引起的炉膛结渣问题。掺混15%油页岩后,燃烧过程中碱金属和碱土金属基本不挥发,炉渣中Na_2O、MgO、CaO和SO_3的含量较准东煤分别降低了2.07%、3.42%、15.08%和10.5%;飞灰中Na_2O、MgO、CaO和SO_3的含量也较准东煤明显下降。同时炉渣和飞灰中的钠主要为钠长石,钾在掺烧前后都以KAl_2(Si_3Al)O_(10)(OH)_2存在。在炉膛中碱土金属的碳酸盐和硫酸盐分解后,大部分转化为钙黄长石。油页岩通过降低碱金属和碱土金属含量及改变其存在形态,解决了准东煤引起的炉膛结渣和受热面沾污的问题。     

氧化物固体溶液对PVC的阻燃性能影响

讨论了固体溶液阻燃剂对 PVC材料的阻燃作用 ,对几种氧化物的混合物高温灼烧后对 PVC材料进行阻燃处理进行了分析 ,通过 DTA- TG、氧指数和机械性能等测试方法测定其性能。实验证明添加固体溶液阻燃剂可以使 PVC材料的氧指数和剩炭率比未添加固体溶液阻燃剂的 PVC材料提高 ,分解温度和热降解反应活化能降低。并且添加少量的固体溶液阻燃剂就能取得较好的阻燃效果 ,并不影响材料的机械性能。     

水热条件下CaO—MgO—SiO_2—H_2O体系中反应物的竞争与产物的转化机制

本文研究了 Ca O—Mg O—Si O2 — H2 O体系的水热反应特性。结果表明 :在 Ca O— Mg O—Si O2 一 H2 O系统中 ,Ca O优先与 Si O2 反应生成水化硅酸钙 ,Mg O部分固溶于水化硅酸钙中 ,部分生成 Mg( OH) 2 ,部分与剩余的 Si O2 反应生成水化硅酸镁 ;Mg O固溶时 ,可促进托勃莫来石向硬硅钙石转化 ,不固溶 ,则其转化温度提高     

用于煤矿防灭火的高吸水树脂的合成与吸水性能研究

以蒙脱土、丙烯酸为主要原料,采用溶液聚合法合成了超强吸水性复合树脂.讨论了蒙脱土加入量、引发剂加入量、交联剂的用量、丙烯酸的中和度对高吸水性复合树脂吸水倍率的影响,优化了该复合材料吸自来水性能的配方,即蒙脱土添加量为40％,单体的中和度为80％,交联剂用量为0.08％,引发剂用量为0.15％.在此配方下制备的复合材料吸自来水倍率达到156倍.傅里叶红外光谱图研究证实蒙脱土能够有效地与高聚物结合,不但提高了树脂的保水能力和耐热性,而且大大降低了树脂成本.     

掺CeO_2的MgO－CaO系中CaO和MgO的晶粒生长动力学

研究了ＭｇＯ－ＣａＯ系耐火材料中主要氧化物ＣａＯ和ＭｇＯ在高温下的晶粒生长动力学，发现ＣｅＯ２的存在降低了ＣａＯ和ＭｇＯ的晶粒生长活化能，提高了结构基元的扩散速率，促进了ＣａＯ和ＭｇＯ晶粒的生长，从而揭示了掺ＣｅＯ２的ＭｇＯ－ＣａＯ系耐火材料抗水化性提高的本质     

高强度矿渣胶凝材料改性的研究

研究矿渣的粉磨细度，激发剂的掺量，改性剂的种类与掺量对高强度矿渣胶凝材料的干燥收缩性能及其强度的影响。研究表明，掺加9－10％的Na2SiO2激发剂和10％左右的硅酸盐水泥，控制适当的粉磨细度，可以使高强度矿渣胶凝材料的干燥收缩率降低到与硅酸盐水泥相近的程度，并且强度提高，达到了综合改性的目的。其水化产物都是含有少量Na2O,MgO的铝硅酸钙凝胶。