7022铝合金搅拌摩擦焊焊接区的组织与力学性能

以厚度为10mm的7022铝合金为对象进行搅拌摩擦焊接试验,研究了搅拌摩擦焊工艺参数对接头组织和力学性能的影响.结果表明:焊接接头具有良好的力学性能,在搅拌头转速为400r/min、焊接速度为100mm/min时,7022铝合金的搅拌摩擦焊接头抗拉强度和屈服强度分别达615MPa和533 MPa,均超过了母材;焊接接头的显微硬度略低于母材;断口形貌分析表明,7022铝合金搅拌摩擦焊接件拉伸断裂为韧性断裂.     

搅拌摩擦焊工艺参数对超薄铝合金板/高强钢搭接焊接头组织及性能的影响

采用复合式搅拌头对0.7 mm厚6010铝合金板和2.0 mm厚DP600钢板进行搅拌摩擦搭接焊,在不磨损搅拌头的同时获得了性能优良的焊接接头。研究了不同焊接工艺参数对铝合金/高强钢焊接接头界面结构及力学性能的影响。结果表明,在搅拌针未进入钢板的情况下,顶锻力是搅拌摩擦焊过程中的关键参数,存在一个实现铝合金/高强钢异种材料搅拌摩擦搭接焊的最小顶锻力。在恒定顶锻力5.0 kN,转速1 200 r/min的焊接条件下得到了最佳性能的焊接接头,拉伸强度达到260 MPa,且断裂发生在铝合金母材区。铝合金/高强钢界面存在一层厚2.0 μm的过渡层。     

35#钢摩擦焊多级加压对轴向缩短量及焊后组织的影响

以35#钢为焊接母材,应用连续驱动摩擦焊接方式,采用正交试验的方法并经过极差分析后,探究了中等直径焊件多级加压方式下各工艺参数对轴向缩短量的影响规律,并对焊接接头显微组织及显微硬度进行了分析.实验结果表明,对焊件轴向缩短量影响程度依次为:二级摩擦位移、二级摩擦压力、一级摩擦压力、一级摩擦位移;观察焊接接头显微组织发现焊缝处得到了细小的铁素体与珠光体相互融合的优良组织,焊缝组织达到正火态;通过对焊件焊缝及热影响区显微硬度测试后可以得出,各焊件焊缝的显微硬度值明显高于母材,不同焊接工艺参数组合方式对焊件接头晶粒存在一定影响并直接影响焊件接头硬度.     

2219铝合金焊缝组织及其对力学性能的影响

针对厚度为4 mm的2219-T87铝合金进行惰性气体钨极保护焊(Tungsten inert gas arcwelding,TIGAW)试验研究,分析焊缝的组织结构及力学性能。拉伸试验结果显示,接头试样平均屈服强度为母材的49.3%,平均抗拉强度为母材的67.8%,断后伸长率为母材的18.5%。测试了焊接试样各区域的显微硬度,测试结果表明焊缝区域硬度高于其他部位,其中熔合线和热影响区之间的显微硬度最低,同时焊接试样的整体区域硬度均比母材低。对焊接试样进行腐蚀试验,发现接头焊缝区抗腐蚀能力明显强于母材。要提高2219铝合金焊接性能,需改进焊接工艺,减少熔合区以及热影响区的粗大晶粒的形成,解决CuAl2相的偏析等问题。     

2219-T6静轴肩辅助搅拌摩擦焊组织与性能分析

为探究安装外部静止轴肩对搅拌摩擦焊接头成形和力学性能的影响,采用自主研制的外部静止轴肩辅助搅拌摩擦焊(Non-Rotational Shoulder Assisted Friction Stir Welding,NR-SA-FSW)焊具对2219-T6铝合金4 mm厚板材进行对接焊试验,观察焊后接头表面成形情况.采用拉伸和显微硬度试验对焊缝的力学性能进行测试,并与相同焊接参数下的搅拌摩擦焊(Friction Stir Welding,FSW)进行对比分析.使用金相显微镜和场发射扫描电镜对接头焊缝组织进行分析.结果表明,由于静止轴肩的平动刮擦作用,NRSA-FSW相比FSW,接头表面更加光滑,无鱼鳞纹、飞边以及接头减薄现象.NRSA-FSW接头相比于FSW接头软化区有所增加,接头显微硬度分布更加均匀.NRSA-FSW接头平均抗拉强度323 MPa,达到母材的72％,抗拉强度同FSW相近.NRSA-FSW焊核呈"U"状,焊缝组织无缺陷.接头拉伸试验在焊核区(Nuggest-Zone,NZ)处断裂,为韧性断裂.     

微弧氧化处理提高AZ31B镁合金搅拌摩擦焊焊缝的耐蚀性

为提高镁合金焊接接头的耐蚀性,对6mm厚的AZ31B板材搅拌摩擦焊焊缝进行微弧氧化处理,并研究焊缝的微观组织、截面显微硬度及其微弧氧化前后的耐蚀性.结果表明:接头的微观组织明显分为3个区域:焊核区、热机械影响区及热影响区,并且接头整体硬度低于母材,焊接时焊核部位出现软化现象,导致其硬度最低.盐水浸泡实验和电化学测试表明,微弧氧化前焊缝的耐蚀性低于母材,经过微弧氧化处理后,焊缝表面形成一层致密光滑的陶瓷膜,极大提高其耐蚀性.并且,经同工艺微弧氧化处理后,焊缝表面微弧氧化膜要比母材的微弧氧化膜厚.     

大端面铝与钢的摩擦焊焊缝组织及性能

以铝和钢为焊接材料,采用连续驱动摩擦焊技术对大截面铝与钢异种金属进行焊接试验.通过显微组织、电子探针、X射线衍射、力学性能分析及微区硬度测试检测焊接性能.结果表明:大截面铝与钢之间具有良好的摩擦焊接性,焊接接头强度等于或高于铝基材;焊接接头在近缝区发生晶粒细化,在粘塑层发生原子扩散,形成扩散层.     

冷却条件对2519A铝合金搅拌摩擦焊焊缝性能的影响

采用搅拌摩擦焊焊接厚度为2.75 mm的2519A铝合金板材。分别研究在空气和水流中冷却对焊接性能和焊缝组织的影响。实验结果表明:在旋转速度为2 700 r/min,焊接速度为60 mm/min条件下,水冷焊接得到美观并无明显缺陷的接头,提高了接头强度,抗拉强度达到340 MPa;在水冷条件下,热影响区的范围变窄,热影响区平均硬度提高,焊核区晶粒粒度比空冷条件下的更加小,硬度几乎呈直线分布;而在空冷条件下,焊核区硬度呈先上升后下降趋势,变化明显,水冷焊核区平均硬度低于空冷条件下平均硬度,这是因为空冷焊接能够提高固溶度并促进随后的时效发生。     

铝合金/不锈钢冷金属过渡熔-钎焊的接头性能

以ER4043(AlSi5)型焊丝作为填充金属,利用冷金属过渡熔-钎焊技术焊接异种材料6061铝合金与304奥氏体不锈钢,研究了不同焊接速度条件下焊接接头界面化合物层的物相组成及其抗拉强度.结果表明:通过优化焊接工艺参数能够得到连续均匀的焊缝,而且当焊接速度达到420mm/min时,焊缝表面的成形质量最好;在焊接接头的铝/钢界面形成了一定厚度的Fe-Al化合物层,其主要成分为Fe_2Al_5及FeAl_3相;焊接接头的抗拉强度为40 MPa,焊接接头的断裂发生于铝/钢的界面处,断口呈脆性断裂.     

厚板搅拌摩擦焊接头的组织与性能

针对厚度为30mm的1060铝合金板材搅拌摩擦焊对焊连接,采用在试板上加工盲孔的方法减少了焊接时大量的飞边.分析了焊缝的组织与力学性能.结果表明:1060铝合金厚板搅拌摩擦焊焊接成形良好.沿厚度方向上的抗拉强度呈先下降后上升的趋势,热影响区与热机影响区之间金属流动性不同,存在明显的结合线,由于该区域组织存在不连续性导致应力集中,拉伸试样的断裂位置主要存在于热影响区与热机影响区的交界处.在焊接接头上部与中部的后退侧的显微硬度高于前进侧,而下部后退侧的显微硬度低于前进侧;焊缝中部的显微硬度随着厚度增大而减小得比较明显,而前进侧与后退侧的减小程度比较小.     

搅拌摩擦焊、搅拌振动摩擦焊和钨极惰性气体焊接AA6061-T6接头的组织和力学特性对比研究

This study compared the microstructure and mechanical characteristics of AA6061-T6 joints produced using friction stir welding (FSW), friction stir vibration welding (FSVW), and tungsten inert gas welding (TIG). FSVW is a modified version of FSW wherein the joining specimens are vibrated normal to the welding line during FSW. The results indicated that the weld region grains for FSVW and FSW were equiaxed and were smaller than the grains for TIG. In addition, the weld region grains for FSVW were finer compared with those for FSW. Results also showed that the strength, hardness, and toughness values of the joints produced by FSVW were higher than those of the other joints produced by FSW and TIG. The vibration during FSW enhanced dynamic recrystallization, which led to the development of finer grains. The weld efficiency of FSVW was approximately 81%, whereas those of FSW and TIG were approximately 74% and 67%, respectively.     

Microstructure and mechanical characteristics of AA6061-T6 joints produced by friction stir welding,friction stir vibration welding and tungsten inert gas welding: A comparative study

This study compared the microstructure and mechanical characteristics of AA6061-T6 joints produced using friction stir welding(FSW), friction stir vibration welding(FSVW), and tungsten inert gas welding(TIG). FSVW is a modified version of FSW wherein the joining specimens are vibrated normal to the welding line during FSW. The results indicated that the weld region grains for FSVW and FSW were equiaxed and were smaller than the grains for TIG. In addition, the weld region grains for FSVW were finer compared with those for FSW.Results also showed that the strength, hardness, and toughness values of the joints produced by FSVW were higher than those of the other joints produced by FSW and TIG. The vibration during FSW enhanced dynamic recrystallization, which led to the development of finer grains.The weld efficiency of FSVW was approximately 81%, whereas those of FSW and TIG were approximately 74% and 67%, respectively.     

焊后多次正火对超细晶粒钢热影响区组织与硬度的影响

为研究400 MPa级超细晶粒钢焊接接头热影响区粗晶区的晶粒细化行为,对其空冷与水冷接头均进行了3次焊后正火热处理.组织观察表明:第1次正火后粗晶区晶粒明显细化,但细晶区和母材区的晶粒均比正火前的稍微粗大,第2次与第3次正火并不能进一步细化晶粒;冷却条件对热影响区组织的影响并不十分显著.显微硬度测试表明:第1次正火使接头硬度大幅度降低,甚至低于母材的原始硬度,后续正火对硬度的影响较小;在所有试样中,仅水冷接头第1次正火后的热影响区硬度与原始母材及母材区的硬度接近.由于焊后多次正火并不能使热影响区晶粒进一步细化,反而使其有粗化与软化的趋势,故应避免焊后多次正火处理.     

紫铜的搅拌摩擦焊工艺与接头性能分析

搅拌摩擦焊是一种新型固相塑性连接方法,它的出现为铜的焊接提供了一种新的工艺.对紫铜的搅拌摩擦焊工艺进行了研究,通过工艺试验,对其焊缝成形、接头组织形态及其力学性能进行了分析.研究结果表明,搅拌摩擦焊接紫铜时应选用搅拌头旋转速度在400~700 r/min,焊接速度为35~60 mm/min;从显微组织角度,由于接头主要发生了动态再结晶,焊接接头没有热力影响区,而是三个区,即焊核区、热影响区、母材区.研究还发现用搅拌摩擦焊得到的铜接头出现了明显的软化现象,接头的机械性能比母材低,但比熔化焊得到的接头性能要高,其平均抗拉强度可达到母材的80%.     

高速列车车厢用的铝合金板焊接接头的组织与性能

利用光学显微镜和透射电子显微镜研究了国产7020铝合金熔化极惰性气体保护焊(MIG)接头的微观组织结构,并对接头的力学性能进行研究.结果表明,接头的硬度以焊缝中心线为轴呈对称分布,且焊缝中心为接头的最薄弱环节;焊缝区为典型的树枝状晶的铸造组织.在熔合区,焊缝一侧为沿散热方向排列的柱状晶,另一侧为细小的等轴晶组织.热影响区内,仍可见纤维状加工痕迹,部分析出相固溶到基体中;强化相的粗化,是热影响区内出现软化区的主要原因.国产7020铝合金焊接接头强度达到欧洲标准.     

Ca对AZ31镁合金CO_2激光焊接接头组织和性能的影响

采用添加填充材料的CO2激光焊接工艺对AZ31镁合金薄板进行焊接,研究了不同Ca含量对焊缝金属的显微组织和力学性能的影响.结果表明:当激光功率为1 500W,焊接速度为3 m/min时,AZ31镁合金CO2激光焊接的焊缝金属中添加一定量的σCa0.19%元素,可以得到成分相对较均匀、组织细小的焊缝.当填充带材为AZC04(焊缝中Cσa=0.19%)时,焊缝区晶粒相对细小,析出相细小弥散,此时焊接接头的力学性能最优,焊接效率基本可达到100%.     

7075-T6合金超声辅助搅拌摩擦焊接头搅拌区组织与力学性能

搅拌区的金属流动不充分容易导致轴肩影响区与搅拌针影响区之间的过渡区出现疏松缺陷并恶化接头的力学性能.在不同焊接参数条件下,对7075-T6铝合金分别进行常规搅拌摩擦焊接(FSW)和超声辅助搅拌摩擦焊接(UAFSW),研究了超声振动对接头搅拌区的金属流动行为、微观组织特征和力学性能的影响.结果表明:相同焊接参数下,UAFSW接头搅拌区的力学性能均优于FSW接头.焊接参数为1000r/min-110mm/min 的UAFSW接头搅拌区的抗拉强度和延伸率最高,分别达到515MPa和17.3%.在搅拌摩擦焊接过程中施加轴向超声振动可以显著降低搅拌区金属的屈服应力和流变应力,促进塑化金属沿板厚方向的流动.消除搅拌区中过渡区的疏松缺陷,并细化微观组织,是接头力学性能提高的主要原因.     

焊接工艺对6005A-T6铝合金焊接接头晶间腐蚀性能的影响

采用激光填丝焊（laser wire filler welding,LFW）、冷金属过渡（cold metal transfer,CMT）焊和熔化极惰性气体保护（melt inert-gas,MIG）焊方法对6005A-T6铝合金板材进行焊接,研究不同焊接方法得到的焊接件的接头处、焊缝区、热影响区的抗晶间腐蚀能力。研究结果表明：在相同晶间腐蚀环境下,LFW接头处较CMT焊、MIG焊接头处的抗晶间腐蚀能力强;CMT焊焊缝区较MIG焊焊缝区的抗晶间腐蚀能力强,但热影响区抗晶间腐蚀的能力相反;3种接头各自热影响区的抗晶间腐蚀能力均弱于各自焊接接头处和焊缝区的抗晶间腐蚀能力。     

铝与奥氏体不锈钢的火焰钎焊

为改善铝和不锈钢的焊接接头性能,在奥氏体不锈铜（1Crl8Ni9Ti）的表层热浸镀一层ZL102铝合金,然后采用搭接的形式,应用火焰钎焊工艺进行纯铝（1060）板与奥氏体不锈钢板的焊接。利用金相显微镜和扫描电镜分析焊接接头的微观组织,并用显微维氏硬度仪和万能实验机床测定其显微硬度和拉伸性能。结果表明,通过不锈钢表面热浸镀铝,可实现铝与奥氏体不锈钢的火焰钎焊。在不锈钢／纯铝钎焊焊缝中存在不锈钢／热浸镀铝层、热浸镀铝层／钎缝、钎缝／纯铝三个界面。钎焊接头强度取决于各界面的连接质量。热浸镀铝层／钎缝界面是整个接头中最薄弱的界面,剪切断裂均发生在该区域。钎焊接头各区域中,热浸镀铝区硬度最高,达到99．4MPa。     

Effects of thermomechanical treatments on the microstructures and mechanical properties of GTA-welded AZ31B magnesium alloy

Thermomechanical treatments were carried out to improve the properties of AZ31B joints prepared by gas tungsten arc welding. The microstructures of the joints were studied by optical microscopy and scanning electron microscopy with energy-dispersive spectrometry. Tensile tests and hardness tests were performed to investigate the effects of thermomechanical treatments on the mechanical properties of the joints. It is found that the thermomechanical-treated joints show superior mechanical properties against the as-welded joints, and their ultimate tensile strength can reach more than 92% of the base material. This mainly attributes to the formation of fine equiaxed grains in the fusion zone. After thermomechanical treatments the dendrites are transformed to fine spherical grains, and the dendritic segregation can be effectively eliminated.