锦纶66包芯纱牛仔面料开发

使用锦纶66纤维开发高性能、高品质的牛仔面料,以粘胶为外包纤维,锦纶66或氨纶为芯丝制成36.4和28.0 tex的包芯纱为纬纱,使用剑杆织机使其与36.4和28.0 tex的纯棉纱线进行交织,制成牛仔面料。对锦纶66包芯纱和氨纶包芯纱所织制的6种牛仔面料进行色牢度、耐磨性、强力、弹性回复性、折皱回复性和弯曲性能等性能测试并进行对比分析,发现锦纶66包芯纱牛仔面料的弹性达到氨纶包芯纱牛仔面料的弹性水平,且其强力和柔软度更佳。以粘胶/锦纶66(3.33 tex/10 F)包芯纱织制面料比粘胶/锦纶66(3.33 tex/34 F)强力更大、弹性回复性更好,且更柔软。同时,采用36.4 tex纱线所织制的面料的强力、弹性和折皱回复性更好,但28.0 tex纱线所织制的面料更柔软。     

PTT纱线的弹性对无缝内衣织物服用性能的影响

为了了解聚对苯二甲酸丙二醇酯(PTT)及PTT/聚对苯二甲酸乙二醇酯(PET)纱线对织物弹性性能的影响,选择PTT纱线及PTT/PET双组分纱与无缝内衣领域常用的锦纶和两种锦纶/氨纶包芯纱共6种纱线,对比其在沸水处理前后的强力-伸长特征以及定伸长弹性特征,并对比这6种纱线组合编织成的11种无缝内衣织物的弹性回复率.采用显著性检验的数学方法证明含有PTT的双组分纱线的弹性回复率与锦纶/氨纶包芯纱相似,PTT纱线作为无缝内衣织物的底纱较适宜,用其编织的无缝内衣产品的保形性及耐疲劳性优良.     

PTT经编弹力泳装面料弹性的研究

为了解新型聚酯纤维PTT(聚对苯二甲酸丙二醇酯)经编弹力泳装面料的弹性,用PTT纤维织制的经编弹力泳装面料,与锦纶(PA)和涤纶(PET)织制的经编弹力泳装面料进行对比研究.实测了它们15N和5次及25N和9次定负荷的拉伸性能,比较了它们的弹性回复率、塑性变形率和拉伸弹性伸长率;为进一步寻找3种面料的弹性回复率变化规律,列出了它们弹性回复率的回归方程式.结果显示,PTT经编弹力泳装面料断裂强力较小、伸长率较大,具有优异的弹力回复性,是制作泳装的理想面料.     

PBST/棉包芯纱的拉伸回复性能

通过对不同捻度和混纺比的PBST(聚丁二酸-共-对苯二甲酸丁二醇酯)与棉包芯纱拉伸回复性能的分析,探讨了捻度和混纺比对PBST包芯纱回弹性能的影响.在捻度相同、PBST纤维相同的条件下,PBST包芯纱的拉伸弹性回复性随着棉纤维的增加而减少;在纱线混纺比相同时、PBST包芯纱的拉伸弹性回复率随着捻度的增加呈先增后降的趋势.采用捻度为500捻/m和40/60的混纺比纺制PBST/棉包芯纱时,纱线的拉伸弹性回复性能较好,并且在小变形下,PBST包芯纱能保持良好的拉伸回复性.这对PBST包芯纱的开发和应用具有一定的参考价值.     

PTT/PBT共混体系结晶及晶貌形态的研究

通过WAXD，POM对聚对苯二甲酸丙二醇酯（PTT）与聚对苯二甲酸丁二醇酯（PBT）共混物．在非等温条件下结晶度及晶貌形态进行了研究。结果表明，PTT／PBT共混体系的结晶度随着组分含量变化而变化。当PTT，PBT的组分相差很大时，其结晶性能好；当PTT，PBT的组分接近时．其结晶性能差。等温结晶时问及组分含量对晶体的生长有一定的影响。     

Fe-Mn-Si基形状记忆合金的记忆性能

研究了Ｆｅ－Ｍｎ－Ｓｉ合金和Ｆｅ－Ｍｎ－Ｓｉ－Ｃｒ－Ｎｉ合金的记忆性能—回复率和回复力．结果表明：Ｃｒ，Ｎｉ元素明显提高回复率和回复力．两种合金的回复率随淬火温度升高而增大，在７００～８００℃达到最大值，以后随淬火加热温度进一步升高而降低．回复率随预变形量增加而降低．在预变形—加热回复的循环过程中，回复率发生降低，３０次后趋于稳定．预变形量小于２％时，回复力随预变形量增加而增大；预变形量大于２％后，回复力增加缓慢     

聚丙烯拉伸丝结构和加弹丝变形效果的关系

本文研究了聚丙烯拉伸丝结构与高弹丝卷曲弹性的关系,发现拉伸丝的取向、结晶度以及结晶型式均与高弹丝的卷曲性能有关,其中尤以晶型更为重要。较低的结晶度、适中的取向和不稳定的酝晶结构是提高卷曲弹性的必要条件。同时,还对加弹前后的纤维结构和性能作了分析比较。     

摩擦包芯纱织物性能的研究

章对棉包涤纶长丝摩擦纱、棉包锦纶高弹丝摩擦纱、棉包锦纶全牵伸丝摩擦纱以及棉包粘胶长丝摩擦纱的平纹织物的性能进行了试验研究，并将它们与纯棉环锭纱和纯棉摩擦纱的平纹织物的性能进行了比较和分析。研究结果表明，锦包涤纶长丝摩擦纱织物和棉包锦纶高弹丝摩擦纱织物在服用、舒适性等方面均优于环锭纱织物。这两种摩擦包芯纱织物作为服用织物将具有良好的发展前景。     

摩擦包芯纱织物性能的研究

文章对棉包涤纶长丝摩擦纱、棉包锦纶高弹丝摩擦纱、棉包锦纶全牵伸丝摩擦纱以及棉包粘胶长丝摩擦纱的平纹织物的性能进行了试验研究,并将它们与纯棉环锭纱和纯棉摩擦纱的平纹织物的性能进行了比较和分析。研究结果表明,棉包涤纶长丝摩擦纱织物和棉包锦纶高弹丝摩擦纱织物在服用、舒适性等方面均优于环锭纱织物。这两种摩擦包芯纱织物作为服用织物将具有良好的发展前景。     

一体化编织型血管覆膜支架的压缩性能

采用新型编织技术制备了螺旋平行分布和交叉分布的4种不同结构的一体化血管覆膜支架,研究支架不同结构与其平面压缩性能的关系,考察不同压缩测试条件(压缩和回复速率以及压缩停滞时间)对支架的径向压缩强力、应力松弛率和弹性回复率的影响,综合评价其压缩性能.结果表明:小节距同向螺旋平行分布血管覆膜支架(A2)具有压缩强力较高、应力松弛率最小、弹性回复率高,故其压缩性能最好;随着压缩停滞时间的延长,大节距同向螺旋平行分布血管覆膜支架(A1)和交叉分布血管覆膜支架(B1和B2)的应力松弛率明显增加,且弹性回复率降低.     

纳米改性氢氧化铝与包覆红磷协效阻燃尼龙66的研究

文中分别研究了纳米改性氢氧化铝 (CG-ATH)单独使用以及与包覆红磷协效阻燃尼龙66(PA66 )复合体系的阻燃性能和力学性能。将纳米CG-ATH和包覆红磷以不同比例添加到PA6-6中,制得复合材料。用氧指数法测定了复合体系的阻燃性能,此外还进行了拉伸和冲击性能测试。结果表明,包覆红磷与纳米CG-ATH具有一定的协同效应,当复合材料中PA66、包覆红磷和纳米CG-ATH的质量比为100∶13∶20时,该复合体系的氧指数为33,而只PA66和纳米CG-ATH的质量比为100∶40的 PA66复合体系的氧指数29.5,但是100g PA6 6中,只添加15g包覆红磷时,该复合体系的氧指数只有27,该协效阻燃体系的拉伸强度为79.3MPa,拉伸弹性模量为2182.3MPa,断裂伸长率为5.9% ,冲击强度为4.5kJ/m² 。因此,纳米改性氢氧化铝与包覆红磷的协同效应,实现了在无机阻燃剂添加量相对较少且保证 PA66本身力学性能的前提下,大幅度改善材料阻燃性能的要求。     

确定PTT/PET并列复合纤维卷曲结构的材料参数

通过实测3种不同横截面形状的PTT(聚对苯二甲酸丙二醇酯)/PET(聚对苯二甲酸乙二醇酯)自卷曲纤维的拉伸曲线和两组分在横截面中的面积分布,得到PTT和PET两组分材料的弹性模量比为0.333.由Denton的曲率计算模型推导得到3种特殊截面的自卷曲纤维的曲率表达式,结合实测的卷曲曲率,求得PTT和PET两组分的热收缩率差是在7%～10%之间.最后,用数值模拟方法考查了这3种横截面的自卷曲纤维的卷曲曲率随着两组分收缩率差、弹性模量比的变化关系,得到不同横截面形状及材料参数对PTT/PET自卷曲纤维卷曲曲率的影响.     

PTT/PBT共混体系相容性

通过扫描量热仪DCS,X-射线衍射仪WAXD对聚对苯二甲酸丙二醇酯（PTT）与聚对苯二甲酸丁二醇酯（PBT）共混物的相容性进行了研究。结果表明,PTT/PBT的共混体系两组分在无定型区具有相容性,而在晶区两组分分别结晶,形成非均相体系。     

Effect of Knitting Process on Elastic Property of Polyethylene Terephthalate (PET)/Polybutylene Terephthalate (PBT) Warp Knitted Fabric

This study investigated the elastic elongation and elastic recovery of the elastic warp knitted fabric made of polyethylene terephthalate( PET) and polybutylene terephthalate( PBT)filament. The effect of knitting parameter on the elasticity of PBT /PET warp knitted fabric was analyzed. The increase of drawing density( from 16 to 26 courses per centimeter( CPC)) on machine resulted in the decrease of elongation at the weft direction. But,the elongation at the warp direction fluctuated as drawing density increasing. The yarn run-in speed influenced the elongation of PET /PBT warp knitted fabric as well. When the yarn run-in speed of GB1( front bar) was kept a constant,the increase of GB2( back bar) yarn run-in speed caused the gradual enhancement of the elastic elongation at the warp direction,but the different trends of the elastic elongation at the weft direction. When yarn run-in speed of GB2 was kept a constant,the increase of GB1 yarn run-in speed enlarged the elastic warp elongation from 104.16 to 124.97 mm,while the weft elongation decreased from 110.34 to 98.03 mm.Eventually yarn run-in speeds of GB1 and GB2 were retained at1 360 and 1 170 mm / rack respectively under 20 CPC drawing density. It could not only balance the two directions of elongation but also reach the highest elongation at both directions( 126. 32 and115.88 mm) under 100 N tension. These results provide a better understanding of characteristics of PET / PBT warp knitted fabric,and its elastic elongation and recovery behavior for development and effective applications.     

水分对尼龙1010/6力学性能的影响

通过研究饱和吸水的尼龙1010/6系列共聚物力学性能,并与干燥状态进行对比,发现水分对尼龙1010/6共聚物力学性能有明显影响.水分的存在可以明显降低尼龙1010/6共聚物的杨氏模量、弯曲模量、屈服应力、屈服应变,增大断裂应变,而对断裂强度、断裂能以及冲击强度的影响较为复杂.     

Effect of Blending Ratio on Properties of Core Yarn and Fabric of Polysulfonamide(PSA)/Flame Retardant Viscose(FRV)/Conductive Filament

In order to develop a fabric with excellent flame resistance function, antistatic function, moisture absorption and breathability, the polysulfonamide(PSA) fiber and the flame retardant viscose(FRV) fiber were blended. Meanwhile, the conductive filaments were used as the core yarn, and then they were made into the core-spun yarn and the fabric at different blending ratios of PSA/FRV. The effects of the blending ratio of PSA/FRV on the mechanical properties and the evenness of the yarn were studied. The effects of the blending ratio of PSA/FRV on mechanical properties, flame retardant properties, antistatic properties, moisture permeability and drape of the fabric were analyzed. With the increase of the blending ratios of PSA/FRV, the strength and the elongation of the core-spun yarn increased firstly and then decreased. Moreover, the evenness of the core-spun yarn was improved, the fabric strength increased firstly and then decreased, the flame resistance decreased, and the antistatic performance improved. These results provide an important basis for the preparation and wide application of fabrics made of PSA/FRV/conductive filament.     

尼龙66/聚酚氧树脂共混体系的研究

用熔融共混法制备了尼龙66/聚酚氧共混物, 对其力学性能、 结晶与熔融行为及组 分间相容性进行了表征. 共混物只有一个玻璃化转变温度, 且符合线性加和规则; 观察不 到两相形态, 表明两组分相容. 随聚酚氧含量增加, 尼龙66的冷结晶温度升高、 熔融温 度和熔体结晶温度降低, 结晶和熔融温度范围变宽, 熔融热和结晶热降低. 共混物的屈服 强度、 断裂强度和断裂伸长率均呈正协同效应, 并在聚酚氧含量30％～40％(均为质量分 数)呈极大值. 随聚酚氧含量的增加, 断裂强度与屈服强度的差值变小, 当聚酚氧含量达 到80％时, 二者已无明显差别.