Plasma preparation and low-temperature sintering of spherical TiC–Fe composite powder

A spherical Fe matrix composite powder containing a high volume fraction (82vol%) of fine TiC reinforcement was produced us-ing a novel process combining in situ synthesis and plasma techniques. The composite powder exhibited good sphericity and a dense struc-ture, and the fine sub-micron TiC particles were homogeneously distributed in theα-Fe matrix. A TiC–Fe cermet was prepared from the as-prepared spherical composite powder using powder metallurgy at a low sintering temperature;the product exhibited a hardness of HRA 88.5 and a flexural strength of 1360 MPa. The grain size of the fine-grained TiC and special surface structure of the spherical powder played the key roles in the fabrication process.     

Microstructure and mechanical properties of Nb–Si alloysfabricated by spark plasma sintering

This paper deals with microstructural evolutions and mechanical properties of Nb-Si binaries containing dual-phase Nb/Nb5Si3 with Nb to Nb5Si3 fraction ratios of 90:10,80:20,70:30 and 50:50,prepared by spark plasma sintering(SPS).Dense Nb/Nb5Si3 samples with a relative density larger than 99.5% were obtained by SPS processing.The SPS samples consist of the Nb and Nb5Si3 phases with less than 3% fraction of NbO oxide.Hv at room temperature,and compressive strength at 1150℃ and 1250 1C of the bulk SPS alloys increase monolithically by enhancing fraction of the stiffening Nb5Si3 phase.For example,0.2% yield strength,σ0.2,increases from 175 MPa to 420 MPa at 1150℃ and from 110 MPa to 280 MPa at 1250℃,when the Nb5Si3 fraction increases from 10% to 50%.It is interesting that the fracture toughness,KQ,of the bulk SPS samples seems not to be sensitive to phase fraction.Heat treatment,however,plays a key role on the KQ as compared with that of the as-sintered state,at the corresponding Nb5Si3 fraction and considerably improves the KQ by about 100% for samples with the Nb5Si3 fractions of 10%-30%,and by about 50% for the sample with 50% Nb5Si3 fraction.     

Erratum to: Electrical conductivity of molten LiF–DyF3–Dy2O3–Cu2O system for Dy–Cu intermediate alloy production

Erratum to:International Journal of Minerals, Metallurgy and Materials Volume 26, Number 6, June 2019, Page 701https://doi.org/10.1007/s12613-019-1775-z The acknowledgements of this article unfortunately contained a mistake. The grant number of the National Natural     

Effect of particle size distribution on the microstructure,texture, and mechanical properties of Al–Mg–Si–Cu alloy

The effect of particle size distribution on the microstructure, texture, and mechanical properties of Al–Mg–Si–Cu alloy was investigated on the basis of the mechanical properties, microstructure, and texture of the alloy. The results show that the particle size distribution influences the microstructure and the final mechanical properties but only slightly influences the recrystallization texture. After the pre-aging treatment and natural aging treatment (T4P treatment), in contrast to the sheet with a uniform particle size distribution, the sheet with a bimodal particle size distribution of large constituent particles and small dispersoids exhibits higher strength and a somewhat lower plastic strain ratio (r) and strain hardening exponent (n). After solution treatment, the sheet with a bimodal particle size distribution of large constituent particles and small dispersoids possesses a finer and slightly elongated grain structure compared with the sheet with a uniform particle size distribution. Additionally, they possess almost identical weak recrystallization textures, and their textures are dominated by CubeND {001}<310> and P {011}<122> orientations.     

Effect of CuO addition on the sintering temperature and microwave dielectric properties of CaSiO3– Al2O3 ceramics

CuO-doped CaSiO3–1 wt% Al2O3 ceramics were synthesized via a traditional solid-state reaction method, and their sintering behavior,microstructure and microwave dielectric properties were investigated. The results showed that appropriate CuO addition could accelerate the sintering process and assist the densification of CaSiO3–1 wt% Al2O3 ceramics, which could effectively lower the densification temperature from1250 1C to 1050 1C. However, the addition of CuO undermined the microwave dielectric properties. The optimal amount of CuO addition was found to be 0.8 wt%, and the derived CaSiO3–Al2O3ceramic sintered at 1100 1C presented good microwave dielectric properties of εr?7.27,Q f?16,850 GHz and τf? 39.53 ppm/1C, which is much better than those of pure CaSiO3 ceramic sintered at 1340oC(Q f?13,109 GHz).The chemical compatibility of the above ceramic with 30 Pd/70 Ag during the cofiring process has also been investigated, and the result showed that there was no chemical reaction between palladium–silver alloys and ceramics.& 2014 Chinese Materials Research Society. Production and hosting by Elsevier B.V. All rights reserved.     

Effect of Yb2O3 doping on the grain boundary of NiFe2O4–10NiO-based cermets after sintering

xYb2O3–15(20Ni–Cu)/(85?x)(NiFe2O4–10NiO) (x=0, 0.25, 0.5, 0.75, 1.0, 2.0, and 10.0) cermets for aluminum electrolysis were prepared to investigate the effect of Yb2O3 doping on the grain boundary of the cermets after sintering. The results showed that each interface was very clear and that with increasing Yb2O3 content, most of the Yb was evenly distributed at the grain boundary. Moreover, according to the phase composition and microstructural analysis by X-ray diffraction (XRD), scanning electron microscopy with energy dispersive X-ray spectroscopy (SEM/EDX), and electron probe microanalysis (EPMA), YbFeO3 was produced along the grain boundary. The YbFeO3 was concluded to not only have formed from the interaction between the NiFe2O4 or Fe2O3 component and Yb2O3 at the grain boundary of the cermets, but also from the decomposition of NiFe2O4 into NiO and Fe2O3 and the subsequent reaction of Fe2O3 with Yb2O3. Thus, the pro-duction of YbFeO3 resulted in a cermet with high relative density, good electrical conductivity, and good corrosion resistance.     

Effect of Ni content on the wear behavior of Al–Si–Cu–Mg–Ni/SiC particles composites

In recent years, the addition of Ni has been widely acknowledged to be capable of enhancing the mechanical properties of Al–Si alloys. However, the effect of Ni on the wear behaviors of Al–Si alloys and Al matrix composites, particularly at elevated temperatures, remains an understudied area. In this study, Al–Si–Cu–Mg–Ni/20wt% SiC particles(SiCp) composites with varying Ni contents were prepared by using a semisolid stir casting method. The effect of Ni content on the dry sliding wear behavior ...     

Effect of Yb_2O_3 doping on the grain boundary of NiFe_2O_4–10NiO-based cermets after sintering

xY b2O3–15(20Ni–Cu)/(85- x)(NiF e2O4–10NiO)(x = 0, 0.25, 0.5, 0.75, 1.0, 2.0, and 10.0) cermets for aluminum electrolysis were prepared to investigate the effect of Yb2O3 doping on the grain boundary of the cermets after sintering. The results showed that each interface was very clear and that with increasing Yb2O3 content, most of the Yb was evenly distributed at the grain boundary. Moreover, according to the phase composition and microstructural analysis by X-ray diffraction(XRD), scanning electron microscopy with energy dispersive X-ray spectroscopy(SEM/EDX), and electron probe microanalysis(EPMA), YbF eO 3 was produced along the grain boundary. The YbF eO 3 was concluded to not only have formed from the interaction between the NiF e2O4 or Fe2O3 component and Yb2O3 at the grain boundary of the cermets, but also from the decomposition of NiF e2O4 into NiO and Fe2O3 and the subsequent reaction of Fe2O3 with Yb2O3. Thus, the production of YbF eO 3 resulted in a cermet with high relative density, good electrical conductivity, and good corrosion resistance.     

Effect of homogenization process on the hardness of Zn–Al–Cu alloys

The effect of a homogenizing treatment on the hardness of as-cast Zn–Al–Cu alloys was investigated. Eight alloy compositions were prepared and homogenized at 350 ℃ for 180 h, and their Rockwell “B” hardness was subsequently measured. All the specimens were analyzed by X-ray diffraction and metallographically prepared for observation by optical microscopy and scanning electron microscopy. The results of the present work indicated that the hardness of both alloys (as-cast and homogenized) increased with increasing Al and Cu contents; this increased hardness is likely related to the presence of the θ and τ' phases. A regression equation was obtained to determine the hardness of the homogenized alloys as a function of their chemical composition and processing parameters, such as homogenization time and temperature, used in their preparation.     

Preparation of Al2O3–SiO2 composite aerogels and their Cu2+absorption properties

In order to remediate heavy metal ions from waste water,Al2O3–SiO2 composite aerogels are prepared via a sol–gel and an organic solvent sublimation drying method.Various characterisation techniques have been employed including X-ray diffraction(XRD),Fourier transform infrared spectrometry(FTIR),scanning electron microscope(SEM),Energy-dispersion X-ray spectroscopy(EDX),Brunauer–Emmett–Teller(BET)N2 adsoprtion isotherm,and atomic absorption spectrometer(AAS).XRD and FTIR suggest that the aerogels are composed of mainly Al2O3 and minor SiO2.They have a high specific surface area(827.544 m^2/g)and high porosity(86.0%)with a pore diameter of~20 nm.Their microstructures show that the distribution of Al,Si,and O is homogeneous.The aerogels can remove~99%Cu^2+within~40 min and then reach the equilibrium uptake(~69 mg/g).Preliminary calculations show that the Cu2+uptake by the aerogels follows pseudo second-order kinetics where chemical sorption may take effect owing largely to the high surface area,high porosity,and abundant functional groups,such as Al–OH and Si–OH,in the aerogel network.The prepared aerogels may serve as efficient absorbents for Cu^2+removal.     

Microstructure and mechanical properties of Cr doped WCoB based cermets by spark plasma sintering and first principle calculation

WCoB based cermet is a potential hard alloy to replace WC-Co cermets with high hardness and corrosion resistance. WCoB based cermets with different Cr doping contents were fabricated by spark plasma sintering in liquid phase sintering stage. The densification behavior, phase composition, microstructure and mechanical properties of Cr doped WCoB cermets were investigated by XRD, EDS and SEM. Due to the lower density of Cr,the density of WCoB cermets decreased with the increasing of Cr doping content. The phase composition consisted of Cr doped WCoB, unreacted W, Co–Cr binary binder phase. When the doping content exceeded11.736 wt%, the Cr enrichment zones appeared, which was harmful to the TRS. The increasing of Cr doping content contributed to the increase of unreacted W phases content and the formation of pores. The maximum value of Vickers hardness was 1751 Hv0.5 at 9.356 wt% Cr doping content. The variation trend was explained by first principle calculation, which is consistent with Hv-Zhou hardness model.     

SPS工艺对CuCr/CNTs复合材料组织性能的影响

放电等离子烧结（SPS）工艺可以实现快速烧结成型,且制备出的复合材料致密度高、硬度高、导电和导热性能好、晶粒尺寸均匀.在采用化学气相沉积（CVD）法原位合成分布均匀的CuCr/CNTs复合粉末的基础上,运用不同的SPS工艺制备CuCr/CNTs复合材料.利用扫描电子显微镜、偏光显微镜、数字金属导电率测试仪、微拉伸试验机、显微硬度计等对其组织性能进行表征.结果表明,当烧结温度为750 ℃,烧结压力为45 MPa,烧结时间为10 min,升温速率为80 ℃/min时,制备的CuCr/CNTs复合材料的组织和性能较佳,导电率、硬度和抗拉强度分别为86.8%IACS、95.8（HV）、178 MPa.     

W-Ni-Fe高比重合金的SPS烧结行为

采用放电等离子烧结(SPS)设备制备了93W-5.6Ni-1.4Fe高比重合金,烧结温度范围为1 100～1 180 ℃,保温时间为5 min.对不同烧结温度下的样品进行了密度、硬度、抗弯强度等性能测试,采用场发射SEM观察了样品表面形貌及断裂行为.结果表明:采用SPS烧结,可以在较低的温度下实现93W-5.6Ni-1.4Fe高比重合金的固相烧结,使合金致密化,并能有效控制钨晶粒长大,提高材料的硬度、抗弯强度等力学性能.     

机械合金化与等离子体烧结法制备CoSb3热电材料

研究用机械合金化及等离子体烧结法制备热电材料CoSb3化合物,试验结果表明,原始粉末机械合金化10h后,在500~600℃采用等离子体活化烧结能获得单相的CoSb3化合物,随烧结温度的升高,烧结样品密度增大,热导率随烧结温度的升高而降低。     

机械活化放电等离子烧结制备Ce_(0.8)Sm_(0.2)O_(1.9)固溶体

采用机械球磨方法制备(CeO2)0.8(SmO1.5)0.2纳米粉,并探讨了其适宜的工艺条件.分别用常规烧结和放电等离子烧结对所获纳米粉进行烧制,获得Ce0.8Sm0.2O1.9复合氧化物陶瓷,比较了两种烧结方法对材料结构与性能的影响.通过X射线衍射(XRD)、扫描电镜(SEM)等手段对氧化物进行了结构表征,交流阻抗谱测试了其电性能.结果表明:两种烧结方法所得样品均呈现单一的立方萤石结构;机械活化(CeO2)0.8(SmO1.5)0.2纳米粉于900℃时放电等离子烧结10min即可获得致密度90%以上的烧结体;放电等离子烧结材料的电导率高于常规烧结材料.