柱状纳米羟基磷灰石的制备和结构表征

以P2O5,Ca(NO3)2.4H2O为原料,无水乙醇为溶剂,通过调节pH值控制凝胶的形成,利用溶胶-凝胶/水热法制备柱状纳米羟基磷灰石(HAP).通过XRD、FTIR、电镜(TEM、SEM)等检测手段,对凝胶燃烧产物和经水热处理后的粉体相组成、形貌进行分析,探讨HAP晶体形成的原因.结果表明,利用溶胶-凝胶经低温燃烧后形成主晶相为纳米级的HAP,形状以柱状为主,经水热处理后,可得高纯度的HAP柱状晶体(100 nm×1800 nm),杂以少量粒状纳米粒子(30 nm×60 nm).     

羟基磷灰石纳米线的可控制备

用P2O5和Ca(NO3)2作为前驱体溶液,将溶胶—凝胶法与氧化铝模板(AAO)技术相结合,大面积制备出结构均匀、晶相一致、彼此平行且高度有序的羟基磷灰石(HAP)纳米线．结果表明,通过控制制备AAO模板的条件,可达到控制HAP形貌的目的．     

纳米级羟基磷灰石生物陶瓷粉末的制备新方法

对溶胶凝胶法制备纳米级羟基磷灰石生物陶瓷粉末的技术工艺进行了探索性研究。研究表明选择合适的原料配比，溶胶液的ｐＨ值、烧结温度和恒温时间，对于提高制备ＨＡ粉末的纯度和结晶度，改善ＨＡ晶体的纳米结构，并形成直径１μｍ左右的团聚体是极为重要的。     

溶胶-凝胶法制备羟基磷灰石粉体化学机理分析

利用硝酸钙醇溶液和五氧化二磷醇溶液,通过溶胶-凝胶法,制备了羟基磷灰石（HAP）粉体．对前驱体和不同热处理温度的HAP粉体试样进行了FTIR与XRD测试分析,讨论分析了在溶胶-凝胶法制备HAP过程中HAP生成化学反应的机理．     

鳌合剂对溶胶凝胶制备纳米羟基磷灰石的影响

采用硝酸钙(Ca(NO3)2.4H2O)、磷酸三甲酯(PO(CH3O)3,简称TMP)作为钙与磷的先驱体,用溶胶凝胶法合成纳米羟基磷灰石粉体.探讨了工艺过程中添加乙二醇、柠檬酸、甘氨酸三种鳌合剂对粉体制备及其特性的影响.实验结果表明,在合适配比下,鳌合剂的加入影响干凝胶的形态,并促使碳酸钙晶相出现.柠檬酸和甘氨酸会改变体系pH值,影响酯的水解反应,同时通过鳌合作用及表面电荷作用影响粉体粒径.研究表明甘氨酸是低温下制备纳米羟基磷灰石粉体合适的鳌合剂.     

镁表面制备羟基磷灰石涂层方法研究

镁及其合金由于具有良好的生物学特性,成为潜在的可生物降解的植入材料;但是其低的抗腐蚀能力会导致植入失败。在镁基体表面获得羟基磷灰石(HA)涂层用以改善镁及其合金的抗腐蚀能力。以硝酸钙和五氧化二磷为前躯体,使用溶胶-凝胶法制备出羟基磷灰石,并使用旋涂法在工业纯镁表面合成羟基磷灰石(HA)涂层。样品利用X射线衍射仪(XRD)、扫描电镜(SEM)进行了表征,并探讨了热处理温度对涂层的影响以及涂层的生成机理。     

柠檬酸对溶胶-凝胶法制备羟基磷灰石粉体的影响

为改善以Ca(NO) 3·4H2 O和 (CH3O) 3PO为前驱体、采用溶胶凝胶法制备羟基磷灰石(HAP)粉体的颗粒较大 ,尝试加入螯合剂柠檬酸 (C6H8O7) ,研究其对HAP粉体特征的影响 .SEM结果显示柠檬酸的加入使得粉体粒度明显变小 ,进一步在TEM观察 ,可以发现HAP粉体尺寸约为 5 0nm .XRD和FTIR分析表明柠檬酸的加入可使更多的CO2 -3 以B型替代的方式进入HAP结构中 ,并引起HAP晶格微畸变     

碳钠米管/羟基磷灰石复合材料的制备探讨

本文通过溶胶-凝胶法合成碳钠米管/羟基磷灰石复合材料,采用X射线衍射、红外光谱、热重等方法对产物的结构进行表征,并研究了陈化时间、煅烧温度、浓度、不同的钙磷比对复合产物的影响.实验表明,陈化时间对产物的影响较大,没有陈化直接就进行煅烧不能制备所需要的复合材料,经过了12h的陈化后则可制备相应的复合材料.此外,浓度对所制备材料的影响较小.     

原位制备聚己内酯和羟基磷灰石复合材料

采用溶胶-凝胶技术和真空干燥技术,原位制备了聚己内酯(PCL)和羟基磷灰石(HAP)多孔复合材料.对样品进行扫描电镜(SEM)、X射线粉末衍射仪(XRD)和拉曼散射光谱(Raman)表征和分析.结果表明,羟基磷灰石与聚己内酯分子间存在弱氢键作用;当羟基磷灰石在复合材料中的质量分数低于40％时,没有明显的相分离现象出现.     

人工合成纳米羟基磷灰石的研究

以磷酸二氢钙 ( Ca( H2 PO4) 2 · H2 O)和氢氧化钙 ( Ca( OH) 2 )的沉淀反应为基础 ,重点探讨反应条件、形核剂、干燥温度、烧结温度对羟基磷灰石形貌及尺寸的影响 .结果表明 ,通过控制反应温度、搅拌速度、反应时间及加入一定量的形核剂 ,可以得到纳米级、分散性良好的羟基磷灰石     

卵磷脂参与沉淀法制备纳米羟基磷灰石

改进传统的沉淀法,利用卵磷脂形成囊泡时产生的特殊反应环境限制羟基磷灰石(HAP)晶体的生长,得到了纳米HAP粉体．经500℃灼烧晶体粒径为10～20nm,700℃灼烧粒径保持在50nm左右,比相同热处理条件下由沉淀法获得的晶体(700℃灼烧时粒径在80～120nm左右)粒径显减小．这一结果与卵磷脂-水体系形成的高度分散的反应微环境的影响有关。     

Preparation and characterization of chitosan/nano-hydroxyapatite composite used as bone substitute materials

Chitosan/nano-hydroxyapatite composites with different weight ratios were prepared through a co-precipitation method using Ca（OH）2, H3PO4 and chitosan as starting materials. The properties of these composites were characterized by means of TEM, IR, XRD, TGA, burn-out tests and universal matertial testing machine. The results showed that the HA synthesized here was poorly crystalline carbonated nanometer crystals and dispersed uniformly in chitosan phase and there was no phase-separation between the two phases. The addition of n-HA resulted in a decrease of decomposing temperature of chitosan. Because of the interactions between chitosan and n-HA, the mechanical properties of these composites were improved, and the maximum value of the compressive strength was measured to be about 120MPa corresponding to the chitosan/n-HA composite with a weight ratio of 30/70.     

Organic-inorganic Polymer Nano-hybrids Based on Sol-gel Reaction

1 Results Nano-ordered composite materials consisting of organic polymers and inorganic materials have been attracting attention for the purpose of the creation of high-performance or high-functional polymeric materials. Especially,the word of “polymer hybrid“ claims the blends of organic and inorganic components at nano-level dispersion. By using this idea,an enhancement of mechanical strength of organic polymers with silica particles is possible.High transparency of this material is another important ...     

纳米二氧化钛材料的制备与性能研究

分别用溶胶-凝胶法与水热合成法制备了纳米二氧化钛.水热合成法与溶胶-凝胶法合成的纳米二氧化钛相比,比表面积很大,形貌比较规则;并且水热法合成的纳米二氧化钛已经出现纳米棒状结构,用自然界唯一的碱性多糖壳聚糖为模板剂合成的比表面积可以达432.36 m2/g.     

纳米级SiO2负载型多金属氧酸盐复合材料的制备及表征

采用溶胶-凝胶法制备了孔径为3.2nm的SiO2载体,通过自组装技术合成了纳米级SiO2负载型多金属氧酸盐复合材料PW11Ni-APS-SiO2.经N2吸附测定、UV/DRS、FT-IR、ICP-AES检测,母体PW11Ni与被胺修饰的载体之间不是单纯的吸附,而是生成了新的化学键,很好的解决了非均相反应中,负载型多金属氧酸盐易脱落的问题.     

钛掺杂BiFeO3光催化剂的制备及其催化性能

用溶胶-凝胶法制备钛(Ti)掺杂BiFeO₃纳米颗粒(Ti-BiFeO₃), 研究不同煅烧温度对Ti掺杂BiFeO₃结构调控及光催化性能的影响, 用X射线衍射（XRD）、 扫描电子显微镜（SEM）、 能谱分析（EDS）、 紫外-可见（UV-Vis)光谱技术对颗粒的相结构、 形貌、 原子比例、 光催化性能等进行测试及分析, 并以罗丹明-B为目标降解物, 对Ti掺杂BiFeO3光催化性能进行研究. 结果表明: Ti掺杂BiFeO₃样品在不同煅烧温度均出现Bi₂Fe₄O₉相; 煅烧温度可对Bi₂Fe₄O₉的含量进行调控, 在650 ℃煅烧样品中含有适量的Bi₂Fe₄O₉相, 能有效提高Ti掺杂BiFeO₃的光催化活性, 且具有较高的降解活性, 60 min内降解效率达85%.     

纳米TiO2膜的制备及表征

通过溶胶-凝胶工艺制备了表面均匀的纳米TiO2光催化薄膜．用UV—Vis、AFM、XRD和XPS等对薄膜的表面形貌、结构和组成等进行了表征．结果表明，TiO2膜的表面均匀，颗粒大小约50nm，晶型为锐钛矿型．     

掺杂Co的介孔SiO_2的制备与表征

利用溶胶-凝胶法,在碱性条件下,以正硅酸乙酯和KH550(γ-氨丙基三乙氧基硅烷)为硅源,CTAB为模板制备掺杂Co的介孔SiO2,并用BET、XRD、FT-IR、XPS对所得介孔SiO2进行表征.结果表明:所得介孔SiO2上负载了钴纳米粒子,煅烧温度在400℃的样品的比表面积最大,当温度逐渐提高时所得样品比表面积反而减小;当n(SiO2)∶n(CTAB)为1∶0.20时,所得样品比表面积(514.2 m2.g-1)相对较高,所制备的样品呈双介孔结构.